US4043846A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing ferromagnetic metal powder by gaseous reduction of silicon compound-coated raw material
Assignee: Hitachi Ltd
•
Filing: 1976-03-17
•
Granted: 1977-08-23
•
Expires: 1996-03-17
Abstract
Abstract A method of producing ferromagnetic iron powder comprises the steps of dipping iron compound powder in a solution in which silicone oil is dissolved, removing solvent from the iron compound powder, reducing the iron compound powder in a reducing atmosphere at an elevated temperature and forming oxide layers on whole surfaces of the individual particles of the iron compound powder. Ferromagnetic iron powder produced according to this method has both a high coercive force and a high remanence ratio.
Inventors
- 👤 Masahiro Amemiya
- 👤 Seiichi Asada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:22
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/16; B22F9/18; B22F9/20; B22F9/22; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; H01F1/065
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
126 words
A method of producing ferromagnetic metal powder comprising the sequential steps of: i. coating a starting raw material powder with a solution containing more than 0.05 g/l of one silicon compound selected from the group consisting of sodium silicate, potassium silicate, silicic acid, potassium metasilicate, magnesium silicate, cobalt silicate, calcium metasilicate, metasilicic acid, sodium metasilicate and silicone oil and a solution containing ions of a silver compound in which the content of silver compound is more than 0.02 g/l, said raw material being at least one selected from the group consisting of oxalate, formate, oxide and oxyhydroxide of iron, ii. heating said powder at temperature ranging from 200° to 700° C. in a reducing atmosphere, and iii. cooling said powder reduced in the preceding step (ii).
Claim 2
Independent Claim
126 words
A method of producing ferromagnetic metal powder comprising the sequential steps of: i. coating a starting raw material powder with a solution containing more than 0.05 g/l of one silicon compound selected from the group consisting of sodium silicate, potassium silicate, silicic acid, potassium metasilicate, magnesium silicate, cobalt silicate, calcium metasilicate, metasilicic acid, sodium metasilicate and silicone oil and a solution containing ions of a silver compound in which the content of silver compound is more than 0.02 g/l, said raw material being at least one selected from the group consisting of oxalate, formate, oxide and oxyhydroxide of iron, ii. heating said powder at temperature ranging from 200° to 700° C. in a reducing atmosphere, and iii. cooling said powder reduced in the preceding step (ii).
Claim 3
Independent Claim
133 words
A method of producing ferromagnetic metal powder comprising the steps of: i. coating a starting raw material powder with a solution containing more than 0.05 g/l of one silicon compound selected from the group consisting of sodium silicate, potassium silicate, silicic acid, potassium metasilicate, magnesium silicate, cobalt silicate, calcium metasilicate, metasilicic acid, sodium metasilicate and silicone oil and a solution containing ions of a silver compound in which the content of silver compound is more than 0.02 g/l, said raw material being at least one selected from the group consisting of oxalate, formate, oxide and oxyhydroxide of iron, ii. drying said powder coated at step (i), iii. heating said powder at temperature ranging from 200° to 700° C. in a reducing atmosphere, and iv. cooling said powder reduced in the preceding step (iii).
Claim 4
Independent Claim
133 words
A method of producing ferromagnetic metal powder comprising the steps of: i. coating a starting raw material powder with a solution containing more than 0.05 g/l of one silicon compound selected from the group consisting of sodium silicate, potassium silicate, silicic acid, potassium metasilicate, magnesium silicate, cobalt silicate, calcium metasilicate, metasilicic acid, sodium metasilicate and silicone oil and a solution containing ions of a silver compound in which the content of silver compound is more than 0.02 g/l, said raw material being at least one selected from the group consisting of oxalate, formate, oxide and oxyhydroxide of iron, ii. drying said powder coated at step (i), iii. heating said powder at temperature ranging from 200° to 700° C. in a reducing atmosphere, and iv. cooling said powder reduced in the preceding step (iii).
Claim 5
Dependent Claim
25 words
The method of claim 2, in which said raw material is at least one selected from the group consisting of iron oxide and iron oxyhydroxide.
Claim 6
Dependent Claim
13 words
The method of claim 2, in which said raw material is iron oxide.
Claim 7
Dependent Claim
24 words
The method of claim 2, in which said raw material is at least one selected from the group consisting of ferric oxide and magnetite.
Claim 8
Dependent Claim
29 words
The method of claim 5, in which said raw material further comprises at least one element selected from the group consisting of Ni, Co, Al, Cr, Mg and B.
Claim 9
Dependent Claim
13 words
The method of claim 2, in which said silicon compound is silicone oil.
Claim 10
Dependent Claim
16 words
The method of claim 7, in which said silicone oil is dissolved in a organic solvent.
Claim 11
Dependent Claim
17 words
The method of claim 2, in which said content of silicon compound is more than 0.1 g/l.
Claim 12
Dependent Claim
14 words
The method of claim 2, in which said content is more than 0.2 g/l.
Claim 13
Dependent Claim
19 words
The method of claim 2, in which the temperature of heating said powder ranges from 250° to 600° C.
Claim 14
Dependent Claim
27 words
The method of claim 2, in which a step of forming surface layers on the surface of the particles composing said powder is added after step (iii).
Claim 15
Dependent Claim
27 words
The method of claim 2, in which said raw material is iron oxide, and said solution is a solution of silicone oil dissolved in an organic solvent.
Claim 16
Dependent Claim
29 words
The method of claim 13, in which the content of said silicone oil is more than 0.2 g/l and said heating temperature ranges from 250 ° to 550° C.
Claim 17
Dependent Claim
39 words
The method of claim 2, in which said silicon compound is silicone oil and said solution containing silver ions is a solution of one silver salt selected from the group consisting of silver nitrate, silver sulfate and silver chloride.
Claim 18
Dependent Claim
30 words
The method of claim 2, in which said content of said silicon compound is more than 0.2 g/l and said content of said silver compound is more than 0.05 g/l.
Claim 19
Dependent Claim
37 words
The method of claim 16, in which said raw material is iron oxide, said silicon compound is silicone oil dissolved in an organic solvent and the heating temperature at step (iii) ranges from 250° to 600° C.
Claim 20
Dependent Claim
27 words
The method of claim 2, in which both of said solution containing a silver compound and said solution containing silver ions are contained in a mixed solution.
Claim 21
Dependent Claim
34 words
The method of claim 2 in which said solution containing silver ions is a solution of at least one silver compound selected from the group consisting of silver nitrate, silver sulfate and silver chloride.
Claim 22
Dependent Claim
39 words
The method of claim 19, in which said solution containing said silver ions is said solution of said one silver compound dissolved in a solvent selected from the group consisting of water, liquid ammonia, strong inorganic acid and alcohol.
Claim 23
Dependent Claim
17 words
The method of claim 2, in which said content of silver compound is more than 0.05 g/l.
Claim 24
Dependent Claim
78 words
The method of claim 2, in which said raw material is iron oxide, said solution containing said silicon compound is a solution of more than 0.2 g/l of silicone oil dissolved in an organic solvent, said silver ion containing solution is a solution of more than 0.05 g/l of one silver compound selected from the group consisting of silver nitrate, silver sulfate and silver chloride and the heating temperature at step (iii) ranges from 250° to 600° C.
Claim 25
Dependent Claim
41 words
The method of claim 2 wherein the starting raw material is coated by immersing the raw material initially into the solution containing the silicon compound, and the solution containing the raw material is added to the solution of the silver compound.
Claim 26
Dependent Claim
38 words
The method of claim 2, wherein the raw material is coated by initially immersing the raw material into the solution of the silicon compound and then the raw material is immersed in the solution of the silver compound.
References Cited (Backward Citations)
US2651105A
Cited
US2744040A
Cited
US3598568A
Cited
US3607218A
Cited
US3627509A
Cited
US3702270A
Cited
US3725036A
Cited
US3843349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |