Forming a lubricating and release coating on metal mold and treated metal surface
Assignee: Ball Corp
•
Filing: 1976-08-06
•
Granted: 1979-02-20
•
Expires: 1996-08-06
Abstract
Abstract Release and lubricating compositions are disclosed for avoiding seizure between molten glass and metal molds for forming glass articles and for improving the quality of glassware produced therefrom, comprising an aqueous dispersion containing polyphenylene sulfide, an inorganic binder, and a solid lubricant. The inorganic binder may be represented by the general formula MPO 4 wherein M is a metal ion selected from the group consisting of aluminum, chromium, magnesium, iron and zinc. The particular solid lubricants include members selected from the group consisting of graphite, molybdenum disulfide, polyterafluorethylene, and mixtures thereof.
Inventors
- 👤 Arnold F. Marcantonio
- 👤 Paul J. Kress
- 👤 Gene A. Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:55
CPC Classifications
C; C03; C03B; C03B40/00; C03B40/02; C10; C10M; C10M111/00; C10M7/00; C10M2201/00; C10M2201/04; C10M2201/041; C10M2201/042; C10M2201/06; C10M2201/065; C10M2201/066; C10M2201/085; C10M2209/00; C10M2209/10; C10M2209/103; C10M2209/104; C10M2211/00; C10M2211/06; C10M2213/00; C10M2213/02; C10M2213/06; C10M2213/062; C10M2221/00; C10N; C10N2050/00; C10N2050/08; C10N2050/10; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998; Y10T428/30; Y10T428/31504; Y10T428/31533; Y10T428/3154; Y10T428/31678; Y10T428/31692; Y10T428/31855; Y10T428/31909; Y10T428/31928
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
134 words
A treated metal surface for forming hot glass articles consisting essentially of a metal surface having securely adhered thereto a coating consisting essentially of a water-free remainder of an aqueous dispersion consisting essentially of about 5 to 40 weight percent polyphenylene sulfide having a molecular weight in excess of 1000, about 30 to 80 weight percent inorganic binder having the formula MPO 4 wherein M is a metal ion selected from the group consisting of aluminum, chromium, magnesium, iron, zinc and mixtures thereof, and about 10 to 40 weight percent of a solid lubricant selected from the group consisting of graphite, molybdenum disulfide, polytetrafluoroethylene and mixtures thereof, the balance being essentially water, said coating being from about 0.5 to about 5 mils in thickness and having improved elongation, impact resistance and thermal stability characteristics.
Claim 2
Dependent Claim
134 words
A treated metal surface for forming hot glass articles consisting essentially of a metal surface having securely adhered thereto a coating consisting essentially of a water-free remainder of an aqueous dispersion consisting essentially of about 5 to 40 weight percent polyphenylene sulfide having a molecular weight in excess of 1000, about 30 to 80 weight percent inorganic binder having the formula MPO 4 wherein M is a metal ion selected from the group consisting of aluminum, chromium, magnesium, iron, zinc and mixtures thereof, and about 10 to 40 weight percent of a solid lubricant selected from the group consisting of graphite, molybdenum disulfide, polytetrafluoroethylene and mixtures thereof, the balance being essentially water, said coating being from about 0.5 to about 5 mils in thickness and having improved elongation, impact resistance and thermal stability characteristics.
Claim 3
Dependent Claim
16 words
The treated metal surface of claim 1 wherein said aqueous dispersion also includes a wetting agent.
Claim 4
Independent Claim
149 words
A method of forming a lubricating and release coating on a metal mold surface which contacts hot glass material during the molding thereof, comprising applying to said metal mold surface an aqueous dispersion consisting essentially of about 5 to 40 weight percent polyphenylene sulfide having a molecular weight in excess of 1000, about 30 to 80 weight percent inorganic binder having the formula MPO 4 wherein M is a metal ion selected from the group consisting of aluminum, chromium, magnesium, iron, zinc and mixtures thereof, and about 10 to 40 weight percent of a solid lubricant selected from the group consisting of graphite, molybdenum disulfide, polytetrafluoroethylene, and mixtures thereof, the balance being essentially water, and heating said surface and said dispersion applied thereto to remove the water of said dispersion so as to form on said surface a thin coating having improved elongation, impact resistance and thermal stability characteristics.
Claim 5
Independent Claim
149 words
A method of forming a lubricating and release coating on a metal mold surface which contacts hot glass material during the molding thereof, comprising applying to said metal mold surface an aqueous dispersion consisting essentially of about 5 to 40 weight percent polyphenylene sulfide having a molecular weight in excess of 1000, about 30 to 80 weight percent inorganic binder having the formula MPO 4 wherein M is a metal ion selected from the group consisting of aluminum, chromium, magnesium, iron, zinc and mixtures thereof, and about 10 to 40 weight percent of a solid lubricant selected from the group consisting of graphite, molybdenum disulfide, polytetrafluoroethylene, and mixtures thereof, the balance being essentially water, and heating said surface and said dispersion applied thereto to remove the water of said dispersion so as to form on said surface a thin coating having improved elongation, impact resistance and thermal stability characteristics.
Claim 6
Dependent Claim
14 words
The method of claim 3 wherein said aqueous dispersion also includes a wetting agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-19 | 1982-08-21 | 1983-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-19 | 1986-08-21 | 1987-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-19 | 1990-08-21 | 1991-02-20 | $7700.00 | Window Closed / Lapsed |