Metal article and powder alloy and method for producing metal article from aluminum base powder alloy containing silicon and manganese
Assignee: Alcoa Corp
•
Filing: 1976-12-17
•
Granted: 1979-01-23
•
Expires: 1996-12-17
Abstract
Abstract A method is provided for producing a metal article from an Al-Si-Mn powder alloy. The alloy is produced by alloying elements in a molten state and a powder of the alloy is produced by atomization. Powder is heated, worked into a finished article of at least 99% density. A metal article produced has a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F and relatively high strength at temperatures greater than 400° F (478° K). Article produced is ideally suited for uses, such as piston, requiring limited thermal expansion while maintaining high temperature strength. An aluminum base powder alloy provided consists essentially of 10 to 25%, Si, 2 to 5% Mn, the balance essentially aluminum and incidental elements and impurities, and is substantially free of Mg, Zn and Ni. Additive elements may be Fe or Cu and Cr, V Zr and Ti. The powder alloy can be atomized in a temperature range of 1400 to 1600° F (1033 to 1144° K).
Inventors
- 👤 Walter S. Cebulak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:17
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/02; C22C1/026; Y; Y10; Y10S; Y10S75/00; Y10S75/95
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
143 words
A method for producing an aluminum base article comprises: alloying elements in a molten state to produce an alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn, and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities; producing a powder from said alloy in a molten state by atomization at temperatures from as low as 1400 to 1600° F.; heating said powder to a substantially uniform temperature sufficient to facilitate metallurgical bonding during conditions of plastic deformation; and working said powder in dies into a finished worked shape of said article requiring no further plastic deformation and having a density of at least 99%, said article characterized by a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 2
Independent Claim
143 words
A method for producing an aluminum base article comprises: alloying elements in a molten state to produce an alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn, and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities; producing a powder from said alloy in a molten state by atomization at temperatures from as low as 1400 to 1600° F.; heating said powder to a substantially uniform temperature sufficient to facilitate metallurgical bonding during conditions of plastic deformation; and working said powder in dies into a finished worked shape of said article requiring no further plastic deformation and having a density of at least 99%, said article characterized by a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 3
Dependent Claim
24 words
The method set forth in claim 1 wherein said alloy further contains as an element, up to 1.5% Fe or 2 to 5% Cu.
Claim 4
Dependent Claim
23 words
The method set forth in claim 2 wherein when said alloy contains 0.25 to 1.5% Fe, said alloy contains 2 to 4% Mn.
Claim 5
Dependent Claim
23 words
The method set forth in claim 2 wherein when said alloy contains 2 to 5% Cu, said alloy contains 2 to 5% Mn.
Claim 6
Dependent Claim
31 words
The method set forth in claim 1 wherein said alloy further contains up to 0.4% each of one or more elements from the group consisting of Cr, V, Zr and Ti.
Claim 7
Dependent Claim
15 words
The method set forth in claim 1 wherein working said powder is performed by forging.
Claim 8
Dependent Claim
17 words
The method set forth in claim 6 wherein forging said powder is done in one compressive step.
Claim 9
Dependent Claim
20 words
The method set forth in claim 1 wherein said alloy contains 13 to 20% Si and 3 to 4.5% Mn.
Claim 10
Independent Claim
173 words
A method for producing an article, having a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at elevated temperatures, from an aluminum base powder alloy, comprises: melting and alloying elements to produce a homogeneous alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn and no more than 1% Mg, 1% Zn and 1% Ni, the total amount of Mg, Zn and Ni being no more than 2%, the balance essentially aluminum and incidental elements and impurities; atomizing said alloy in a molten state to produce an aluminum base powder at a temperature of 1420 to 1550° F.; placing in a deformable container an amount of loose powder needed to forge said article to a predetermined density; heating said powder to a substantially uniform temperature of at least 500° F. to facilitate metallurgical bonding during conditions of plastic deformation; and forging said container and powder therein into a forged shape of said article having a predetermined density of at least 99%.
Claim 11
Independent Claim
173 words
A method for producing an article, having a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at elevated temperatures, from an aluminum base powder alloy, comprises: melting and alloying elements to produce a homogeneous alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn and no more than 1% Mg, 1% Zn and 1% Ni, the total amount of Mg, Zn and Ni being no more than 2%, the balance essentially aluminum and incidental elements and impurities; atomizing said alloy in a molten state to produce an aluminum base powder at a temperature of 1420 to 1550° F.; placing in a deformable container an amount of loose powder needed to forge said article to a predetermined density; heating said powder to a substantially uniform temperature of at least 500° F. to facilitate metallurgical bonding during conditions of plastic deformation; and forging said container and powder therein into a forged shape of said article having a predetermined density of at least 99%.
Claim 12
Dependent Claim
146 words
In a method of producing an article from an aluminum base powder alloy having the steps of melting and alloying elements to produce a homogeneous alloy, atomizing said alloy to produce a powder thereof, heating said powder to a substantially uniform temperature to facilitate metallurgical bonding during plastic deformation, working said powder in dies into a finished worked shape having a density of at least 99%, wherein the improvement comprises: providing said alloy consisting essentially of 10 to 25% Si, 2 to 5% Mn and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities; atomizing said alloy at a temperature of 1400 to 1600° F. to produce a powder which is worked into an article having a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 13
Dependent Claim
146 words
In a method of producing an article from an aluminum base powder alloy having the steps of melting and alloying elements to produce a homogeneous alloy, atomizing said alloy to produce a powder thereof, heating said powder to a substantially uniform temperature to facilitate metallurgical bonding during plastic deformation, working said powder in dies into a finished worked shape having a density of at least 99%, wherein the improvement comprises: providing said alloy consisting essentially of 10 to 25% Si, 2 to 5% Mn and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities; atomizing said alloy at a temperature of 1400 to 1600° F. to produce a powder which is worked into an article having a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 14
Dependent Claim
101 words
A metal article produced from a powder of an aluminum base alloy atomized at a temperature as low as 1400° F. and consisting essentially of 10 to 25% Si, 2 to 5% Mn and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities, said powder being substantially uniformly heated to facilitate metallurgical bonding and being subjected to plastic deformation to produce said article having a predetermined density of at least 99%, a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 15
Dependent Claim
101 words
A metal article produced from a powder of an aluminum base alloy atomized at a temperature as low as 1400° F. and consisting essentially of 10 to 25% Si, 2 to 5% Mn and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities, said powder being substantially uniformly heated to facilitate metallurgical bonding and being subjected to plastic deformation to produce said article having a predetermined density of at least 99%, a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 16
Dependent Claim
33 words
The metal article as set forth in claim 11 wherein said powder aluminum base alloy further contains one element from the group consisting of up to 1.5% Fe and 2 to 5% Cu.
Claim 17
Dependent Claim
22 words
The metal article as set forth in claim 12 wherein said alloy contains 0.25 to 1.5% Fe and 2 to 4% Mn.
Claim 18
Dependent Claim
22 words
The metal article as set forth in claim 12 wherein said alloy contains 2 to 5% Cu and 2 to 5% Mn.
Claim 19
Dependent Claim
36 words
The metal article as set forth in claim 12 wherein said powder aluminum base alloy further contains up to 0.4% each of one or more elements from the group consisting of Cr, V, Zr and Ti.
Claim 20
Dependent Claim
19 words
The metal article as set forth in claim 11 wherein plastic deformation of said powder is done by forging.
Claim 21
Dependent Claim
18 words
The metal article as set forth in claim 16 wherein said forging is performed in one compressive step.
Claim 22
Dependent Claim
146 words
A metal article produced from a powder of an aluminum base alloy by heating said powder to a substantially uniform temperature and forging said powder to a predetermined density, said alloy consisting essentially of 10 to 25% Si, 2 to 5% Mn, up to 1.5% Fe or 2 to 5% Cu, and up to 0.4% each of one or more elements from the group consisting of Cr, V, Zr and Ti, and no more than 1% Mg, 1% Zn and 1% Ni, the total amount of Mg, Zn and Ni being no more than 2%, the balance essentially aluminum and incidental elements and impurities, said powder atomized at a metal temperature of 1420 to 1550° F., said article being characterized by a coefficient of thermal expansion of less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures of greater than 400° F.
Claim 23
Dependent Claim
146 words
A metal article produced from a powder of an aluminum base alloy by heating said powder to a substantially uniform temperature and forging said powder to a predetermined density, said alloy consisting essentially of 10 to 25% Si, 2 to 5% Mn, up to 1.5% Fe or 2 to 5% Cu, and up to 0.4% each of one or more elements from the group consisting of Cr, V, Zr and Ti, and no more than 1% Mg, 1% Zn and 1% Ni, the total amount of Mg, Zn and Ni being no more than 2%, the balance essentially aluminum and incidental elements and impurities, said powder atomized at a metal temperature of 1420 to 1550° F., said article being characterized by a coefficient of thermal expansion of less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures of greater than 400° F.
Claim 24
Dependent Claim
104 words
An aluminum base powder alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities, said alloy being made by allowing said elements in a molten state and then atomizing said alloy at a temperature of 1400 to 1600° F. to produce a powder of said alloy, said powder when hot worked producing an aluminum alloy article characterized by a thermal coefficient of expansion of less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures of greater than 400° F.
Claim 25
Dependent Claim
104 words
An aluminum base powder alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn and substantially free of Mg, Zn and Ni, the balance essentially aluminum and incidental elements and impurities, said alloy being made by allowing said elements in a molten state and then atomizing said alloy at a temperature of 1400 to 1600° F. to produce a powder of said alloy, said powder when hot worked producing an aluminum alloy article characterized by a thermal coefficient of expansion of less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures of greater than 400° F.
Claim 26
Dependent Claim
26 words
The aluminum powder alloy as set forth in claim 19 further containing an additive alloying constituent of up to 1.5% Fe or 2 to 5% Cu.
Claim 27
Dependent Claim
30 words
The aluminum powder alloy as set forth in claim 19 further containing up to 0.4% of one or more elements from the group consisting of Cr, V, Zr and Ti.
Claim 28
Dependent Claim
140 words
Aluminum base powder alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn, an element selected from the group consisting of up to 1.5% Fe and 2 to 5% Cu and up to 0.4% each of one or more elements from the group consisting of Cr, V, Zr and Ti, and no more than 1% Mg, 1% Zn and 1% Ni, the total amount of Mg, Zn and Ni being no more than 2%, said alloy being made by alloying said elements in a molten state, and then producing a powder thereof, by atomization at a temperature of 1420 to 1550° F., which when hot worked produces an aluminum alloy article characterized by a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
Claim 29
Dependent Claim
140 words
Aluminum base powder alloy consisting essentially of the elements 10 to 25% Si, 2 to 5% Mn, an element selected from the group consisting of up to 1.5% Fe and 2 to 5% Cu and up to 0.4% each of one or more elements from the group consisting of Cr, V, Zr and Ti, and no more than 1% Mg, 1% Zn and 1% Ni, the total amount of Mg, Zn and Ni being no more than 2%, said alloy being made by alloying said elements in a molten state, and then producing a powder thereof, by atomization at a temperature of 1420 to 1550° F., which when hot worked produces an aluminum alloy article characterized by a coefficient of thermal expansion less than 11.0 × 10 -6 inch/inch/° F. and relatively high strength at temperatures greater than 400° F.
References Cited (Backward Citations)
US3544392A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-22 | 1982-07-24 | 1983-01-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-22 | 1986-07-24 | 1987-01-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-22 | 1990-07-24 | 1991-01-23 | $7700.00 | Window Closed / Lapsed |