Flake- or sliver-like porous structure of polymeric material and process of producing same, and process of producing sheet-like structure therefrom
Assignee: Mitsubishi Chemical Corp
•
Filing: 1975-09-02
•
Granted: 1979-03-27
•
Expires: 1995-09-02
Abstract
Abstract Flake- or sliver-like porous structures of a polymeric material heavily loaded with a finely divided inorganic substance are prepared by spurting a mixture of the polymeric and finely divided inorganic components in a solvent. The products have many fine, irregular voids. The thickness of walls forming such voids is 5 mu or less. The products are especially useful for producing sheet-like structures therefrom by beating and/or refining them followed by general paper making procedures. The sheets, when calendered, have a high initial modulus and improved dimensional stability.
Inventors
- 👤 Masahiko Miyanoki
- 👤 Takeshi Uotani
- 👤 Fujio Itani
- 👤 Toshi Yoshihara
- 👤 Masayuki Igawa
- 👤 Munehiro Okumura
- 👤 Syoji Imao
- 👤 Yoshiaki Taniyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 04:07
CPC Classifications
D; D01; D01D; D01D5/00; D01D5/11; C; C08; C08J; C08J9/00; C08J9/0066; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/17
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
245 words
A process for the production of flake- or silver-like porous structures composed of a finely divided inorganic component and a fiber forming synthetic polymeric component which comprises: (1) forming a mixture consisting essentially of the finely divided inorganic component in a weight fraction of W f and a fiber or film forming polymeric component in a weight fraction of 1 - W f dispersed in a solvent which has a boiling point lower than the softening point of the polymeric component and is capable of dissolving the polymeric component at elevated temperatures, the solvent being present in an amount at least sufficient to dissolve the polymeric component at an elevated temperature, the weight fraction W f satisfying the following relation: 0.9 ≧ W.sub.f ≧ V.sub.p /(V.sub.p + V.sub.a - V.sub.f) wherein W f is the weight fraction of the finely divided inorganic component based on the combined weight of the finely divided inorganic and polymeric components, V p is the specific volume of the polymeric component, V a is the bulkiness of the finely divided inorganic component and V f is the true specific volume of the finely divided inorganic component; (2) heating said mixture to an elevated temperature under at least autogenous pressure to dissolve the polymeric component in the solvent and (3) ejecting the heated mixture through an orifice into a zone of lower pressure and lower temperature whereby solvent is evaporated from the mixture and flake- or sliver-like porous structures are formed.
Claim 2
Dependent Claim
245 words
A process for the production of flake- or silver-like porous structures composed of a finely divided inorganic component and a fiber forming synthetic polymeric component which comprises: (1) forming a mixture consisting essentially of the finely divided inorganic component in a weight fraction of W f and a fiber or film forming polymeric component in a weight fraction of 1 - W f dispersed in a solvent which has a boiling point lower than the softening point of the polymeric component and is capable of dissolving the polymeric component at elevated temperatures, the solvent being present in an amount at least sufficient to dissolve the polymeric component at an elevated temperature, the weight fraction W f satisfying the following relation: 0.9 ≧ W.sub.f ≧ V.sub.p /(V.sub.p + V.sub.a - V.sub.f) wherein W f is the weight fraction of the finely divided inorganic component based on the combined weight of the finely divided inorganic and polymeric components, V p is the specific volume of the polymeric component, V a is the bulkiness of the finely divided inorganic component and V f is the true specific volume of the finely divided inorganic component; (2) heating said mixture to an elevated temperature under at least autogenous pressure to dissolve the polymeric component in the solvent and (3) ejecting the heated mixture through an orifice into a zone of lower pressure and lower temperature whereby solvent is evaporated from the mixture and flake- or sliver-like porous structures are formed.
Claim 3
Dependent Claim
73 words
A process according to claim 1 wherein said solvent for the polymeric component is at least one selected from the group consisting of benzene, toluene, butane, hexane, cyclohexane, pentene, methylene chloride, chloroform, methyl chloride, propyl chloride, trichloroethylene, trichloroethane, tetrachloroethylene, tetrachloroethane, chlorobenzenes, methanol, ethanol, propanol, butanol, acetone, cyclopentanone, methyl ethyl ketone, hexafluoroacetone, methyl acetate, ethyl acetate, X-butyrolactone, ethyl ether, tetrahydrofurane, dioxane, acetonitrile, propionitrile, trifluoroacetic acid, carbon tetrachloride, carbon/disulfide, water, Freon gas and sulfur dioxide.
Claim 4
Dependent Claim
46 words
A process according to claim 1 wherein the mixture of the finely divided inorganic component and the polymeric component dispersed in the solvent is heated in a closed system to a sufficient temperature at which an autogenous pressure of at least 5 kg/cm 2 is created.
Claim 5
Dependent Claim
31 words
A process according to claim 3 wherein the heated mixture is ejected under a pressure of at least the autogenous pressure through an orifice into a zone of substantially atmospheric pressure.
Claim 6
Dependent Claim
9 words
The product obtained by the process of claim 1.
Claim 7
Dependent Claim
9 words
The product obtained by the process of claim 4.
References Cited (Backward Citations)
US2810646A
Cited
US3003304A
Cited
US3210239A
Cited
US3884030A
Cited
US3912665A
Cited
US3912666A
Cited
NL7100859A
Cited
US3785919A
Cited
US3931762A
Cited
US4049593A
Cited
US3911070A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-26 | 1982-09-25 | 1983-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-26 | 1986-09-25 | 1987-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-26 | 1990-09-25 | 1991-03-27 | $7700.00 | Window Closed / Lapsed |