Process for treating acicular magnetite containing co to stabilize the magnetic properties thereof
Assignee: Toda Kogyo Corp
•
Filing: 1977-08-01
•
Granted: 1979-01-23
•
Expires: 1997-08-01
Abstract
Abstract A process for treating acicular magnetite containing Co to stabilize the magnetic properties thereof comprises the steps of heating acicular magnetite containing 0.1 to 2.5% by atom of Co with respect to Fe as starting material at a temperature in the range of 300 - 1000° C in an inert gas atmosphere in which the partial pressure of oxygen is controlled at a value in the range of 0.001 - 1% by weight and for the time sufficient to homogenize the crystal structure of the acicular magnetite by thermal-diffusion of oxygen thereinto, and thereafter saturating the resultant acicular magnetite with oxygen by heating it at a temperature in the range of 40 - 100° C in an oxygen rich atmosphere such as air.
Inventors
- 👤 Nanao Horiishi
- 👤 Atushi Takedoi
- 👤 Hiroyuki Kondo
- 👤 Hiroshi Sumita
- 👤 Akira Mukaizaka
- 👤 Goro Matsui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:21
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70678; G11B5/70684; G11B5/70689
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
184 words
A process for treating acicular magnetite containing Co to stabilize the magnetic properties against change with lapse of time, comprising the steps of: heating acicular magnetite having a Fe 2+ /Fe 3+ weight ratio in the range of 0.3 to 0.49 and containing 0.1 to 2.5% by atom of Co with respect to Fe as starting material at a temperature in the range of 300-1000° C. in an inert gas atmosphere in which the partial pressure of oxygen is controlled at a value in the range of 0.001-1% by weight and for a time sufficient to effect the equilibrium partial pressure of oxygen in accordance with Gibb's phase rule, and thereafter saturating the resultant acicular magnetite with oxygen by heating it at a temperature in the range of 40 to 100° C. in an air atmosphere while substantially retaining the value of the Fe 2+ /Fe 3+ weight ratio that is exhibited by said acicular magnetite after the heating in said inert atmosphere and prior to said saturating with oxygen, whereby obtaining an acicular magnetite having highly stable coercive force with lapse of time.
Claim 2
Dependent Claim
184 words
A process for treating acicular magnetite containing Co to stabilize the magnetic properties against change with lapse of time, comprising the steps of: heating acicular magnetite having a Fe 2+ /Fe 3+ weight ratio in the range of 0.3 to 0.49 and containing 0.1 to 2.5% by atom of Co with respect to Fe as starting material at a temperature in the range of 300-1000° C. in an inert gas atmosphere in which the partial pressure of oxygen is controlled at a value in the range of 0.001-1% by weight and for a time sufficient to effect the equilibrium partial pressure of oxygen in accordance with Gibb's phase rule, and thereafter saturating the resultant acicular magnetite with oxygen by heating it at a temperature in the range of 40 to 100° C. in an air atmosphere while substantially retaining the value of the Fe 2+ /Fe 3+ weight ratio that is exhibited by said acicular magnetite after the heating in said inert atmosphere and prior to said saturating with oxygen, whereby obtaining an acicular magnetite having highly stable coercive force with lapse of time.
Claim 3
Dependent Claim
25 words
The process of claim 1, in which the acicular magnetite as starting material contains 0.5 to 2% by atom of Co with respect to Fe.
Claim 4
Dependent Claim
29 words
The process of claim 1, in which the step of saturating the acicular magnetite with oxygen is effected at a temperature in the range of 70 to 100° C.
Claim 5
Dependent Claim
32 words
The process of claim 1, in which the step of heating the acicular magnetite in the inert gas atmosphere is effected at a temperature in the range of 350 to 800° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-22 | 1982-07-24 | 1983-01-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-22 | 1986-07-24 | 1987-01-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-22 | 1990-07-24 | 1991-01-23 | $7700.00 | Window Closed / Lapsed |