US4143015A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Water base, non-polluting, slow leaching, anti-fouling paint
Assignee: Individual
•
Filing: 1977-01-21
•
Granted: 1979-03-06
•
Expires: 1997-01-21
Abstract
Abstract A water-base vinyl paint containing a toxicant for the protection of underwater surfaces from fouling growth. Suitable modified vinyl acetate resins are dissolved in a water solution brought to a pH of at least about 8 by a suitable poly-functional amine. A suitable toxicant, such as cuprous oxide is dispersed in the solution, and after the addition of modifiers, the finished product is then painted onto a surface to be protected from fouling growth when immersed into the ocean. The dried coating dissolves or leaches slowly in alkaline water, such as sea water, providing constantly fresh toxicant to prevent fouling growth. Desired characteristics of the coating may be modified by adding other agents, such as defoamers, urea formaldehyde resins, to the coating solution.
Inventors
- 👤 Ernolff Soeterik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:46
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/16; C09D5/1656; C09D5/1662; C09D161/00; C09D161/20; C09D161/22; C09D161/24; C08; C08L; C08L31/00; C08L31/02; C08L31/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
82 words
A water base paint resistant to fouling by marine organisms when exposed to sea water which comprises: (a) about 100 parts by weight water; (b) from about 12 to 60 parts by weight modified poly-vinyl acetate resin; (c) from about 6 to 30 parts by weight of a poly-functional amine having low volatility; (d) from about 15 to about 130 parts by weight liquid urea formaldehyde resin; and (e) from about 30 to 600 parts by weight of a finely divided toxicant.
Claim 2
Dependent Claim
82 words
A water base paint resistant to fouling by marine organisms when exposed to sea water which comprises: (a) about 100 parts by weight water; (b) from about 12 to 60 parts by weight modified poly-vinyl acetate resin; (c) from about 6 to 30 parts by weight of a poly-functional amine having low volatility; (d) from about 15 to about 130 parts by weight liquid urea formaldehyde resin; and (e) from about 30 to 600 parts by weight of a finely divided toxicant.
Claim 3
Dependent Claim
32 words
The paint according to claim 1 wherein said polyfunctional amine is selected from the group consisting of triethanol amine, tri-ethyl amine, tri-ethylene diamine, 2-dimethylamino-2-methyl-1-propanol, N,N-diethyl ethanolamine, 2-amino-2-methyl-1-propanol, N,N-dimethyl ethanolamine and mixtures thereof.
Claim 4
Dependent Claim
13 words
The paint according to claim 1 wherein said polyfunctional amine is tri-ethanol amine.
Claim 5
Dependent Claim
23 words
The paint according to claim 1 wherein said toxicant is selected from the group consisting of cuprous oxide, organo tin and mixtures thereof.
Claim 6
Dependent Claim
22 words
The paint according to claim 1 further including from 5 to 8 parts by weight defoamer per 100 parts by weight water.
Claim 7
Independent Claim
133 words
A method of manufacturing a water base paint which is resistant to fouling by marine organisms when exposed to sea water, which comprises the steps of: (a) placing in a mixer about 70 to 85 parts by weight water; (b) mixing therewith from about 12 to 60 parts by weight of a poly-functional amine having low volatility; (c) dissolving therein from about 6 to 36 parts by weight modified poly-vinyl acetate resin; (d) adding thereto from about 15 to 100 parts urea formaldehyde resin emulsion; (e) dispersing therein from about 30 to 600 parts of a toxicant; (f) mixing therewith sufficient water to bring the total water added to about 100 parts by weight; (g) mixing therewith sufficient urea formaldehyde resin emulsion to bring the solution pH to from about 8.5 to 9.
Claim 8
Independent Claim
133 words
A method of manufacturing a water base paint which is resistant to fouling by marine organisms when exposed to sea water, which comprises the steps of: (a) placing in a mixer about 70 to 85 parts by weight water; (b) mixing therewith from about 12 to 60 parts by weight of a poly-functional amine having low volatility; (c) dissolving therein from about 6 to 36 parts by weight modified poly-vinyl acetate resin; (d) adding thereto from about 15 to 100 parts urea formaldehyde resin emulsion; (e) dispersing therein from about 30 to 600 parts of a toxicant; (f) mixing therewith sufficient water to bring the total water added to about 100 parts by weight; (g) mixing therewith sufficient urea formaldehyde resin emulsion to bring the solution pH to from about 8.5 to 9.
Claim 9
Dependent Claim
32 words
The method according to claim 6 wherein said poly-functional amine is selected from the group consisting of tri-ethanol amine, tri-ethyl amine, tri-ethylene diamine, 2-dimethylamino-2-methyl-1-propanol, N,N-diethyl ethanolamine, 2-amino-2-methyl-1-propanol, N,N-dimethyl ethanolamine and mixtures thereof.
Claim 10
Dependent Claim
13 words
The method according to claim 6 wherein said polyfunctional amine is tri-ethanol amine.
Claim 11
Dependent Claim
23 words
The method according to claim 6 wherein said toxicant is selected from the group consisting of cuprous oxide, organo tin and mixtures thereof.
Claim 12
Dependent Claim
30 words
The method according to claim 6 further including the step of adding from about 5 to 8 parts by weight defoamer to the initial solution of water and poly-functional amine.
Claim 13
Dependent Claim
23 words
The method according to claim 6 wherein the temperature throughout is maintained in the range of from about 75° F. to 120° F.
References Cited (Backward Citations)
US2287218A
Cited
US3236793A
Cited
US3331693A
Cited
US3861949A
Cited
US4010141A
Cited
US3794501A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-05 | 1982-09-04 | 1983-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-05 | 1986-09-04 | 1987-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-05 | 1990-09-04 | 1991-03-06 | $7700.00 | Window Closed / Lapsed |