Catalyst and method for making
Assignee: RTX Corp
•
Filing: 1977-11-23
•
Granted: 1979-01-30
•
Expires: 1997-11-23
Abstract
Abstract The rate of platinum recrystallization of a platinum supported on carbon catalyst is reduced by depositing porous carbon on and around the supported platinum crystallites. The reduced rate of platinum recrystallization results in higher platinum surface areas over a period of time and therefore improves the performance of the catalyst. The porous carbon can be deposited by any suitable technique, a preferred method being to heat the supported platinum in the presence of carbon monoxide to decompose the carbon monoxide thereby depositing carbon on and around the platinum crystallites.
Inventors
- 👤 Vinod M. Jalan
- 👤 Calvin L. Bushnell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:52
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/92; H01M4/925; H01M4/926; B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J23/42; H01M4/96; H01M2004/8678; H01M2004/8684; H01M2004/8689; H01M2300/00; H01M2300/0002; H01M2300/0005; H01M2300/0008; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
26 words
A method for improving a catalyst of platinum crystallites supported on carbon comprising the step of depositing porous carbon on and around the supported platinum crystallites.
Claim 2
Independent Claim
26 words
A method for improving a catalyst of platinum crystallites supported on carbon comprising the step of depositing porous carbon on and around the supported platinum crystallites.
Claim 3
Dependent Claim
30 words
The method according to claim 1 wherein said step of depositing includes heating the catalyst in the presence of a carbonaceous compound to decompose said compound to form porous carbon.
Claim 4
Dependent Claim
32 words
The method according to claim 2 wherein said carbonaceous compound is in the form of a gas or vapor and said catalyst is heated in the presence of said gas or vapor.
Claim 5
Dependent Claim
13 words
The method according to claim 3 wherein said carbonaceous compound is carbon monoxide.
Claim 6
Dependent Claim
36 words
The method according to claim 4 wherein said step of heating includes heating to within the temperature range of 500° F. to 1200° F. and holding the temperature within said range for one to sixty minutes.
Claim 7
Dependent Claim
29 words
The method according to claim 5 wherein said temperature range is 500° F. to 800° F. and the temperature is held within said range for five to thirty minutes.
Claim 8
Dependent Claim
30 words
The method according to claim 4 wherein said step of heating includes heating to a maximum temperature of about 700° F. and holding said maximum temperature for about ten minutes.
Claim 9
Dependent Claim
42 words
The method according to claim 3 wherein said carbonaceous compound is a hydrocarbon vapor or gas, and said step of heating includes heating to a temperature sufficiently high to decompose the hydrocarbon to deposit porous carbon on and around the platinum crystallites.
Claim 10
Dependent Claim
23 words
The method according to claim 8 wherein said hydrocarbon is selected from the group consisting of n-hexene, heptane, benzene, acetylene, methane or ethylene.
Claim 11
Dependent Claim
61 words
The method according to claim 2 wherein said carbonaceous material is a soluble organic material and said step of depositing carbon includes applying a layer of said soluble organic material on the catalyst and then heating the catalyst in an inert atmosphere or vacuum to decompose the organic material in said layer leaving porous carbon on and around the platinum crystallites.
Claim 12
Dependent Claim
40 words
The method according to claim 10 wherein the step of applying a layer of soluble organic material comprises soaking said catalyst in an aqueous solution of said organic material and drying the catalyst to remove the water from the layer.
Claim 13
Dependent Claim
12 words
The method according to claim 2 wherein said carbonaceous material is sucrose.
Claim 14
Dependent Claim
13 words
The method according to claim 11 wherein said soluble organic material is sucrose.
Claim 15
Dependent Claim
36 words
The method according to claim 13 wherein said step of heating includes heating to within the temperature range of 800° F. to 1200° F. and holding the temperature within said range for one-half to six hours.
Claim 16
Dependent Claim
41 words
An improved catalyst comprising platinum crystallites supported on carbon particles, porous carbon having been deposited on and around said crystallites to reduce migration of said crystallites on the surface of said carbon particles during subsequent treatment or use of said catalyst.
Claim 17
Dependent Claim
41 words
An improved catalyst comprising platinum crystallites supported on carbon particles, porous carbon having been deposited on and around said crystallites to reduce migration of said crystallites on the surface of said carbon particles during subsequent treatment or use of said catalyst.
Claim 18
Dependent Claim
43 words
The improved catalyst according to claim 15 wherein said deposited carbon was applied by heating the catalyst without the porous carbon deposits in the presence of a carbonaceous compound which decomposed to form said porous carbon deposits on and around said platinum crystallites.
Claim 19
Dependent Claim
15 words
The improved catalyst according to claim 16 wherein said carbonaceous compound was carbon monoxide gas.
Claim 20
Dependent Claim
17 words
The improved catalyst according to claim 16 wherein said carbonaceous compound was a hydrocarbon vapor or gas.
Claim 21
Dependent Claim
13 words
The improved catalyst according to claim 16 wherein said carbonaceous compound was sucrose.
Claim 22
Dependent Claim
24 words
A fuel cell electrode including an improved catalyst comprising platinum crystallites supported on carbon particles, said crystallites having porous carbon deposited thereon and therearound.
Claim 23
Dependent Claim
24 words
A fuel cell electrode including an improved catalyst comprising platinum crystallites supported on carbon particles, said crystallites having porous carbon deposited thereon and therearound.
Claim 24
Dependent Claim
43 words
The electrode according to claim 20 wherein said deposited porous carbon was applied by heating the catalyst without the porous carbon deposits in the presence of a carbonaceous compound which decomposed to form said porous carbon deposits on and around said platinum crystallites.
Claim 25
Dependent Claim
52 words
The electrode according to claim 20 wherein said deposited porous carbon was applied by heating the catalyst without the porous carbon deposits in the presence of carbon monoxide gas to within the temperature range of 500° F. to 1200° F. and holding the temperature within said range for one to sixty minutes.
Claim 26
Dependent Claim
52 words
The electrode according to claim 20 wherein said deposited porous carbon was applied by heating the catalyst without the porous carbon deposits in the presence of carbon monoxide gas to within the temperature range of 500° F. to 800° F. and holding the temperature within said range for five to thirty minutes.
Claim 27
Dependent Claim
46 words
The electrode according to claim 20 wherein said deposited porous carbon was applied by heating the catalyst without the porous carbon deposits in the presence of carbon monoxide gas to a maximum temperature of about 700° F. and holding said maximum temperature for about ten minutes.
Claim 28
Dependent Claim
61 words
The fuel cell electrode according to claim 20 wherein said deposited porous carbon was applied by applying a layer of a soluble organic material on the catalyst without the porous carbon deposits, and heating said catalyst in an inert atmosphere or vacuum to decompose the organic material in said layer leaving said porous carbon deposits on and around said platinum crystallites.
Claim 29
Dependent Claim
13 words
The electrode according to claim 25 wherein said soluble organic material was sucrose.
Claim 30
Dependent Claim
43 words
The electrode according to claim 25 wherein said heating of the catalyst in an inert atmosphere or vacuum included heating to within the temperature range of 800° F. to 1200° F. and holding the temperature within said range for one-half to six hours.
Claim 31
Dependent Claim
45 words
The electrode according to claim 20 wherein said deposited porous carbon was applied by heating the catalyst without the porous carbon deposits in the presence of a hydrocarbon gas or vapor which decomposed to form said porous carbon deposits on and around said platinum crystallites.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-29 | 1982-07-31 | 1983-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-29 | 1986-07-31 | 1987-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-29 | 1990-07-31 | 1991-01-30 | $7700.00 | Window Closed / Lapsed |