Preparation of high-quality gelatine having low chromium content from chromed waste stock

Claim 2

A process for preparing low chromium content gelatine from a chrome leather stock containing trivalent chromium, comprising: extracting a trivalent chromium containing leather stock with a solution of a compound which forms coordination complexes with trivalent chromium to remove a major amount of chromium present in said stock; conditioning the extracted leather stock with an alkaline solution containing sodium sulfate to partially depolymerize the collagen network of said leather stock; oxidizing a substantial portion of the residual trivalent chromium in the conditioned leather stock to the hexavalent state by treatment with hydrogen peroxide at a pH in the range of about 10 to 12.5 under approximately ambient temperature conditions; washing said oxidized stock to partially remove said hexavalent chromium; and extracting gelatin from the washed leather stock with an extracting solution containing magnesium oxide or sulfate.

Claim 3

The process of claim 1 wherein at least about 80% of the trivalent chromium is removed with a solution of a compound which forms soluble coordination complexes therewith.

Claim 4

The process of claim 1 wherein the compound which forms soluble coordination complexes with trivalent chromium is selected from the group consisting of monocarboxylic acids, dicarboxylic acids, tricarboxylic acids, hydroxycarboxylic acids, aminocarboxylic acids, phosphates, borates, polyhydric alcohols, phenols and salts of said carboxylic acids.

Claim 5

The process of claim 1 wherein the stock is treated at a temperature above ambient temperature with a solution of a compound which forms soluble coordination complexes with trivalent chromium.

Claim 6

The process of claim 1 wherein the stock is washed several times with water prior to the conditioning step.

Claim 7

The process of claim 1 wherein the treating solution containing trivalent chromium complex is treated to selectively precipitate chromium therefrom, said precipitated chromium is separated as a byproduct, and the dechromed solution retaining the compound which forms a soluble coordination complex with trivalent chromium is reused in treating said chrome stock.

Claim 8

The process of claim 1 wherein the conditioned partially depolymerized collagen containing stock is washed with water prior to any oxidation of the residual trivalent chromium.

Claim 9

The process of claim 1 wherein magnesium oxide is present during the extraction of gelatine from the washed stock.

Claim 10

The process of claim 3 wherein an acid or salt from an acid selected from the group consisting of lactic, citric, oxalic, tartaric and glycolic acid is used in the process.

Claim 11

The process of claim 3 wheren the chromium complexing compound is glycolic acid and is present in an aqueous solution in the concentration of from about 10 to 20%, said solution having a pH of from between about 5 to 9.

Claim 12

The process of claim 6 wherein the chromium is precipitated by adding 1 or 2% sodium hydroxide and lime in an amount which is two or three times the weight of the chromium present in the solution.

Claim 13

The process of claim 1 wherein the alkaline sulphate solution contains from about 4 to about 15% sodium hydroxide and from about 15 to about 20% sodium sulphate and is applied for at least about 8 hours at ambient temperature.

Claim 14

The process of claim 9 wherein the trivalent chromium complexing compound is sodium glycolate.

Claim 15

The process of claim 1 wherein the gelatine extraction is carried out at a temperature in the range of 60° C. to 95° C.

Claim 16

The process of claim 1 wherein the gelatine extraction is carried out in a plurality of steps with increasing temperature for each succeeding step, the first step being conducted at approximately 60° C.

Claim 17

A process for preparing low chromium content gelatine of minimum bloom strength of 200 grams and minimum viscosity of 30 mpoise from a chrome leather stock containing trivalent chromium, comprising: extracting a trivalent chromium containing leather stock with a solution of sodium glycolate at a pH of about 5 to 9 to remove a major amount of trivalent chromium present in said stock; conditioning the extracted leather stock with an alkaline solution containing sodium sulfate to partially depolymerize the collagen network of said leather stock; oxidizing a substantial portion of the residual trivalent chromium in the conditioned leather stock to the hexavalent state by treatment with hydrogen peroxide at a pH in the range of about 10 to 12.5 under approximately ambient temperature conditions; washing said oxidized stock to partially remove said hexavalent chromium; extracting gelatin from the washed leather stock with an extracting solution containing magnesium sulfate; and removing additional hexavalent chromium from the extracted gelatin by deionization.

Claim 18

A process for preparing low chromium content gelatine of minimum bloom strength of 200 grams and minimum viscosity of 30 mpoise from a chrome leather stock containing trivalent chromium, comprising: extracting a trivalent chromium containing leather stock with a solution of sodium glycolate at a pH of about 5 to 9 to remove a major amount of trivalent chromium present in said stock; conditioning the extracted leather stock with an alkaline solution containing sodium sulfate to partially depolymerize the collagen network of said leather stock; oxidizing a substantial portion of the residual trivalent chromium in the conditioned leather stock to the hexavalent state by treatment with hydrogen peroxide at a pH in the range of about 10 to 12.5 under approximately ambient temperature conditions; washing said oxidized stock to partially remove said hexavalent chromium; extracting gelatin from the washed leather stock with an extracting solution containing magnesium sulfate; and removing additional hexavalent chromium from the extracted gelatin by deionization.

Claim 19

The process of claim 16 wherein the extracted gelatine is clarified and deionized by passage through a strong anion-exchanging resin and a strong cation-exchanging resin.