Stable heat shrinkable ternary β-brass alloys containing aluminum
Assignee: Raychem Corp
•
Filing: 1977-03-30
•
Granted: 1979-03-13
•
Expires: 1997-03-30
Abstract
Abstract Those alloys falling within the area on a ternary diagram defined by the points: ______________________________________ A. 78.3% Cu 9.7% Al 12% Zn B. 75.1% Cu 7.5% Al 17.4% Zn C. 67% Cu 4.2% Al 28.8% Zn D. 72.6% Cu 7.9% Al 19.5% Zn ______________________________________ Are particularly suited for use as the material of heat recoverable articles as they exhibit good ductility and stability and are easily worked by hot working techniques. Additionally, they have M 3 temperatures which enables them to be fabricated into heat recoverable articles useful in many applications. A heat recoverable article, made from a ternary alloy of copper, aluminum, and zinc whose composition falls on or near the eutectoid line, is particularly suited for use in circumstances where the article has been recovered from its recoverable state under conditions such that a degree of unresolved recovery remains.
Inventors
- 👤 Peter L. Brooks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:13
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/006; C22C; C22C9/00; C22C9/01
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
126 words
A ternary alloy comprised of copper, aluminum and zinc having a β-brass type structure falling within the area on a ternary diagram defined by the points: ______________________________________
A. 78.3% Cu 9.7% Al 12% Zn
B. 75.1% Cu 7.5% Al 17.4% Zn
C. 67% Cu 4.2% Al 28.8% Zn
D. 72.6% Cu 7.9% Al 19.5% Zn
______________________________________ said alloy being in its martensitic state and an M s temperature of 0° C. or lower and having been deformed from an original configuration to render it heat recoverable, said alloy exhibiting stress stability of at least 1,000 hrs at 125°° C. when caused to recover by being warmed to a temperature at which the alloy exists in its austenitic state so that a degree of unresolved recovery remains.
Claim 2
Dependent Claim
126 words
A ternary alloy comprised of copper, aluminum and zinc having a β-brass type structure falling within the area on a ternary diagram defined by the points: ______________________________________
A. 78.3% Cu 9.7% Al 12% Zn
B. 75.1% Cu 7.5% Al 17.4% Zn
C. 67% Cu 4.2% Al 28.8% Zn
D. 72.6% Cu 7.9% Al 19.5% Zn
______________________________________ said alloy being in its martensitic state and an M s temperature of 0° C. or lower and having been deformed from an original configuration to render it heat recoverable, said alloy exhibiting stress stability of at least 1,000 hrs at 125°° C. when caused to recover by being warmed to a temperature at which the alloy exists in its austenitic state so that a degree of unresolved recovery remains.
Claim 3
Dependent Claim
75 words
An alloy in accordance with claim 1 wherein said alloy has an eutectoidal composition, said eutectoidal composition being a composition wherein no metal of the group consisting of copper, aluminum and zinc is present in said alloy in an amount that differs by more than 1% by weight from the amount of said metal present in a composition corresponding to a eutectoidal composition defined by the line XY of the ternary diagram of FIG. 1.
Claim 4
Dependent Claim
14 words
An alloy in accordance with claim 2 wherein said alloy has an eutectoid composition.
Claim 5
Dependent Claim
172 words
A process for making a heat recoverable article that exhibits stress stability of at least 1,000 hours at 125° C. when allowed to recover so that a degree of unresolved recovery remains comprising the steps: (a) selecting a ternary alloy capable of being rendered heat recoverable comprised of copper, aluminum and zinc having a β-brass type structure and having an M s temperature of 0° C. or lower falling within the area on a ternary diagram defined by the points: ______________________________________
A. 78.3% Cu 9.7% Al 12% Zn
B. 75.1% Cu 7.5% Al 17.4% Zn
C. 67% Cu 4.2% Al 28.8% Zn
D. 72.6% Cu 7.9% Al 19.5% Zn
______________________________________ (b) fabricating said article from the selected alloy into an original, heat-stable configuration, (c) cooling said article to a temperature at which the alloy exists in its martensitic state, and (d) deforming said article to a second, heat-unstable configuration from which recovery occurs when said article is warmed to a temperature at which the alloy reverts to austenite from said martensitic state.
Claim 6
Dependent Claim
172 words
A process for making a heat recoverable article that exhibits stress stability of at least 1,000 hours at 125° C. when allowed to recover so that a degree of unresolved recovery remains comprising the steps: (a) selecting a ternary alloy capable of being rendered heat recoverable comprised of copper, aluminum and zinc having a β-brass type structure and having an M s temperature of 0° C. or lower falling within the area on a ternary diagram defined by the points: ______________________________________
A. 78.3% Cu 9.7% Al 12% Zn
B. 75.1% Cu 7.5% Al 17.4% Zn
C. 67% Cu 4.2% Al 28.8% Zn
D. 72.6% Cu 7.9% Al 19.5% Zn
______________________________________ (b) fabricating said article from the selected alloy into an original, heat-stable configuration, (c) cooling said article to a temperature at which the alloy exists in its martensitic state, and (d) deforming said article to a second, heat-unstable configuration from which recovery occurs when said article is warmed to a temperature at which the alloy reverts to austenite from said martensitic state.
Claim 7
Dependent Claim
66 words
A process according to claim 4 wherein said alloy has an eutectoidal composition, said eutectoidal composition being a composition wherein no metal of the group consisting of copper, aluminum and zinc is present in an amount that differs by more than 1% by weight from the amount of said metal in a composition corresponding to an eutectoid composition defined by the line XY of FIG. 1.
Claim 8
Dependent Claim
13 words
A process according to claim 5 wherein said alloy has an eutectoid composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-12 | 1982-09-11 | 1983-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-12 | 1986-09-11 | 1987-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-12 | 1990-09-11 | 1991-03-13 | $7700.00 | Window Closed / Lapsed |