Cell and process for electrolyzing aqueous solutions using a porous anode separator
Assignee: Olin Corp
•
Filing: 1977-03-28
•
Granted: 1979-02-20
•
Expires: 1997-03-28
Abstract
Abstract Electrolysis of alkali metal chloride solutions to produce chlorine and alkali metal hydroxides is accomplished in a cell comprising an anode compartment, a cathode compartment, a cation permeable divider separating the anode compartment from the cathode compartment, where the anode compartment contains an anode separator. The anode separator is comprised of a porous plate of a valve metal having an electrochemically active coating on the face, and an electrochemically non-active barrier layer on the back and a portion of the interior. The anode separator is positioned in the anode compartment so that the back of the anode separator is spaced apart from the cation permeable divider. An alkaline brine zone is formed between the anode separator and the cation permeable divider which increases the service life of the cation permeable divider. In addition, the anode separator provides improved chlorine gas separation properties, increased service life for the electroconductive coating on the face, and enables the cell to operate with a reduced cell voltage.
Inventors
- 👤 Igor V. Kadija
- 👤 Byung K. Ahn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:14
CPC Classifications
C; C25; C25B; C25B1/00; C25B1/01; C25B1/34; C25B1/46; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091; C25B9/00; C25B9/17; C25B9/19
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
198 words
A cell for electrolyzing alkali metal chloride solutions comprised of an anode compartment, a cathode compartment, a cation permeable divider separating said anode compartment from said cathode compartment, a cathode in said cathode compartment, an anode separator serving as the anode in said anode compartment, wherein said anode separator is comprised of a porous plate of a valve metal selected from the group consisting of titanium, tantalum and niobium, said porous plate having a face, a back and an interior structure, said face having an electrochemically active coating selected from the group consisting of a platinum group metal, a platinum group metal oxide and mixtures thereof, said back and a portion of said interior having an electrochemically non-active barrier layer, said electrochemically non-active barrier layer comprising a mixture of a valve metal oxide selected from the group consisting of titanium oxide, tantalum oxide and niobium oxide with a ceramic oxide selected from the group consisting of silicon oxide, aluminum oxide, magnesium oxide, calcium oxide and mixtures thereof, wherein said portion having said barrier layer is at least 10 percent of said interior structure, and said cation permeable divider is spaced apart from said back of said anode separator.
Claim 2
Dependent Claim
198 words
A cell for electrolyzing alkali metal chloride solutions comprised of an anode compartment, a cathode compartment, a cation permeable divider separating said anode compartment from said cathode compartment, a cathode in said cathode compartment, an anode separator serving as the anode in said anode compartment, wherein said anode separator is comprised of a porous plate of a valve metal selected from the group consisting of titanium, tantalum and niobium, said porous plate having a face, a back and an interior structure, said face having an electrochemically active coating selected from the group consisting of a platinum group metal, a platinum group metal oxide and mixtures thereof, said back and a portion of said interior having an electrochemically non-active barrier layer, said electrochemically non-active barrier layer comprising a mixture of a valve metal oxide selected from the group consisting of titanium oxide, tantalum oxide and niobium oxide with a ceramic oxide selected from the group consisting of silicon oxide, aluminum oxide, magnesium oxide, calcium oxide and mixtures thereof, wherein said portion having said barrier layer is at least 10 percent of said interior structure, and said cation permeable divider is spaced apart from said back of said anode separator.
Claim 3
Dependent Claim
14 words
A process for electrolyzing alkali metal chloride solutions employing the cell of claim 1.
Claim 4
Dependent Claim
39 words
The cell of claim 1 in which said cation permeable divider is spaced apart from said back of said anode separator a distance of from about 1/50th to about 1/2 of an inch to provide an alkaline brine zone.
Claim 5
Dependent Claim
14 words
A process for electrolyzing alkali metal chloride solutions employing the cell of claim 3.
Claim 6
Dependent Claim
23 words
The cell of claim 3 in which said anode separator has a thickness of from about 1/16th to about 1/2 of an inch.
Claim 7
Dependent Claim
35 words
The cell of claim 5 in which said anode separator has a porosity of from about 30 percent to about 75 percent and a pore size of from about 5 microns to about 500 microns.
Claim 8
Dependent Claim
23 words
The cell of claim 6 in which said porous plate has a foraminous structure of a valve metal enveloped by said porous plate.
Claim 9
Dependent Claim
15 words
The cell of claim 7 in which said foraminous structure is an expanded titanium mesh.
Claim 10
Dependent Claim
19 words
The cell of claim 1 in which said valve metal is titanium and said ceramic oxide is silicon oxide.
Claim 11
Dependent Claim
23 words
The cell of claim 9 in which said valve metal oxide is selected from the group consisting of titanium oxide and tantalum oxide.
Claim 12
Dependent Claim
32 words
The cell of claim 10 in which the cation permeable divider is selected from the group consisting of perfluorosulfonic acid resins having an equivalent weight of from about 900 to about 1600.
Claim 13
Dependent Claim
14 words
A process for electrolyzing alkali metal chloride solutions employing the cell of claim 10.
Claim 14
Dependent Claim
32 words
The cell of claim 1 in which said valve metal oxide is titanium oxide and said ceramic oxide is selected from the group consisting of silicon oxide, aluminum oxide and mixtures thereof.
Claim 15
Dependent Claim
36 words
The cell of claim 13 in which said electrochemically active coating is a platinum group metal oxide selected from the group consisting of platinum oxide, palladium oxide, iridium oxide, ruthenium oxide, rhodium oxide and osmium oxide.
Claim 16
Dependent Claim
14 words
The cell of claim 14 in which said electrochemically active coating is ruthenium oxide.
Claim 17
Dependent Claim
32 words
The cell of claim 15 in which said cation permeable divider is selected from the group consisting of perfluorosulfonic acid resins having an equivalent weight of from about 900 to about 1600.
Claim 18
Dependent Claim
13 words
A process for electrolyzing sodium chloride solutions employing the cell of claim 16.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-19 | 1982-08-21 | 1983-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-19 | 1986-08-21 | 1987-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-19 | 1990-08-21 | 1991-02-20 | $7700.00 | Window Closed / Lapsed |