Process for preparing mixed metal oxide catalysts

Claim 2

In a process for synthesizing a mixed metal oxide catalyst material comprising at least one platinum group metal and having a predetermined composition and a predetermined crystal structure by a method comprising grinding and heating a mixture of powders to obtain a product of predetermined composition, the improvement which comprises subjecting a mixture of powders selected from at least one of the group consisting of elemental metals, alloys and compounds which on processing will convert to the desired mixed metal oxide, said mixture of powders being formulated to contain, or on heat treatment in an oxidizing atmosphere to contain, a stoichiometric ratio of the constituents of the predetermined mixed metal oxide composition to dry, high energy impact milling for a period of time sufficient to produce a mechanically-alloyed powder which will convert on heat treatment to an essentially single phase structure of the predetermined composition and crystal structure, and heating said mechanically-alloyed powder in an oxidizing atmosphere to effect conversion to said mixed metal oxide catalyst material.

Claim 3

The process of claim 1, wherein the mixed metal oxide catalyst material is of a structural type selected from the group consisting of perovskite, spinel, pyrochlore, ilmenite, rutile, and rock salt.

Claim 4

The process of claim 1, wherein the mixed metal oxide is a perovskite of the ABO 3 type.

Claim 5

In a process of synthesizing a mixed metal oxide catalyst material having a predetermined crystal structure by a method comprising grinding and heating a mixture of powders to obtain a product of predetermined composition, the improvement which comprises subjecting a mixture of powders selected from at least one of the group consisting of elemental metals, alloys and compounds which on processing will convert to the desired mixed metal oxide, said mixture of powders being formulated to contain, or on heat treatment in an oxidizing atmosphere to contain, a stoichiometric ratio of the constituents of the predetermined mixed metal oxide composition, to high energy impact milling for a period of time sufficient to produce a mechanically-alloyed powder which will convert on heat treatment to an essentially single phase structure of the predetermined composition and crystal structure, and heating the mechanically-alloyed product obtained by dry, high energy impact milling in an oxidizing atmosphere to a temperature below about 800° C. for a period of time of up to about 5 hours and then raising the temperature to above about 900° C. for a period of about 1 to about 100 minutes to effect conversion to said mixed metal oxide catalyst material.

Claim 6

In a process of synthesizing a mixed metal oxide catalyst material having a predetermined crystal structure by a method comprising grinding and heating a mixture of powders to obtain a product of predetermined composition, the improvement which comprises subjecting a mixture of powders selected from at least one of the group consisting of elemental metals, alloys and compounds which on processing will convert to the desired mixed metal oxide, said mixture of powders being formulated to contain, or on heat treatment in an oxidizing atmosphere to contain, a stoichiometric ratio of the constituents of the predetermined mixed metal oxide composition, to high energy impact milling for a period of time sufficient to produce a mechanically-alloyed powder which will convert on heat treatment to an essentially single phase structure of the predetermined composition and crystal structure, and heating the mechanically-alloyed product obtained by dry, high energy impact milling in an oxidizing atmosphere to a temperature below about 800° C. for a period of time of up to about 5 hours and then raising the temperature to above about 900° C. for a period of about 1 to about 100 minutes to effect conversion to said mixed metal oxide catalyst material.

Claim 7

In a process for synthesizing a mixed metal oxide catalyst material, said mixed metal oxide having a predetermined composition of the empirical formula ABO 3 and a perovskite-type structure, as shown by X-ray diffraction, by a method comprising grinding and heating a mixture of powders to obtain a product of the predetermined composition, the improvement which comprises subjecting a mixture of powders selected from at least one of the group consisting of elemental metals, alloys and compounds which on processing will convert to the desired mixed metal oxide, said mixture of powders being formulated to contain, or on heat treatment in an oxidizing atmosphere to contain, a stoichiometric ratio of the predetermined ABO 3 composition, to dry, high energy impact milling to produce a mechanically-alloyed powder product which will convert on heat treatment to an essentially single phase perovskite structure of the predetermined composition, and heating said mechanically-alloyed product in an oxidizing atmosphere to effect conversion to said perovskite structure of predetermined composition.

Claim 8

In a process for synthesizing a mixed metal oxide catalyst material, said mixed metal oxide having a predetermined composition of the empirical formula ABO 3 and a perovskite-type structure, as shown by X-ray diffraction, by a method comprising grinding and heating a mixture of powders to obtain a product of the predetermined composition, the improvement which comprises subjecting a mixture of powders selected from at least one of the group consisting of elemental metals, alloys and compounds which on processing will convert to the desired mixed metal oxide, said mixture of powders being formulated to contain, or on heat treatment in an oxidizing atmosphere to contain, a stoichiometric ratio of the predetermined ABO 3 composition, to dry, high energy impact milling to produce a mechanically-alloyed powder product which will convert on heat treatment to an essentially single phase perovskite structure of the predetermined composition, and heating said mechanically-alloyed product in an oxidizing atmosphere to effect conversion to said perovskite structure of predetermined composition.

Claim 9

The process of claim 5, wherein in the empirical formula ABO 3 , A represents at least one element selected from the group consisting of alkali metals, alkaline earth metals, rare earth metals, lead and bismuth, and B represents at least one element selected from groups IB, IVB, VB, VIB, VIIB, and VIII of the Periodic Table.

Claim 10

The process of claim 5, wherein said component B comprises at least one element selected from the group consisting of nickel, cobalt, platinum, palladium, ruthenium, rhodium, iridium and osmium.

Claim 11

The process of claim 6, wherein said component B comprises at least one platinum group metal.

Claim 12

The process of claim 8, wherein said platinum group metal is ruthenium.

Claim 13

The process of claim 5, where the components of the powder formulation subjected to high energy impact milling are selected from at least one of the group consisting of elemental metals, oxides, carbonates, halides, hydroxides, nitrates, oxalates of the components A and B of the empirical formula ABO 3 .

Claim 14

The process of claim 5, wherein the heat treatment comprises heating the mechanically alloyed powder obtained by high energy impact milling to a final temperature greater than 800° C.

Claim 15

The process of claim 11, wherein the final temperature is in the range between about 900° C. and 1200° C.

Claim 16

The process of claim 11, wherein the heat treatment comprises subjecting said mechanically alloyed powder in oxidizing atmosphere to a temperature below about 800° C. for a period of up to about 5 hours and then elevating the temperature to above 900° C. for a period of about 1 to about 100 minutes.

Claim 17

The process of claim 13 wherein the mechanically alloyed powder is subjected to a temperature of about 300° C. to 700° C. for a period of 1/4 to 4 hours and then to a temperature of about 900° C. to 1200° C. for a period of 1 to 100 minutes.

Claim 18

The process of claim 11, wherein the final heat treatment temperature of the powder is carried out with the powder maintained at a bed depth equivalent to no greater than 1 inch.

Claim 19

The process of claim 5, wherein the high energy impact milling is carried out at a ball-to-powder ratio of about 5 to 1 to about 20 to 1 for a period of up to about 40 hours.

Claim 20

The process of claim 16, wherein the said high energy impact milling is carried out for a period of about 10 to 30 hours.

Claim 21

The process of claim 5, wherein the powder produced by said high energy impact milling has an average particle size of about 1 to 20 microns and after heat treatment the product powder obtained consists essentially of agglomerates of crystals, the average particle size of said agglomerates being typically about 10 to 100 microns.

Claim 22

The process of claim 5, wherein the final treatment temperature is less than about 1200° C.

Claim 23

The process of claim 5, wherein the heat treatment is carried out at a temperature of less than about 1200° C., and a single phase product is obtained in a period of time of up about 7 hours.

Claim 24

The process of claim 5, wherein the A component consists essentially of the elements strontium and lanthanum and the B component is at least one element selected from the group consisting of cobalt, manganese, nickel, chromium, titanium, ruthenium, palladium, platinum and rhodium.

Claim 25

The process of claim 4, wherein the mixed metal oxide catalyst material is of a structural type selected from the group consisting of perovskite, spinel, pyrochlore, ilmenite, rutile, and rock salt.

Claim 26

The process of claim 4, wherein the mixed metal oxide material is further treated by a deposit of a platinum group metal.