Bump circuits on tape utilizing chemical milling
Assignee: Hughes Missile Systems Co
•
Filing: 1978-01-30
•
Granted: 1979-02-27
•
Expires: 1998-01-30
Abstract
Abstract Carriers forming strips for semiconductor integrated circuit chips. The carrier consists basically of a flexible tape, such as a polyimide. A conductive sheet, such as a copper sheet, is initially prepared to form a lead circuit on one surface and a bump circuit on the other. This metal sheet may be gold plated. Subsequently, a layer of polyimide is applied to the lead circuit side and both the polyimide sheet and the opposite bump circuit are covered with a metal sheet, such as copper. A photoresist layer is put over the copper and is suitably illuminated and developed to provide apertures through which the copper can be etched to expose the polyimide sheet. This takes place over the windows or openings adjacent the bumps for the application of a heat ram as well as for the sprocket holes used for precisely aligning the carrier with the to-be-associated semiconductor chips. Finally, openings may also be provided to separate adjacent carrier strips from each other. The exposed polyimide layer is now removed by chemical milling. Subsequently the previously applied outer copper sheets are removed as by etching.
Inventors
- 👤 William P. Dugan
- 👤 Eugene Phillips
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:23
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/01; H10W70/04; H10W70/047; H05; H05K; H05K3/00; H05K3/0011; H05K3/0017; H05K3/002; H05K3/02; H05K3/06; H10W70/60; H10W70/67; H10W70/69; H10W70/695; H05K2201/00; H05K2201/01; H05K2201/0137; H05K2201/0154; H05K2201/03; H05K2201/0332; H05K2201/0364; H05K2201/0367; H05K2201/09; H05K2201/09209; H05K2201/09654; H05K2201/09736; H05K2203/00; H05K2203/03; H05K2203/0369; H05K2203/05; H05K2203/0548; H05K2203/0554; H05K3/061; H05K3/064; H05K3/10; H05K3/20; H05K3/202; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49126
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
154 words
A process for the manufacture of a flexible carrier for use with semiconductor integrated circuit chips and for making connections thereto, said carrier comprising a copper sheet having a lead circuit on one surface thereof and a bump circuit on its opposite side, the copper sheet being gold plated except for desired openings, said process comprising the following steps: (a) applying a sheet of a polyimide over the lead side of the carrier; (b) applying respective layers of copper to both sides of the carrier; (c) applying a layer of a photoresist to the lead side only; (d) illuminating the photoresist layer through a mask to provide desired openings representing sprocket holes, line separations between adjacent strips, and openings surrounding the bumps in the bump circuit; (e) developing the photoresist to remove the unexposed photoresist; (f) chemically milling through the exposed copper, thereby to remove the polyimide; and (g) removing both layers of copper.
Claim 2
Dependent Claim
154 words
A process for the manufacture of a flexible carrier for use with semiconductor integrated circuit chips and for making connections thereto, said carrier comprising a copper sheet having a lead circuit on one surface thereof and a bump circuit on its opposite side, the copper sheet being gold plated except for desired openings, said process comprising the following steps: (a) applying a sheet of a polyimide over the lead side of the carrier; (b) applying respective layers of copper to both sides of the carrier; (c) applying a layer of a photoresist to the lead side only; (d) illuminating the photoresist layer through a mask to provide desired openings representing sprocket holes, line separations between adjacent strips, and openings surrounding the bumps in the bump circuit; (e) developing the photoresist to remove the unexposed photoresist; (f) chemically milling through the exposed copper, thereby to remove the polyimide; and (g) removing both layers of copper.
Claim 3
Dependent Claim
25 words
A process as defined in claim 1 wherein the exposed polyimide layer is removed by etching it in a plasma with oxygen and carbon tetrafluoride.
Claim 4
Dependent Claim
25 words
A process as defined in claim 1 including the additional step of etching the carrier where exposed by the gold plating to provide sprocket holes.
Claim 5
Dependent Claim
28 words
A process as defined in claim 1 including the additional step of etching the carrier where exposed by the gold plating through the line separation between adjacent strips.
Claim 6
Dependent Claim
25 words
A process as defined in claim 1 wherein the copper layers are applied to both sides of the carrier by means of adhesive copper sheets.
Claim 7
Dependent Claim
24 words
A process as defined in claim 1 wherein the copper layers are applied to both sides of the carrier by electroless plating with copper.
Claim 8
Dependent Claim
21 words
A process as defined in claim 1 including the additional step of removing the remaining photoresist after chemically milling the polyimide.
Claim 9
Dependent Claim
21 words
A process as defined in claim 1 wherein the remaining photoresist is removed by chemical milling together with the exposed polyimide.
Claim 10
Dependent Claim
162 words
A process for the manufacture of a flexible carrier for use with semiconductor integrated circuit chips and for making connections thereto, said carrier comprising an electrically conductive metal sheet having a lead circuit on one surface thereof, and a bump circuit on its opposite side, the conductive sheet being plated with a metal resistant to a chemical etchant for the conductive sheet, the plating not extending to desired openings, said process comprising the following steps: (a) applying a sheet of a polyimide over the lead side of the conductive metal sheet; (b) applying an additional layer of a conductive metal to both the lead circuit and the bump circuit; (c) applying a layer of a photoresist to the lead side only; (d) illuminating the photoresist layer through a mask to provide desired openings; (e) developing the photoresist to remove the unexposed photoresist; (f) chemically milling the exposed polyimide, thereby to remove it; and (g) removing both layers of the conductive, metal layers.
Claim 11
Dependent Claim
162 words
A process for the manufacture of a flexible carrier for use with semiconductor integrated circuit chips and for making connections thereto, said carrier comprising an electrically conductive metal sheet having a lead circuit on one surface thereof, and a bump circuit on its opposite side, the conductive sheet being plated with a metal resistant to a chemical etchant for the conductive sheet, the plating not extending to desired openings, said process comprising the following steps: (a) applying a sheet of a polyimide over the lead side of the conductive metal sheet; (b) applying an additional layer of a conductive metal to both the lead circuit and the bump circuit; (c) applying a layer of a photoresist to the lead side only; (d) illuminating the photoresist layer through a mask to provide desired openings; (e) developing the photoresist to remove the unexposed photoresist; (f) chemically milling the exposed polyimide, thereby to remove it; and (g) removing both layers of the conductive, metal layers.
Claim 12
Dependent Claim
21 words
A process as defined in claim 9 wherein the remaining photoresist is removed by chemical milling along with the exposed polyimide.
Claim 13
Dependent Claim
18 words
A process as defined in claim 9 wherein the remaining photoresist is removed after the chemical milling step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |