Process for producing acicular magnetic metallic particle powder
Assignee: Toda Kogyo Corp
•
Filing: 1977-03-31
•
Granted: 1979-01-09
•
Expires: 1997-03-31
Abstract
Abstract The process for producing acicular magnetic metallic particle powder with improved magnetic properties which include the characteristic steps for producing the acicular particles of metal oxide with homogeneous and dense coats of crystalline silica and to thereby protect the particles from heat-damages during the reduction thereof under high temperatures.
Inventors
- 👤 Goro Matsui
- 👤 Koji Toda
- 👤 Atushi Takedoi
- 👤 Nanao Horiishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:56
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/16; B22F9/18; B22F9/20; B22F9/22; B22F1/00; B22F1/16; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; H01F1/065
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
173 words
A process for producing acicular magnetic metallic particles comprising the steps of: preparing an aqueous suspension of at least one acicular metal oxide particles as starting material selected from the group consisting of acicular ferric oxide particles, acicular iron (III) oxide hydroxide particles and each of these ones containing Co and/or Ni while adjusting the pH of the suspension at a value higher than 8; adding an amorphous water-soluble silicate into the suspension as fully agitated under non-oxidizing atmosphere so as to prevent the hydrolytic and oxidative decomposition of the amorphous silicate in the suspension into crystalline silica through this step while the pH of the suspension is in the range of 8-12, thereby providing homogeneous and dense coats of amorphous silicate on the acicular metal oxide particles; converting the resultant amorphous silicate coats on the particles into the crystalline silica coats by water-washing or neutralization with acid; and thereafter heating the particles in a stream of reducing gas at a temperature between 400°-800° C. and to thereby obtain acicular magnetic metallic particles.
Claim 2
Dependent Claim
173 words
A process for producing acicular magnetic metallic particles comprising the steps of: preparing an aqueous suspension of at least one acicular metal oxide particles as starting material selected from the group consisting of acicular ferric oxide particles, acicular iron (III) oxide hydroxide particles and each of these ones containing Co and/or Ni while adjusting the pH of the suspension at a value higher than 8; adding an amorphous water-soluble silicate into the suspension as fully agitated under non-oxidizing atmosphere so as to prevent the hydrolytic and oxidative decomposition of the amorphous silicate in the suspension into crystalline silica through this step while the pH of the suspension is in the range of 8-12, thereby providing homogeneous and dense coats of amorphous silicate on the acicular metal oxide particles; converting the resultant amorphous silicate coats on the particles into the crystalline silica coats by water-washing or neutralization with acid; and thereafter heating the particles in a stream of reducing gas at a temperature between 400°-800° C. and to thereby obtain acicular magnetic metallic particles.
Claim 3
Dependent Claim
102 words
The process of claim 1 in which the acicular metal oxide particles as starting material are obtained by adding into a ferrous salt solution an alkali in an amount more than the stoichiometrically equivalent of the ferrous salt at a temperature between 40°-55° C. under non-oxidizing atmosphere to thereby obtain a solution having a pH of higher than 11 and containing a ferrous hydroxide precipitate therein, oxidizing said ferrous hydroxide precipitate by introducing an oxidizing gas into the resultant solution as maintained at a temperature lower than 50° C., and thereafter water-washing, collecting and drying the resultant particles of acicular metal oxide.
Claim 4
Dependent Claim
25 words
The process of claim 2 in which the acicular metal oxide includes 0.01-1 atomic % of Cr based on the amount of Fe component therein.
Claim 5
Dependent Claim
27 words
The process of claim 3 in which the acicular metal oxide includes 0.1-10 atomic % of Co and/or Ni based on the amount of Fe component therein.
Claim 6
Dependent Claim
39 words
The process of claim 1 in which the amount of amorphous water-soluble silicate added into the suspension is 1 to 15 mol % calculated as the amount of SiO 2 based on the amount of the total metal therein.
Claim 7
Dependent Claim
21 words
The process of claim 1 in which the heating temperature in the reducing gas is in the range of 450°-700° C.
Claim 8
Dependent Claim
43 words
The process of claim 1 in which the resultant amorphous silicate on the particles is neutralized by an acid at a temperature between 20°-80° C., said particles being ferric oxide containing Co and/or Ni or iron (III) oxide hydroxide containing Co and/or Ni.
References Cited (Backward Citations)
US3370971A
Cited
US3702270A
Cited
US3843349A
Cited
US3912646A
Cited
JPS4883100A
Cited
US3947502A
Cited
US3956005A
Cited
US4043846A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-08 | 1982-07-10 | 1983-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-08 | 1986-07-10 | 1987-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-08 | 1990-07-10 | 1991-01-09 | $7700.00 | Window Closed / Lapsed |