Method of producing dopant material for iron or nickel-base alloys

Assignee: Individual
•
Filing: 1977-11-22
•
Granted: 1979-01-09
•
Expires: 1997-11-22
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A dopant material, comprising metallic elements constituting alloy base metals and endogeneous high-melting-point compounds selected from the group consisting of titanium, zirconium, tantalum, hafnium and thorium nitrides, carbides, carbonitrides, borides and oxides. The dopant material for iron- or nickel-base alloys is produced by melting a dopant base metal, whereupon the elements required for the formation of the high-melting-point compounds selected from the group consisting of titanium, zirconium, tantalum, hafnium, thorium nitrides, carbides, carbonitrides, borides and oxides, are taken in a stoichiometric ratio and introduced into the melt. These elements are introduced into the melt at a temperature exceeding that required for the formation therein of such compounds. After that the melt with the elements introduced therein is cooled at a rate of 10 2 -10 7 degrees per second until high-melting-point endogeneous dispersed compounds are formed in the solidified base metal. The present invention allows the production of the dopant materials which when used for modifying makes it possible to ensure an enhancement of a total range of properties, such as high-temperature strength, thermostability, crack resistance in casings and weldings, impact toughness, corrosion and erosion resistances in various aggressive media.

Inventors

  • 👤 Jury Z. Babaskin
  • 👤 Viktor A. Efimov
  • 👤 Leonid A. Sokirko
  • 👤 Leonora A. Rostovskaya
  • 👤 Sergei Y. Shipitsyn
  • 👤 Georgy D. Semenyaka
  • 👤 Georgy G. Lutsenko

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-25 19:29
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/02; C22C1/023

Claims Analysis

Total Claims: 5
Claim 1
Independent Claim 188 words
A method of producing a dopant material comprising the steps of melting a dopant base metal selected from the group consisting of iron and nickel; adding rare earth metals, manganese, silicon, molybdenum, and chromium to the molten metal; heating the molten metal to a temperature above that required for the dissolution and formation of high melting point compounds selected from the group consisting of carbides, nitrides, carbonitrides, borides, and oxides of a metal selected from the group consisting of titanium, zirconium, tantalum, hafnium, and thorium; adding non-metallic elements selected from the group consisting of carbon, nitrogen, oxygen, boron, and elements selected from the group consisting of titanium, zirconium, tantalum, hafnium, and thorium to the molten mixture in stoichiometric ratio and in weight amounts which provide for the formation of from 3 to 25 volume percent of said high melting point compounds in said dopant material; and cooling said molten mixture at a rate of from 10 2 to 10 7 degrees per second resulting in the formation of said endogenous high melting point compounds having a particle size of not more than 5 microns in said dopant material.
Claim 2
Independent Claim 188 words
A method of producing a dopant material comprising the steps of melting a dopant base metal selected from the group consisting of iron and nickel; adding rare earth metals, manganese, silicon, molybdenum, and chromium to the molten metal; heating the molten metal to a temperature above that required for the dissolution and formation of high melting point compounds selected from the group consisting of carbides, nitrides, carbonitrides, borides, and oxides of a metal selected from the group consisting of titanium, zirconium, tantalum, hafnium, and thorium; adding non-metallic elements selected from the group consisting of carbon, nitrogen, oxygen, boron, and elements selected from the group consisting of titanium, zirconium, tantalum, hafnium, and thorium to the molten mixture in stoichiometric ratio and in weight amounts which provide for the formation of from 3 to 25 volume percent of said high melting point compounds in said dopant material; and cooling said molten mixture at a rate of from 10 2 to 10 7 degrees per second resulting in the formation of said endogenous high melting point compounds having a particle size of not more than 5 microns in said dopant material.
Claim 3
Dependent Claim 30 words
A method as claimed in claim 2, wherein the manganese, silicon and molybdenum are added to the molten base metal in an amount of not more than 50 weight percent.
Claim 4
Dependent Claim 28 words
A method as claimed in claim 2, wherein the rare-earth metals are added to the molten base metal in an amount of from 0.001 to 10 weight percent.
Claim 5
Dependent Claim 27 words
A method as claimed in claim 2, wherein the chromium is added to the molten base metal in an amount of not more than 50 weight percent.

References Cited (Backward Citations)

US3028234A Cited
US3180727A Cited
US3749569A Cited
US3944416A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1982-01-08 1982-07-10 1983-01-09 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1986-01-08 1986-07-10 1987-01-09 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1990-01-08 1990-07-10 1991-01-09 $7700.00 Window Closed / Lapsed