Low temperature curing epoxy ester copolymers
Assignee: DeSoto Inc
•
Filing: 1977-10-21
•
Granted: 1979-04-24
•
Expires: 1997-10-21
Abstract
Abstract Low temperature curing aqueous coatings are provided in which the resin solids are constituted by an epoxy ester of a resinous polyepoxide with at least about 0.2 moles of monocarboxylic acid containing conjugated unsaturation and at least about 0.5 mole of monocarboxylic acid containing nonterminal nonconjugated unsaturation per equivalent in the polyepoxide. This epoxy ester is substantially free of epoxy groups and is copolymerized in solvent solution with monoethylenic monomers containing terminal unsaturation, including about 3% to about 20% carboxyl-functional monomers based on the weight of the copolymer to provide a nongelled, solvent-soluble copolymer possessing residual ethylenic unsaturation so that the copolymer can be dispersed in water with the aid of a base. These epoxy ester copolymers will dry and cure in air at room temperature. Also, and by including in the copolymer a proportion of monoethylenic monomer containing terminal unsaturation and providing a primary hydroxy group, the copolymer contains primary hydroxyl groups as well as carboxyl groups and residual unsaturation so that when aminoplast or phenoplast resin is incorporated in the water solutions, the applied coatings cure at remarkably low temperature to form solvent and corrosion-resistant coatings.
Inventors
- 👤 Kazys Sekmakas
- 👤 Raj Shah
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:08
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; C09D5/4423; C09D5/4426; C08; C08F; C08F290/00; C08F290/08; C08F290/14; C08F290/144; C08F299/00; C08F299/02; C08F299/026; C09D163/00; C09D163/10; C09D4/00; C09D4/06
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
191 words
A low temperature curing aqueous coating comprising epoxy ester copolymer of an epoxy ester of a resinous polyepoxide having an epoxy functionality in the range of from 1.4 to about 2.0 with at least about 0.2 moles of ethylenically unsaturated monocarboxylic fatty acid containing conjugated ethylenic unsaturation per epoxy equivalent in the polyepoxide, and at least about 0.5 mole of ethylenically unsaturated monocarboxylic fatty acid containing nonterminal nonconjugated ethylenic unsaturation per epoxy equivalent in the polyepoxide, said epoxy ester being substantially free of epoxy functionality and being copolymerized in organic solvent solution with from about 15% to about 150%, based on the weight of the epoxy ester, of monoethylenically unsaturated monomers containing terminal ethylenic unsaturation to form a nongelled, solvent-soluble, copolymer possessing residual ethylenic unsaturation adapting the same for an oxidative cure, said monomers including from about 3% to about 20%, based on the weight of the copolymer, of carboxyl-functional monomers selected from acrylic acid, methacrylic acid, fumaric acid and maleic acid, said copolymer being dispersed in water with the aid of a volatile base and water miscible organic solvent, said water also having dispersed therein an aminoplast or phenoplast resin.
Claim 2
Dependent Claim
191 words
A low temperature curing aqueous coating comprising epoxy ester copolymer of an epoxy ester of a resinous polyepoxide having an epoxy functionality in the range of from 1.4 to about 2.0 with at least about 0.2 moles of ethylenically unsaturated monocarboxylic fatty acid containing conjugated ethylenic unsaturation per epoxy equivalent in the polyepoxide, and at least about 0.5 mole of ethylenically unsaturated monocarboxylic fatty acid containing nonterminal nonconjugated ethylenic unsaturation per epoxy equivalent in the polyepoxide, said epoxy ester being substantially free of epoxy functionality and being copolymerized in organic solvent solution with from about 15% to about 150%, based on the weight of the epoxy ester, of monoethylenically unsaturated monomers containing terminal ethylenic unsaturation to form a nongelled, solvent-soluble, copolymer possessing residual ethylenic unsaturation adapting the same for an oxidative cure, said monomers including from about 3% to about 20%, based on the weight of the copolymer, of carboxyl-functional monomers selected from acrylic acid, methacrylic acid, fumaric acid and maleic acid, said copolymer being dispersed in water with the aid of a volatile base and water miscible organic solvent, said water also having dispersed therein an aminoplast or phenoplast resin.
Claim 3
Dependent Claim
32 words
A low temperature curing aqueous coating as recited in claim 1 in which said carboxy-functional monomers are present in an amount of from 5% to 12% of the weight of the copolymer.
Claim 4
Dependent Claim
44 words
A low temperature curing aqueous coating as recited in claim 2 in which said polyepoxide is a diglycidyl ether of bisphenol A having an average molecular weight of about 800 to about 3000 and an epoxy functionality in the range of 1.8 to 2.0.
Claim 5
Dependent Claim
35 words
A low temperature curing aqueous coating as recited in claim 3 in which said epoxy ester contains from about 0.8 to about 1.5 moles of said conjugated fatty acid per epoxy equivalent in said polyepoxide.
Claim 6
Dependent Claim
22 words
A low temperature curing aqueous coating as recited in claim 1 in which said monocarboxylic fatty acids contain from 8-22 carbon atoms.
Claim 7
Dependent Claim
51 words
A low temperature curing aqueous coating as recited in claim 1 in which said polyepoxide is a bisphenol-based diepoxide having an average molecular weight of from about 350 to about 4000 and an epoxy functionality in the range of 1.8-2.0 and the nonreactive monomers are selected from styrene and vinyl toluene.
Claim 8
Dependent Claim
32 words
A low temperature curing aqueous coating as recited in claim 6 in which said epoxy ester contains less than 2.0 moles of said conjugated fatty acid per epoxy equivalent in said polyepoxide.
Claim 9
Dependent Claim
35 words
A low temperature curing aqueous coating as recited in claim 1 in which said monoethylenically unsaturated monomers are used in an amount of from 25% to 70%, based on the weight of the epoxy ester.
Claim 10
Dependent Claim
24 words
A low temperature curing aqueous coating as recited in claim 1 in which said copolymer has an iodine value of at least about 40.
Claim 11
Dependent Claim
39 words
A low temperature curing aqueous coating as recited in claim 1 in which said monomers further include monomer providing the primary hydroxy group in an amount of from about 1% to about 15% of the weight of the copolymer.
Claim 12
Dependent Claim
32 words
A low temperature curing aqueous coating as recited in claim 10 in which said carboxy-functional monomers are present in an amount of from 5% to 12% of the weight of the copolymer.
Claim 13
Dependent Claim
22 words
A low temperature curing aqueous coating as recited in claim 11 in which said monocarboxylic fatty acids contain from 10-18 carbon atoms.
Claim 14
Dependent Claim
55 words
A low temperature curing aqueous coating as recited in claim 11 in which said polyepoxide is a diglycidyl ether of bisphenol A having an average molecular weight of about 800 to about 3000 and an epoxy functionality in the range of 1.8 to 2.0, and the nonreactive monomers are selected from styrene or vinyl toluene.
Claim 15
Dependent Claim
39 words
A low temperature curing aqueous coating as recited in claim 13 in which from about 0.3 to about 2% of a drier is present, based on the weight of the copolymer, to speed the oxidative cure of said copolymer.
Claim 16
Dependent Claim
35 words
A low temperature curing aqueous coating as recited in claim 11 in which said epoxy ester contains from about 0.8 to about 1.5 moles of said conjugated fatty acid per epoxy equivalent in said polyepoxide.
Claim 17
Dependent Claim
55 words
A low temperature curing aqueous coating as recited in claim 11 in which said monoethylenically unsaturated monomers are used in an amount of from 50% to 90% based on the weight of the epoxy ester, and said hydroxy monomer is present in an amount of from 2% to 8% of the weight of the copolymer.
Claim 18
Dependent Claim
23 words
A low temperature curing aqueous coating as recited in claim 11 in which the acidity of said copolymer is provided by acrylic acid.
Claim 19
Dependent Claim
24 words
A low temperature curing aqueous coating as recited in claim 11 in which said copolymer has an iodine value of at least about 40.
Claim 20
Dependent Claim
20 words
A low temperature curing aqueous coating as recited in claim 11 in which said hydroxy monomer is hydroxy ethyl acrylate.
Claim 21
Dependent Claim
24 words
The low temperature curing aqueous coating of claim 11 in which said copolymer is neutralized with an amine and said aminoplast resin is benzoguanamine-formaldehyde.
Claim 22
Dependent Claim
23 words
The low temperature curing aqueous coating of claim 11 in which the proportion of aminoplast resin is from 5%-40%, based on total resin.
References Cited (Backward Citations)
US2596737A
Cited
US2877195A
Cited
US3107226A
Cited
US3457324A
Cited
US3506601A
Cited
US3536641A
Cited
US3674731A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |