Process for making aqueous cationic coating from amine-epoxy adduct, polyamide, and semiblocked polyisocyanate, acid salt, and product
Assignee: Kansai Paint Co Ltd
•
Filing: 1977-07-22
•
Granted: 1979-01-16
•
Expires: 1997-07-22
Abstract
Abstract A process for preparing a cationic electrophoretic coating composition comprising the steps of: (I) mixing or reacting (1) a reaction product of an epoxy-amine adduct (A) and a partially blocked polyisocyanate (C) and (2) a reaction product of a polyamide (B) and a partially blocked polyisocyanate (C) and (II) dissolving or dispersing the resulting mixture or reaction product in an aqueous medium by neutralization with an acid.
Inventors
- 👤 Akira Tominaga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:51
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/60; C08G18/603; C08G18/64; C08G18/6415; C08G18/643; C08G59/00; C08G59/18; C08G59/40; C08G59/50; C08G59/56; C08G69/00; C08G69/48; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; Y; Y10; Y10S; Y10S524/00; Y10S524/901
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
209 words
A process for preparing a cationic electrophoretic coating composition comprising the steps of: (I) mixing or reacting (1) a reaction product of an epoxy-amine adduct (A) and a partially blocked polyisocyanate (C) in the weight ratio of from 95 to 5 of (A) to from 5 to 95 of (C) and (2) a reaction product of a polyamide (B) and a partially blocked polyisocyanate (C) in the weight ratio of from 95 to 5 of (B) to from 5 to 95 of (C), said epoxy-amine adduct (A) being a reaction product prepared by reacting an epoxy resin with a basic amino compound having at least one basic amino group, said polyamide (B) being a polyamide having at least one basic amino group and said partially blocked polyisocyanate (C) being a polyisocyanate compound having at least one blocked isocyanate group in the molecule and an average of more than zero to not more than one free isocyanate group per molecule, and the weight ratio being from 90 to 10 of said reaction product of (A) and (C) to from 10 to 90 of said reaction product of (B) and (C) and (II) dissolving or dispersing the resulting mixture or reaction product in an aqueous medium by neutralization with an acid.
Claim 2
Dependent Claim
209 words
A process for preparing a cationic electrophoretic coating composition comprising the steps of: (I) mixing or reacting (1) a reaction product of an epoxy-amine adduct (A) and a partially blocked polyisocyanate (C) in the weight ratio of from 95 to 5 of (A) to from 5 to 95 of (C) and (2) a reaction product of a polyamide (B) and a partially blocked polyisocyanate (C) in the weight ratio of from 95 to 5 of (B) to from 5 to 95 of (C), said epoxy-amine adduct (A) being a reaction product prepared by reacting an epoxy resin with a basic amino compound having at least one basic amino group, said polyamide (B) being a polyamide having at least one basic amino group and said partially blocked polyisocyanate (C) being a polyisocyanate compound having at least one blocked isocyanate group in the molecule and an average of more than zero to not more than one free isocyanate group per molecule, and the weight ratio being from 90 to 10 of said reaction product of (A) and (C) to from 10 to 90 of said reaction product of (B) and (C) and (II) dissolving or dispersing the resulting mixture or reaction product in an aqueous medium by neutralization with an acid.
Claim 3
Dependent Claim
20 words
A process as defined in claim 1 wherein the epoxy resin has a molecular weight of about 200 to 4,000.
Claim 4
Dependent Claim
20 words
A process as defined in claim 2 wherein the molecular weight is in the range of about 400 to 2,000.
Claim 5
Dependent Claim
19 words
A process as defined in claim 1 wherein the epoxy resin is one obtained from bisphenol A and epichlorohydrin.
Claim 6
Dependent Claim
26 words
A process as defined in claim 1 wherein the basic amino compound is an aliphatic or alicyclic amino compound having a primary and/or secondary amino group.
Claim 7
Dependent Claim
17 words
A process as defined in claim 5 wherein the basic amino compound is a water-soluble aliphatic monoamine.
Claim 8
Dependent Claim
27 words
A process as defined in claim 1 wherein the epoxy resin is reacted with the basic amino compound at a temperature of about 50 to 150° C.
Claim 9
Dependent Claim
48 words
A process as defined in claim 1 wherein the polyamide is a product prepared by condensation of a dicarboxylic acid and polyamine, a product by reacting a polyamine with an oligomer prepared by the ring-opening polymerization of a lactam, or a polyesterpolyamide of an alkanolamine and dicarboxylic acid.
Claim 10
Dependent Claim
44 words
A process as defined in claim 1 wherein the partially blocked polyisocyanate compound is an aromatic polyisocyanate having at least one blocked isocyanate group in the molecule and an average of more than zero to not more than one free isocyanate group per molecule.
Claim 11
Dependent Claim
28 words
A process as defined in claim 9 wherein the aromatic polyisocyanate is tolylene diisocyanate, xylylene diisocyanate, or an adduct of tolylene diisocyanate or xylylene diisocyanate and a polyol.
Claim 12
Dependent Claim
36 words
A process as defined in claim 1 wherein the reaction product of (A) and (C) is obtained by reacting from 80 to 30 of (A) with from 20 to 70 of (C), in the weight ratio.
Claim 13
Dependent Claim
36 words
A process as defined in claim 1 wherein the reaction product of (B) and (C) is obtained by reacting from 80 to 30 of (B) with from 20 to 70 of (C), in the weight ratio.
Claim 14
Dependent Claim
55 words
A process as defined in claim 1 wherein the reaction product of (A) and (C) is mixed or reacted with the reaction product of (B) and (C) in such a proportion that the weight ratio is from 90 to 10 of the former reaction product to from 10 to 90 of the latter reaction product.
Claim 15
Dependent Claim
22 words
A process as defined in claim 1 wherein the acid to be used for neutralization is a water-soluble organic or inorganic acid.
Claim 16
Dependent Claim
20 words
A process as defined in claim 1 wherein the resinous binder has an amine value of about 25 to 400.
Claim 17
Dependent Claim
20 words
A process as defined in claim 15 wherein the amine value is in the range of about 50 to 200.
Claim 18
Dependent Claim
21 words
A process as defined in claim 1 which contains a binder in a concentration of about 3 to 30% by weight.
Claim 19
Dependent Claim
16 words
A process as defined in claim 1 which has a pH of about 3 to 9.
Claim 20
Dependent Claim
16 words
A process as defined in claim 1 which further contains a neutral or cationic water-soluble resin.
Claim 21
Dependent Claim
13 words
A cationic electrophoretic coating composition produced by the process claimed in claim 1.
References Cited (Backward Citations)
US3336253A
Cited
US3799854A
Cited
US3922253A
Cited
US3947338A
Cited
US4036795A
Cited
US4017438A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-15 | 1982-07-17 | 1983-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-15 | 1986-07-17 | 1987-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-15 | 1990-07-17 | 1991-01-16 | $7700.00 | Window Closed / Lapsed |