Method of fabricating composite structures for water cooled gas turbine components
Assignee: General Electric Co
•
Filing: 1977-10-03
•
Granted: 1979-02-06
•
Expires: 1997-10-03
Abstract
Abstract A method is provided for fabricating complex composite components for water-cooled, high temperature gas turbines. Each component comprises a core, a thermally conducting layer of copper bonded to the core, metal tubing through which water may pass embedded in and bonded to the layer, and a corrosion resistant cladding. The method utilizes powder metallurgy techniques to form the thermally conducting layer and hot isostatic pressure to bond the corrosion resistant cladding spar and tubes to said layer.
Inventors
- 👤 Adrian M. Beltran
- 👤 Myron C. Muth
- 👤 William F. Schilling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:24
CPC Classifications
F; F01; F01D; F01D5/00; F01D5/12; F01D5/14; F01D5/18; F01D5/187; B; B22; B22F; B22F5/00; B22F5/04; B22F7/00; B22F7/06; B22F7/08; B23; B23P; B23P15/00; B23P15/04; F01D5/28; F01D5/288; Y; Y02; Y02T; Y02T50/00; Y02T50/60; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/49336; Y10T29/49339; Y10T29/49341; Y10T29/49343
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
180 words
A method of making a water-cooled, high temperature turbine article comprising the steps of: a. forming a preshaped body comprising a spar and two rigid endwalls having openings extending through said endwalls and said endwalls extending beyond said spar and defining a space between them, b. placing a multiplicity of cooling tubes along locations on the outer surface of said spar and extending through the openings of the endwalls, and forming a leak tight joint between the tubing and the endwalls, c. enclosing the predefined space with metal panels to form an internal cavity with the spar and cooling tubes therein; d. filling the internal cavity between the metal panels and the spar with a metal powder selected from the group consisting of copper, copper alloy, nickel and nickel alloy, e. consolidating the powder by hot isostatic pressing while maintaining said tubes open to gas pressure, f. removing the excess metal by machining to form said turbine article with a heat conducting layer having cooling tubes embedded therein; and g. attaching a corrosion resistant cladding over said heat conducting layer.
Claim 2
Independent Claim
180 words
A method of making a water-cooled, high temperature turbine article comprising the steps of: a. forming a preshaped body comprising a spar and two rigid endwalls having openings extending through said endwalls and said endwalls extending beyond said spar and defining a space between them, b. placing a multiplicity of cooling tubes along locations on the outer surface of said spar and extending through the openings of the endwalls, and forming a leak tight joint between the tubing and the endwalls, c. enclosing the predefined space with metal panels to form an internal cavity with the spar and cooling tubes therein; d. filling the internal cavity between the metal panels and the spar with a metal powder selected from the group consisting of copper, copper alloy, nickel and nickel alloy, e. consolidating the powder by hot isostatic pressing while maintaining said tubes open to gas pressure, f. removing the excess metal by machining to form said turbine article with a heat conducting layer having cooling tubes embedded therein; and g. attaching a corrosion resistant cladding over said heat conducting layer.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein said body is cast from an alloy selected from the group consisting of a nickel-base alloy, and a chromium-nickel-iron alloy.
Claim 4
Dependent Claim
14 words
The method of claim 2, wherein said tubes are formed from a chromium-nickel-iron alloy.
Claim 5
Dependent Claim
10 words
The method of claim 2, wherein said tubes are monel.
Claim 6
Dependent Claim
25 words
The method of claim 2, wherein said corrosion resistant cladding is an alloy consisting essentially of 50-80% by weight nickel and 20-50% by weight chromium.
Claim 7
Dependent Claim
14 words
The method of claim 1, wherein said metal powder is copper or copper alloy.
Claim 8
Dependent Claim
13 words
The method of claim 1, wherein said powder is nickel or nickel alloy.
Claim 9
Dependent Claim
36 words
The method of claim 1, wherein said hot isostatic pressing occurs at a temperature of about 1500°-1900° F., at a pressure of 1-25 Ksi and for a time of 0.5-4 hours to provide substantially theoretical density.
Claim 10
Dependent Claim
25 words
The method of claim 8, wherein said body is cast from a chromium-nickel-iron alloy, said powder is copper and said corrosion resistant cladding is Ni-50Cr.
Claim 11
Dependent Claim
21 words
The method of claim 8, wherein said hot isostatic pressing occurs at 1800° F., at 10 Ksi and for 2 hours.
References Cited (Backward Citations)
US2888241A
Cited
US3623825A
Cited
GB1301524A
Cited
US3773506A
Cited
DE2245705A1
Cited
US3748110A
Cited
US3928901A
Cited
US3952939A
Cited
US4017210A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-05 | 1982-08-07 | 1983-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-05 | 1986-08-07 | 1987-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-05 | 1990-08-07 | 1991-02-06 | $7700.00 | Window Closed / Lapsed |