Ceramic capacitor having a bismuth-containing silver-doped dielectric of (Pb,La) (Zr,Ti)O3
Assignee: MRA Laboratories Inc
•
Filing: 1977-05-31
•
Granted: 1979-01-16
•
Expires: 1997-05-31
Abstract
Abstract The dielectric material of a ceramic capacitor contains a high temperature silver doped ceramic with either no glass or with a small proportion of a low temperature glass. The ceramic component consists essentially of a lead zirconate in which from 0.07 to 0.16 molar parts of the lead are replaced by lanthanum and in which from 0.10 to 0.40 molar parts of the zirconate are replaced by titanate. The capacitors are preferably fired in a closed atmosphere at temperatures from above 2000 DEG F to 2200 DEG F. Silver containing electrodes may be employed in a monolithic capacitor of this invention, the co-fired electrode advantageously causing a silver doping of the ceramic that in turn improves the stability of capacitance with temperature and applied voltage. Bismuth trioxide is added to the green ceramic body that permits a lower firing temperature or is included in the glass formulation, in both cases the bismuth serving to accelerate a silver reaction with the ceramic at firing.
Inventors
- 👤 Galeb H. Maher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:27
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1236; H01G4/1245; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
112 words
A ceramic capacitor comprising a dielectric body and two spaced electrodes in contact with said dielectric body, said body consisting essentially of a dense high temperature ceramic, from 0 to 8 weight percent of a low temperature glass and at least 0.4 weight percent Bi 2 O 3 , said ceramic being doped with from 0.1 to 1.0 weight percent silver and consisting substantially of a lead zirconate wherein from 0.07 to 0.16 molar parts of said lead are replaced by lanthanum and wherein from 0.10 to 0.40 molar parts of said zirconate are replaced by titanate, from 0 to 100% of said Bi 2 O 3 being contained in said glass.
Claim 2
Dependent Claim
112 words
A ceramic capacitor comprising a dielectric body and two spaced electrodes in contact with said dielectric body, said body consisting essentially of a dense high temperature ceramic, from 0 to 8 weight percent of a low temperature glass and at least 0.4 weight percent Bi 2 O 3 , said ceramic being doped with from 0.1 to 1.0 weight percent silver and consisting substantially of a lead zirconate wherein from 0.07 to 0.16 molar parts of said lead are replaced by lanthanum and wherein from 0.10 to 0.40 molar parts of said zirconate are replaced by titanate, from 0 to 100% of said Bi 2 O 3 being contained in said glass.
Claim 3
Dependent Claim
19 words
The capacitor of claim 1 wherein said glass amounts to less than 4.5 weight percent of said dielectric body.
Claim 4
Dependent Claim
18 words
The capacitor of claim 1 wherein at least one of said electrodes is buried within said dielectric body.
Claim 5
Dependent Claim
13 words
The capacitor of claim 3 wherein said buried electrode is a silver alloy.
Claim 6
Dependent Claim
30 words
The capacitor of claim 1 wherein said glass amounts to about 7 weight percent of said body and said body contains more than 1.6 weight percent of said bismuth trioxide.
Claim 7
Dependent Claim
20 words
The capacitor of claim 5 wherein said glass has a composition having about 87 weight percent of said bismuth trioxide.
Claim 8
Independent Claim
144 words
A method for producing a ceramic capacitor comprising preparing a mixture of from 99.6 to 92 parts by weight of a pulverized prefired lead zirconate ceramic, from 0 to 8 parts by weight of a finely ground low temperature glass and an organic binder medium wherein from 0.07 to 0.16 molar parts of said lead is replaced with lanthanum and wherein from 0.10 to 0.40 molar parts of said zirconate is replaced by titanate; including in said mixture at least 0.4% bismuth trioxide by weight of said ceramic and glass, forming a body of said ceramic mixture; adding a silver component within said body; forming two spaced electrodes in contact with said ceramic body; and firing said body to maturity at a temperature no greater than 2000° F. whereby said bismuth aids a reaction of said silver with said lead lanthanum zirconate titanate ceramic.
Claim 9
Independent Claim
144 words
A method for producing a ceramic capacitor comprising preparing a mixture of from 99.6 to 92 parts by weight of a pulverized prefired lead zirconate ceramic, from 0 to 8 parts by weight of a finely ground low temperature glass and an organic binder medium wherein from 0.07 to 0.16 molar parts of said lead is replaced with lanthanum and wherein from 0.10 to 0.40 molar parts of said zirconate is replaced by titanate; including in said mixture at least 0.4% bismuth trioxide by weight of said ceramic and glass, forming a body of said ceramic mixture; adding a silver component within said body; forming two spaced electrodes in contact with said ceramic body; and firing said body to maturity at a temperature no greater than 2000° F. whereby said bismuth aids a reaction of said silver with said lead lanthanum zirconate titanate ceramic.
Claim 10
Dependent Claim
30 words
The method of claim 7 wherein said firing is accomplished at a temperature greater than 2000° F. and additionally comprising enclosing said body in a closed crucible during said firing.
Claim 11
Dependent Claim
23 words
The method of claim 8 additionally comprising adding a quantity of a lead containing compound within said closed crucible prior to said firing.
Claim 12
Dependent Claim
25 words
The method of claim 9 wherein no more than 50% of the volume of said closed crucible is occupied by air prior to said firing.
Claim 13
Dependent Claim
18 words
The method of claim 7 wherein said glass is less than 41/2% by weight of said glass-ceramic mixture.
Claim 14
Dependent Claim
29 words
The method of claim 7 wherein said including of said bismuth is accomplished by incorporating from 0 to 100% of said bismuth trioxide in the formulation of said glass.
Claim 15
Dependent Claim
23 words
The method of claim 7 wherein said including is accomplished at least in part by adding bismuth trioxide powder to said ceramic mixture.
Claim 16
Dependent Claim
21 words
The method of claim 7 wherein said adding is accomplished by adding said silver component in powder form to said mixture.
Claim 17
Dependent Claim
12 words
The method of claim 14 wherein said silver component is elemental silver.
Claim 18
Dependent Claim
23 words
The method of claim 7 additionally comprising burying at least one of said electrodes within said body to make a monolithic ceramic capacitor.
Claim 19
Dependent Claim
22 words
The method of claim 16 wherein said adding of said silver is accomplished by forming said buried electrode of a silver alloy.
References Cited (Backward Citations)
US3499704A
Cited
US3591504A
Cited
US3518198A
Cited
US3732117A
Cited
US3638084A
Cited
US4027209A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-15 | 1982-07-17 | 1983-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-15 | 1986-07-17 | 1987-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-15 | 1990-07-17 | 1991-01-16 | $7700.00 | Window Closed / Lapsed |