Method of producing cerium-activated phosphor of improved characteristic
Assignee: Panasonic Holdings Corp
•
Filing: 1977-11-10
•
Granted: 1979-02-27
•
Expires: 1997-11-10
Abstract
Abstract A phosphor expressed fundamentally as YA103:Ce is produced through baking under a usual condition of a mixture of Y2O3, Al2O3, CeO2 and a controlled amount of barium compound exemplified by BaCO3, BaO, Ba(OH)2 and BaF2. The presence of the barium compound in the mixture causes intensification of ultraviolet emission and/or suppression of the formation of blue-emitting Y3Al5O12:Ce. The use of BaF2 as the barium compound or partial replacement of at least one of Y2O3 and Al2O3 respectively by YF3 and AlF3 is favorable to the intensification of the ultraviolet emission.
Inventors
- 👤 Tetsuhiko Tomiki
- 👤 Takeshi Takeda
- 👤 Takeo Miyata
- 👤 Fumio Muramatsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:25
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7774
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
156 words
A method of producing a YAlO 3 :Ce phosphor, comprising the steps of: a. preparing a mixture of Y 2 O 3 , Al 2 O 3 and CeO 2 , the molar ratio of Y 2 O 3 to Al 2 O 3 being substantially 1:1, the amount of CeO 2 being such that cerium in said phosphor amounts to 0.1 to 5 mole% of YAlO 3 ; b. adding a barium compound selected from the group consisting of BaO, BaCO 3 , BaF 2 , BaCl 2 and barium salts which yield BaO at a temperature below 1400° C. to said mixture in an amount of 0.1 to 20 mole% of said mixture; c. baking the resultant mixture at a temperature in the range from about 1000° to about 1400° C.; and d. washing the product of step (c) with an acid when said amount of said barium compound is larger than 8 mole%.
Claim 2
Independent Claim
156 words
A method of producing a YAlO 3 :Ce phosphor, comprising the steps of: a. preparing a mixture of Y 2 O 3 , Al 2 O 3 and CeO 2 , the molar ratio of Y 2 O 3 to Al 2 O 3 being substantially 1:1, the amount of CeO 2 being such that cerium in said phosphor amounts to 0.1 to 5 mole% of YAlO 3 ; b. adding a barium compound selected from the group consisting of BaO, BaCO 3 , BaF 2 , BaCl 2 and barium salts which yield BaO at a temperature below 1400° C. to said mixture in an amount of 0.1 to 20 mole% of said mixture; c. baking the resultant mixture at a temperature in the range from about 1000° to about 1400° C.; and d. washing the product of step (c) with an acid when said amount of said barium compound is larger than 8 mole%.
Claim 3
Dependent Claim
24 words
A method as claimed in claim 1, wherein said salts are Ba(OH) 2 , Ba(NO 3 ) 2 and BaC 2 O 4 .
Claim 4
Dependent Claim
36 words
A method as claimed in claim 1, further comprising the step of baking said mixture prepared at step (a) at a temperature below about 1150° C. and then pulverizing the baked mixture prior to step (b).
Claim 5
Independent Claim
246 words
A method of producing a YAlO 3 :Ce phosphor, comprising the steps of: a. preparing a mixture of Y 2 O 3 , Al 2 O 3 , CeO 2 and at least one of YF 3 and AlF 3 , the molar ratio of (2YF 3 + Y 2 O 3 ) to (2AlF 3 + Al 2 O 3 ) being substantially 1:1, with the molar ratios 2YF 3 /Y 2 O 3 and 2AlF 3 /Al 2 O 3 being each in the range from 0.001 to 0.10 when YF 3 or AlF 3 is present, or with the sum of the molar ratios 2YF 3 /Y 2 O 3 and 2AlF 3 /Al 2 O 3 being in the range from 0.001 to 0.10 when both YF 3 and AlF 3 are present; the amount of CeO 2 being such that cerium in said phosphor amounts to 0.1 to 5 mole% of YAlO 3 ; b. adding a barium compound selected from the group consisting of BaO, BaCO 3 , BaF 2 , BaCl 2 and barium salts which yield BaO at a temperature below 1400° C. to said mixture in an amount of 0.1 to 20 mole% of said mixture; c. baking the resultant mixture at a temperature in the range from about 1000° to about 1400° C.; and d. washing the product of step (c) with an acid when said amount of said barium compound is larger than 8 mole%.
Claim 6
Independent Claim
246 words
A method of producing a YAlO 3 :Ce phosphor, comprising the steps of: a. preparing a mixture of Y 2 O 3 , Al 2 O 3 , CeO 2 and at least one of YF 3 and AlF 3 , the molar ratio of (2YF 3 + Y 2 O 3 ) to (2AlF 3 + Al 2 O 3 ) being substantially 1:1, with the molar ratios 2YF 3 /Y 2 O 3 and 2AlF 3 /Al 2 O 3 being each in the range from 0.001 to 0.10 when YF 3 or AlF 3 is present, or with the sum of the molar ratios 2YF 3 /Y 2 O 3 and 2AlF 3 /Al 2 O 3 being in the range from 0.001 to 0.10 when both YF 3 and AlF 3 are present; the amount of CeO 2 being such that cerium in said phosphor amounts to 0.1 to 5 mole% of YAlO 3 ; b. adding a barium compound selected from the group consisting of BaO, BaCO 3 , BaF 2 , BaCl 2 and barium salts which yield BaO at a temperature below 1400° C. to said mixture in an amount of 0.1 to 20 mole% of said mixture; c. baking the resultant mixture at a temperature in the range from about 1000° to about 1400° C.; and d. washing the product of step (c) with an acid when said amount of said barium compound is larger than 8 mole%.
Claim 7
Dependent Claim
25 words
A method as claimed in claim 4, wherein said barium salts are Ba(OH) 2 , Ba(NO 3 ) 2 and BaC 2 O 4 .
Claim 8
Dependent Claim
36 words
A method as claimed in claim 4, further comprising the step of baking said mixture prepared at step (a) at a temperature below about 1150° C. and then pulverizing the baked mixture prior to step (b).
References Cited (Backward Citations)
US2590411A
Cited
US3657138A
Cited
JPS493913A
Cited
DE2409953A1
Cited
JPS5097590A
Cited
DE2624544A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |