US4143110A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of agglomerating polytetrafluoroethylene powder
Assignee: AGC Inc
•
Filing: 1977-07-08
•
Granted: 1979-03-06
•
Expires: 1997-07-08
Abstract
Abstract Finely ground polytetrafluoroethylene molding powder with or without a filler is subjected to high speed agitation in the presence of a medium consisting essentially of water and a hydrophobic organic liquid at a ratio of 0.5 to 1 liter per 1 Kg of the resin to agglomerate it. Hydrophobic organic liquids mean organic liquid which dissolve less than 15 wt. % in water at the temperature of agglomeration. The volumetric ratio of the organic liquid to water is in a range of 2 to 1/2. The agglomerated product having narrow particle size distribution and high bulk density and free flowing property can be obtained by the agitation for short time.
Inventors
- 👤 Mituharu Morozumi
- 👤 Masataka Arai
- 👤 Shigeru Iseki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:38
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
104 words
A method of agglomerating polytetrafluoroethylene molding powder, which comprises: (a) agglomerating a finely ground polytetrafluoroethylene molding powder by subjecting said powder having an average particle diameter of less than 100 μm to high speed agitation in the presence of a medium consisting of water and a hydrophobic organic liquid, of which less than 15 wt.% is miscible with water at the temperature of agglomeration, at a volumetric ratio of the organic liquid to water of 2:1 to 1:2 and a ratio of 0.5 to 1 liter of the medium per 1 Kg of said powder; and (b) separating the resulting agglomerates from the medium.
Claim 2
Independent Claim
104 words
A method of agglomerating polytetrafluoroethylene molding powder, which comprises: (a) agglomerating a finely ground polytetrafluoroethylene molding powder by subjecting said powder having an average particle diameter of less than 100 μm to high speed agitation in the presence of a medium consisting of water and a hydrophobic organic liquid, of which less than 15 wt.% is miscible with water at the temperature of agglomeration, at a volumetric ratio of the organic liquid to water of 2:1 to 1:2 and a ratio of 0.5 to 1 liter of the medium per 1 Kg of said powder; and (b) separating the resulting agglomerates from the medium.
Claim 3
Dependent Claim
29 words
The method of claim 1, wherein the high speed agitation is conducted with an apparatus in which the peripheral speed of the agitating blades is greater than 5 m/sec.
Claim 4
Dependent Claim
24 words
The method of claim 1, wherein the particles of the finely ground polytetrafluoroethylene molding powder have an average diameter of 20 to 50 μm.
Claim 5
Dependent Claim
15 words
The method of claim 1, wherein the temperature of agglomeration is less than 40° C.
Claim 6
Dependent Claim
21 words
The method of claim 1, wherein the hydrophobic organic liquid has a surface tension less than 45 dyne/cm at 23° C.
Claim 7
Dependent Claim
19 words
The method of claim 1, wherein the hydrophobic organic liquid has a boiling point of 40° to 200° C.
Claim 8
Dependent Claim
28 words
The method of claim 1, wherein the resulting agglomerates have an average diameter of 300 to 600 μm and an angle of repose of less than 45 degrees.
Claim 9
Dependent Claim
22 words
The method of claim 1, wherein the resulting agglomerates contain less than 10 wt.% of particles having diameters greater than 2,000 μm.
Claim 10
Dependent Claim
118 words
A process for preparing an agglomerated polytetrafluoroethylene material containing a solid hydrophobic filler, which comprises: (a) agglomerating a mixture of polytetrafluoroethylene having an average particle diameter of less than 100 μm and the hydrophobic filler under high speed agitation conditions in the presence of a medium consisting of water and a hydrophobic organic liquid, which is soluble in water in an amount of less than 15 wt.% at the temperature of agglomeration, having a volumetric ratio of the organic liquid to water of 2:1 to 1:2 and a ratio of 0.5 to 1 liter of the medium per 1 Kg of the mixture of the resin and the filler; and (b) separating the resulting agglomerates from the medium.
Claim 11
Dependent Claim
118 words
A process for preparing an agglomerated polytetrafluoroethylene material containing a solid hydrophobic filler, which comprises: (a) agglomerating a mixture of polytetrafluoroethylene having an average particle diameter of less than 100 μm and the hydrophobic filler under high speed agitation conditions in the presence of a medium consisting of water and a hydrophobic organic liquid, which is soluble in water in an amount of less than 15 wt.% at the temperature of agglomeration, having a volumetric ratio of the organic liquid to water of 2:1 to 1:2 and a ratio of 0.5 to 1 liter of the medium per 1 Kg of the mixture of the resin and the filler; and (b) separating the resulting agglomerates from the medium.
Claim 12
Dependent Claim
12 words
The process of claim 9, wherein the hydrophobic filler is carbon fiber.
Claim 13
Dependent Claim
34 words
The process of claim 9, wherein the hydrophobic filler is formed by a process in which the surface of a non-hydrophobic filler is modified by a treatment which imparts hydrophobic properties to said surface.
Claim 14
Dependent Claim
29 words
The process of claim 9, wherein the hydrophobic filler is glass fiber whose surface is treated with a polyphenylene sulfide, thereby forming a hydrophobic surface on said glass fiber.
Claim 15
Dependent Claim
12 words
The process of claim 9, wherein the hydrophobic filler is carbon black.
Claim 16
Dependent Claim
27 words
The process of claim 9, wherein the hydrophobic filler is chromium oxide whose surface is treated with polytetrafluoroethylene thereby forming a hydrophobic surface on said chromium oxide.
Claim 17
Dependent Claim
21 words
The process of claim 9, wherein the hydrophobic filler is carbon fiber having an average length of 100 to 200 μm.
Claim 18
Dependent Claim
19 words
The process of claim 9, wherein the content of the filler in the mixture is 10 to 50 wt.%.
References Cited (Backward Citations)
US3265679A
Cited
US3882217A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-05 | 1982-09-04 | 1983-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-05 | 1986-09-04 | 1987-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-05 | 1990-09-04 | 1991-03-06 | $7700.00 | Window Closed / Lapsed |