Patent US4140523A successfully refreshed from Google Patents.
US4140523A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Chemicothermal production of magnesium
Assignee: Dow Chemical Co
•
Filing: 1977-11-28
•
Granted: 1979-02-20
•
Expires: 1997-11-28
Abstract
Abstract Magnesium metal is produced in a two-stage chemicothermal process employing metallothermic reduction of MgO using Al metal, present in an Al alloy, as the reducing metal in one stage according to the reaction 2Al + 3MgO .sup.Δ 3Mg + Al.sub.2 O.sub.3 and employing a carbothermic reduction, Al.sub.2 O.sub.3 + 3C .sup.Δ 2Al + 3CO in the other stage to regenerate the Al metal for recycling back to the metallothermic reduction step. The process substantially avoids the reversion reaction, Mg + CO → MgO + C, by separating the formation of Mg from that of CO (carbon monoxide) and does not rely on having to remove slag from the reactors.
Inventors
- 👤 Philip O. Haddad
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:01
CPC Classifications
C; C22; C22B; C22B5/00; C22B5/02; C22B5/04; C22B26/00; C22B26/20; C22B26/22; C22B5/10; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
170 words
A chemicothermal process for producing Mg metal from MgO, said process comrising feeding particulate MgO to a MgO-reduction vessel containing molten Al alloy, thereby forming a molten Al 2 O 3 slag on the molten Al alloy and releasing Mg metal as a vapor from the vessel, transferring the so-formed Al 2 O 3 slag, along with some of the used molten Al alloy, to an Al 2 O 3 -reduction vessel in which the Al alloy is kept molten, feeding particulate carbon to the contents of the Al 2 O 3 -reduction vessel, thereby reacting it with the Al 2 O 3 to form CO, which is released from the vessel, and Al metal which recombines with the molten Al alloy which is cycled to the MgO-reduction vessel, wherein the temperature in the MgO-reduction vessel is maintained in the range of about 2000° to about 2300° C. and the temperature in the Al 2 O 3 -reduction vessel is in the range of about 1850° to about 2300° C.
Claim 2
Dependent Claim
170 words
A chemicothermal process for producing Mg metal from MgO, said process comrising feeding particulate MgO to a MgO-reduction vessel containing molten Al alloy, thereby forming a molten Al 2 O 3 slag on the molten Al alloy and releasing Mg metal as a vapor from the vessel, transferring the so-formed Al 2 O 3 slag, along with some of the used molten Al alloy, to an Al 2 O 3 -reduction vessel in which the Al alloy is kept molten, feeding particulate carbon to the contents of the Al 2 O 3 -reduction vessel, thereby reacting it with the Al 2 O 3 to form CO, which is released from the vessel, and Al metal which recombines with the molten Al alloy which is cycled to the MgO-reduction vessel, wherein the temperature in the MgO-reduction vessel is maintained in the range of about 2000° to about 2300° C. and the temperature in the Al 2 O 3 -reduction vessel is in the range of about 1850° to about 2300° C.
Claim 3
Dependent Claim
69 words
The process of claim 1 wherein the process is run continuously by cycling the molten Al alloy from the Al 2 O 3 -reduction vessel back to the MgO-reduction vessel while feeding requisite amounts of MgO to the MgO-reduction vessel and carbon to the Al 2 O 3 -reduction vessel and continuously removing Mg vapor from the MgO-reduction vessel and CO from the Al 2 O 3 -reduction vessel.
Claim 4
Dependent Claim
52 words
The process of claim 1 wherein the temperature of the molten Al alloy and slag in the MgO-reduction vessel is in the range of about 2030° to about 2100° C. and the temperature in the Al 2 O 3 -reduction vessel is in the range of about 1950° to about 2100° C.
Claim 5
Dependent Claim
38 words
The process of claim 1 wherein the ratio of Al 2 O 3 /Al alloy going from the MgO-reduction vessel to the Al 2 O 3 -reduction vessel is in the range of about 0.04 to about 5.0.
Claim 6
Dependent Claim
57 words
The process of claim 1 wherein the cycling of molten Al alloy from the Al 2 O 3 -reduction vessel to the MgO-reduction vessel is performed by using a gas-lift pump to lift molten Al alloy from beneath the slag layer in the Al 2 O 3 -reduction vessel into the slag layer in the MgO-reduction vessel.
Claim 7
Dependent Claim
21 words
The process of claim 1 wherein an inert gas atmosphere is employed in the MgO-reduction vessel to exclude air and moisture.
Claim 8
Dependent Claim
57 words
The process of claim 2 wherein the weight ratio of MgO/Al alloy being fed into the MgO-reduction vessel is in the range of about 0.5 to about 1.0, and the weight ratio of carbon/Al 2 O 3 being fed into the Al 2 O 3 -reduction vessel, is in the range of about 0.35 to about 0.4.
Claim 9
Dependent Claim
38 words
The process of claim 1 wherein the molten Al alloy contains at least about 10% Al by weight alloyed with at least one metal selected from the group consisting of Cu, Si, Fe, Sn, Ni, Co, and Cr.
Claim 10
Dependent Claim
29 words
The process of claim 8 wherein the molten Al alloy is an Al-Cu alloy having a weight ratio of Al in the range of about 10% to about 75%.
Claim 11
Dependent Claim
18 words
The process of claim 9 wherein the Al alloy contains about 10% to about 45% Al by weight.
Claim 12
Dependent Claim
134 words
A chemicothermal process for producing Mg metal from MgO, said process comprising feeding particulate MgO to a MgO-reduction vessel containing molten Al alloy at a temperature of about 2000° to about 2300° C., thereby forming a molten Al 2 O 3 slag on the molten Al alloy and releasing Mg metal as a vapor from the vessel, transfering the so-formed Al 2 O 3 slag to an Al 2 O 3 -reduction vessel in which an Al alloy is kept molten at a temperature of about 1850° to about 2300° C., and feeding particulate carbon to the contents of the Al 2 O 3 -reduction vessel, thereby reacting it with the Al 2 O 3 to form CO, which is released from the vessel, and Al metal which combines with the molten Al alloy.
Claim 13
Dependent Claim
134 words
A chemicothermal process for producing Mg metal from MgO, said process comprising feeding particulate MgO to a MgO-reduction vessel containing molten Al alloy at a temperature of about 2000° to about 2300° C., thereby forming a molten Al 2 O 3 slag on the molten Al alloy and releasing Mg metal as a vapor from the vessel, transfering the so-formed Al 2 O 3 slag to an Al 2 O 3 -reduction vessel in which an Al alloy is kept molten at a temperature of about 1850° to about 2300° C., and feeding particulate carbon to the contents of the Al 2 O 3 -reduction vessel, thereby reacting it with the Al 2 O 3 to form CO, which is released from the vessel, and Al metal which combines with the molten Al alloy.
Claim 14
Dependent Claim
121 words
The process of claim 11 wherein the content of the Al in the Al alloy in the MgO-reduction vessel is maintained in the range of about 10% to about 75% by adding make-up Al at a rate commensurate with the amount of Al leaving the MgO-reduction vessel as Al 2 O 3 , and wherein the content of the Al in the Al alloy in the Al 2 O 3 -reduction vessel is maintained in the range of about 10% to about 45% by withdrawing Al alloy at a rate commensurate with the amount of Al being formed from Al 2 O 3 and by adding a make-up amount of alloying agent to replace that which is removed as Al alloy.
References Cited (Backward Citations)
US2396658A
Cited
GB922300A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-19 | 1982-08-21 | 1983-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-19 | 1986-08-21 | 1987-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-19 | 1990-08-21 | 1991-02-20 | $7700.00 | Window Closed / Lapsed |