Method of preparing a hydrogen-permeable membrane catalyst on a base of palladium or its alloys for the hydrogenation of unsaturated organic compounds
Assignee: Individual
•
Filing: 1977-04-06
•
Granted: 1979-01-02
•
Expires: 1997-04-06
Abstract
Abstract The invention is related to a method of preparing a hydrogen-permeable membrane catalyst on a base of palladium or its alloys for the hydrogenation of unsaturated organic compounds. According to the invention the surface of a metalloceramic sheet on a base of nickel, copper or stainless steel with a thickness from 0.05 to 1 mm is covered with an organosilicon polymer which is subsequently cured at a temperature ranging from 20 to 150° C. The curing results in the formation of a film of the organosilicon polymer with a thickness from 0.01 to 1 mm, whereupon a layer of palladium or its alloy with a thickness from 0.001 to 0.1 micron is deposited on the polymer film. The method of the invention allows decreasing by hundreds of times the consumption of palladium, and other noble metals such as ruthenium, rhodium, rhenium, silver, and gold.
Inventors
- 👤 Vladimir M. Gryaznov
- 👤 Viktor S. Smirnov
- 👤 Valentin M. Vdovin
- 👤 Margarita M. Ermilova
- 👤 Lia D. Gogua
- 👤 Nina A. Pritula
- 👤 Igor A. Litvinov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:46
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/02; B01J37/024; B01J23/00; B01J23/38; B01J31/00; B01J31/02; B01J31/12; B01J31/123; B01J31/124; B01J31/26; B01J31/28; B01J2231/00; B01J2231/60; B01J2231/64; B01J2231/641; B01J2231/645; C; C10; C10M; C10M2211/00; C10M2211/06; C10M2213/00; C10M2213/02; C10M2213/04; C10M2213/06; C10M2213/062; C10M2215/00; C10M2215/22; C10M2215/221; C10M2215/225; C10M2215/226; C10M2215/24; C10M2215/30; C10N; C10N2030/00; C10N2030/12
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
122 words
A method for preparing a hydrogen permeable membrane catalyst for the hydrogenation of unsaturated organic compounds comprising: coating the surface of a metalloceramic material with an organosilicon polymer selected from the group consisting of polyorganosiloxanes and polyorganosilcarbanes, wherein said metalloceramic material is made of a substance selected from the group consisting of nickel, copper, and stainless steel, and has a thickness of about 0.05 to 1 mm; curing said polymer at a temperature of about 20° to 150° C. to form a polymer film having a thickness of about 0.1 to 1 mm; depositing a layer of a substance selected from the group consisting of palladium and palladium alloys to a thickness of about 0.001 to 0.1 micron on said polymer film.
Claim 2
Independent Claim
122 words
A method for preparing a hydrogen permeable membrane catalyst for the hydrogenation of unsaturated organic compounds comprising: coating the surface of a metalloceramic material with an organosilicon polymer selected from the group consisting of polyorganosiloxanes and polyorganosilcarbanes, wherein said metalloceramic material is made of a substance selected from the group consisting of nickel, copper, and stainless steel, and has a thickness of about 0.05 to 1 mm; curing said polymer at a temperature of about 20° to 150° C. to form a polymer film having a thickness of about 0.1 to 1 mm; depositing a layer of a substance selected from the group consisting of palladium and palladium alloys to a thickness of about 0.001 to 0.1 micron on said polymer film.
Claim 3
Dependent Claim
27 words
The method of claim 1, wherein said layer of palladium or palladium alloy is deposited by means including vacuum sublimation, plasma evaporation, chemical deposition, or anodic deposition.
Claim 4
Dependent Claim
27 words
The method of claim 1 wherein said organosilicon polymer is selected from the group consisting of polydimethylsiloxane, methylphenylsiltrimethylene polymer, polymethylsiloxanes, polyphenylsiloxanes, polymethylphenylsiloxanes, methylphenylsilmonomethylene polymer, and methylphenylsildimethylene polymer.
Claim 5
Dependent Claim
15 words
A method as claimed in claim 3, wherein polydimethylsiloxane is used as the abovesaid polyorganosiloxane.
Claim 6
Dependent Claim
16 words
A method as claimed in claim 3, wherein methylphenylsiltrimethylene polymer is used as the abovesaid polyorganosilcarbane.
Claim 7
Dependent Claim
9 words
A catalyst formed by the method of claim 1.
Claim 8
Dependent Claim
109 words
A hydrogen permeable membrane catalyst assembly consisting essentially of: a first metalloceramic layer having a thickness of about 0.05 to 1 mm, made of a substance selected from the group consisting of nickel, copper, and stainless steel; a second organosilicon polymer layer cured at a temperature of about 20°-150° C. having a thickness of about 0.1 to 1 mm, said polymer being selected from the group consisting of polydimethylsiloxane, methylphenylsiltrimethylene polymer, polymethylsiloxanes, polyphenylsiloxanes, polymethylphenylsiloxanes, methylphenylsilmonomethylene polymer, and methylphenylsildimethylene polymer; and a third layer deposited on said second polymer layer, selected from the group consisting of palladium and palladium alloys, and having a thickness of about 0.01 to 0.1 micron.
Claim 9
Dependent Claim
109 words
A hydrogen permeable membrane catalyst assembly consisting essentially of: a first metalloceramic layer having a thickness of about 0.05 to 1 mm, made of a substance selected from the group consisting of nickel, copper, and stainless steel; a second organosilicon polymer layer cured at a temperature of about 20°-150° C. having a thickness of about 0.1 to 1 mm, said polymer being selected from the group consisting of polydimethylsiloxane, methylphenylsiltrimethylene polymer, polymethylsiloxanes, polyphenylsiloxanes, polymethylphenylsiloxanes, methylphenylsilmonomethylene polymer, and methylphenylsildimethylene polymer; and a third layer deposited on said second polymer layer, selected from the group consisting of palladium and palladium alloys, and having a thickness of about 0.01 to 0.1 micron.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |