Process for the manufacture of sheets from a mixture of vegetable fibres and polyolefine
Assignee: Solvay SA
•
Filing: 1976-08-11
•
Granted: 1979-03-13
•
Expires: 1996-08-11
Abstract
Abstract Manufacture of sheets having a high resistance to water absorption by hot calendering of a mixture produced from 25 to 75% by weight of vegetable fibres and from 75 to 25% by weight of molten polyolefine. As unexpected, such a mixture does not stick to the calender rolls during the sheeting step.
Inventors
- 👤 Michel Dereppe
- 👤 Antoine Deryckere
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:47
CPC Classifications
C; C08; C08L; C08L97/00; C08L97/02; B; B29; B29C; B29C43/00; B29C43/22; B29C43/24; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/13; C08L23/00; C08L23/02; C08L23/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
101 words
Process for the manufacture of sheets having a high resistance to water absorption, from a mixture of vegetable fibres and polyolefine, where a homogenous mixture is produced from 25 to 75% by weight of vegetable fibres and from 75 to 25% by weight of molten polyolefine and in that this mixture is sheeted by hot calendering at a temperature at least equal to the melting point of the polyolefine, the hot calendering being carried out on a calender having a plurality of rolls all of which are heated at the surface to a temperature above the melting point of the polyolefine.
Claim 2
Dependent Claim
101 words
Process for the manufacture of sheets having a high resistance to water absorption, from a mixture of vegetable fibres and polyolefine, where a homogenous mixture is produced from 25 to 75% by weight of vegetable fibres and from 75 to 25% by weight of molten polyolefine and in that this mixture is sheeted by hot calendering at a temperature at least equal to the melting point of the polyolefine, the hot calendering being carried out on a calender having a plurality of rolls all of which are heated at the surface to a temperature above the melting point of the polyolefine.
Claim 3
Dependent Claim
30 words
Process according to claim 1, wherein the homogeneous mixture of vegetable fibres and of molten polyolefine is produced in a plunger-type internal mixer, by introducing these constituents in metered amounts.
Claim 4
Dependent Claim
53 words
Process according to claim 2, wherein the homogeneous mixture of vegetable fibres and of molten polyolefine issuing from the plunger-type internal mixer is received on a roll-type external mixer which converts the successive charges of mixture, delivered by the internal mixer, to a continuous strip which is introduced into a hot calendering installation.
Claim 5
Dependent Claim
36 words
Process according to claim 1, wherein the homogeneous mixture of vegetable fibres and of molten polyolefine is produced by extrusion and is extruded in the form of a thick strand which is sheeted by hot calendering.
Claim 6
Dependent Claim
33 words
Process according to claim 1, wherein the homogeneous mixture of vegetable fibres and of molten polyolefine is heated, before calendering, to a temperature at least equal to the melting point of the polyolefine.
Claim 7
Dependent Claim
39 words
Process according to claim 1, wherein the two first rolls of the calender are heated at the surface to a temperature between the melting point of the polyolefine plus 2° C. and the said melting point plus 20° C.
Claim 8
Dependent Claim
49 words
Process according to claim 1, wherein vegetable fibres which are in the form of particles having a mean size of between 0.1 and 3 mm and a polyolefine which only contains monomeric units derived from an olefine containing from 2 to 8 carbon atoms in its molecule are employed.
Claim 9
Dependent Claim
30 words
Process according to claim 1, wherein a polyolefine containing at least 70% of propylene in its molecule is employed and the calendering temperature is chosen between 172° and 190° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-12 | 1982-09-11 | 1983-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-12 | 1986-09-11 | 1987-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-12 | 1990-09-11 | 1991-03-13 | $7700.00 | Window Closed / Lapsed |