US3981840A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for molding thermoplastic resin compositions
Assignee: Joto Chemical Co Ltd
•
Filing: 1974-03-13
•
Granted: 1976-09-21
•
Expires: 1994-03-13
Abstract
Abstract A process is provided for the manufacture of shaped articles by molding a thermoplastic resin and filler. The process comprises mixing a thermoplastic resin with a filler preheated to a temperature at which the filler will have an amount of heat sufficient for heating the resin to its melting point and which is 50° to 200°C higher than the same melting point, and subjecting the mixture to molding into articles of desired forms and sizes. Various sorts of molding machines can be used, and the manufacturing costs are low.
Inventors
- 👤 Sadanori Yamamoto
- 👤 Isao Osada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 00:59
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/203; B; B29; B29C; B29C48/00; B29C48/022; C08K; C08K9/00; B29C48/03; B29C48/04; B29K; B29K2105/00; B29K2105/06; B29K2105/12
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
202 words
Process for manufacture of shaped articles by molding a thermoplastic resin composition and a filler which comprises (1) preheating the filler to a preheating temperature at which the filler has an amount of heat sufficient for heating the resin to its melting point and which is about 50° to about 200°C higher than the melting point of the thermoplastic resin, (2) mixing and heating thermoplastic resin with the filler in a true volume ratio of resin to filler between about 1 to 0.5 and about 1 to 1.5, controlling said preheating temperature of the filler being limited to a temperature T 2 which is defined by the relation W 1 C 1 (T M -T 1 ) = W 2 C 2 (T 2 -T M ) wherein W 1 and W 2 are the respective weights of resin and filler in one mixture, C 1 and C 2 are the respective specific heats of the resin and filler, T 1 is the temperature of the resin, and T M is the melting point of the resin, and (3) subsequently kneading the resultant mixture of resin and filler under pressure, and then molding the resultant mixture to form the desired shaped article.
Claim 2
Dependent Claim
202 words
Process for manufacture of shaped articles by molding a thermoplastic resin composition and a filler which comprises (1) preheating the filler to a preheating temperature at which the filler has an amount of heat sufficient for heating the resin to its melting point and which is about 50° to about 200°C higher than the melting point of the thermoplastic resin, (2) mixing and heating thermoplastic resin with the filler in a true volume ratio of resin to filler between about 1 to 0.5 and about 1 to 1.5, controlling said preheating temperature of the filler being limited to a temperature T 2 which is defined by the relation W 1 C 1 (T M -T 1 ) = W 2 C 2 (T 2 -T M ) wherein W 1 and W 2 are the respective weights of resin and filler in one mixture, C 1 and C 2 are the respective specific heats of the resin and filler, T 1 is the temperature of the resin, and T M is the melting point of the resin, and (3) subsequently kneading the resultant mixture of resin and filler under pressure, and then molding the resultant mixture to form the desired shaped article.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein said filler is an inorganic substance in the form of powder or granules.
Claim 4
Dependent Claim
16 words
The process of claim 1, wherein said thermoplastic resin is preheated to about its melting point.
Claim 5
Dependent Claim
64 words
The process according to claim 1, wherein said thermoplastic resin is a member selected from the group consisting of polystyrene, polyethylene, polypropylene, polyvinyl chloride, polyamide, AS resin, and ABS resin, and wherein said filler is an inorganic filler comprising at least one member selected from the group consisting of finely divided limestone, granite, andesite, calcium carbonate, silica, clay, asbestos, gypsum, alumina, cement and glass.
Claim 6
Dependent Claim
24 words
The process according to claim 1, wherein, after kneading under pressure, the resultant mixture is extruded to desired shape and size, cooled and recovered.
Claim 7
Dependent Claim
25 words
The process according to claim 1, wherein, after kneading under pressure, the resultant mixture is molded to the desired size and shape, cooled and recovered.
Claim 8
Dependent Claim
91 words
The process according to claim 1, wherein said thermoplastic resin is a member selected from the group consisting of polystyrene, polyethylene, polypropylene, polyvinyl chloride, polyamide, AS resin, ABS resin, and waste plastics thereof, and wherein said filler is an inorganic filler consisting essentially of at least one member selected from the group consisting of finely divided limestone, granite, andesite, calcium carbonate, silica, clay, asbestos, gypsum, alumina, cement, glass, cinders, slag, and sludge, and wherein after kneading under pressure, the resultant mixture is extruded to desired shape and size, cooled and recovered.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |