Corrosion inhibiting molybdate pigment and preparation thereof
Assignee: Noranda Inc
•
Filing: 1977-10-05
•
Granted: 1979-01-02
•
Expires: 1997-10-05
Abstract
Abstract A novel group of corrosion inhibiting pigments has been discovered, which is based on zinc molybdate compounds selected from sodium zinc molybdate, potassium zinc molybdate, ammonium zinc molybdate and mixtures thereof, combined with a suitable carrier, so that the proportion of the zinc molybdate compound is such that the Mo content in the pigment is between about 1 and 30% by weight. Such pigments can be prepared in situ by several methods, such as a double decomposition reaction of sodium, potassium or ammonium molybdate and a solution containing dissolved zinc ion, or an addition of an appropriate acid to zinc oxide dispersed in sodium, potassium or ammonium molybdate solution, or an addition of zinc oxide to a solution which comprises molybdic oxide dissolved in an aqueous solution of sodium, potassium or ammonium molybdate. All these methods are simple, economic and lead to non-toxic pigments of essentially white colour, which have anti-corrosive properties comparable to, or better than, those of zinc yellow and other commercially available corrosion inhibiting pigments.
Inventors
- 👤 Derek G. E. Kerfoot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:15
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/082; C09D5/084; C09C; C09C1/00; C09C1/0003; C09C1/0081; C09C1/0084; C09C1/0087; C01; C01P; C01P2002/00; C01P2002/70; C01P2002/72; C01P2004/00; C01P2004/80; C01P2004/82; C01P2004/84
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
57 words
A corrosion inhibiting pigment comprising a zinc molybdate compound selected from the group consisting of sodium zinc molybdate, potassium zinc molybdate, ammonium zinc molybdate and mixtures thereof, in combination with a suitable carrier, the proportion of the zinc molybdate compound being such that the Mo content in the pigment is between about 1 and 30% by weight.
Claim 2
Dependent Claim
57 words
A corrosion inhibiting pigment comprising a zinc molybdate compound selected from the group consisting of sodium zinc molybdate, potassium zinc molybdate, ammonium zinc molybdate and mixtures thereof, in combination with a suitable carrier, the proportion of the zinc molybdate compound being such that the Mo content in the pigment is between about 1 and 30% by weight.
Claim 3
Dependent Claim
15 words
A corrosion inhibiting pigment according to claim 1, in which the carrier is zinc oxide.
Claim 4
Dependent Claim
22 words
A corrosion inhibiting pigment according to claim 1, in which the carrier is titanium dioxide, calcium carbonate, talc, mica or mixtures thereof.
Claim 5
Dependent Claim
21 words
A corrosion inhibiting pigment according to claim 1, in which the Mo content is between about 5 and 15% by weight.
Claim 6
Dependent Claim
13 words
A corrosion inhibiting pigment according to claim 1, which is in calcined state.
Claim 7
Dependent Claim
45 words
A corrosion inhibiting pigment formed in situ and comprising a combination of zinc oxide particles having a surface deposit of sodium zinc molybdate, potassium zinc molybdate or ammonium zinc molybdate, with the Mo content in the pigment being between about 1 and 30% by weight.
Claim 8
Dependent Claim
45 words
A corrosion inhibiting pigment formed in situ and comprising a combination of zinc oxide particles having a surface deposit of sodium zinc molybdate, potassium zinc molybdate or ammonium zinc molybdate, with the Mo content in the pigment being between about 1 and 30% by weight.
Claim 9
Dependent Claim
34 words
A corrosion inhibiting pigment comprising discrete particles of a substrate coated with sodium zinc molybdate in a proportion such that the Mo content of the pigment is between about 1 and 30% by weight.
Claim 10
Dependent Claim
34 words
A corrosion inhibiting pigment comprising discrete particles of a substrate coated with sodium zinc molybdate in a proportion such that the Mo content of the pigment is between about 1 and 30% by weight.
Claim 11
Dependent Claim
34 words
A corrosion inhibiting pigment comprising discrete particles of a substrate coated with potassium zinc molybdate in a proportion such that the Mo content of the pigment is between about 1 and 30% by weight.
Claim 12
Dependent Claim
34 words
A corrosion inhibiting pigment comprising discrete particles of a substrate coated with potassium zinc molybdate in a proportion such that the Mo content of the pigment is between about 1 and 30% by weight.
Claim 13
Dependent Claim
34 words
A corrosion inhibiting pigment comprising discrete particles of a substrate coated with ammonium zinc molybdate in a proportion such that the Mo content of the pigment is between about 1 and 30% by weight.
Claim 14
Dependent Claim
34 words
A corrosion inhibiting pigment comprising discrete particles of a substrate coated with ammonium zinc molybdate in a proportion such that the Mo content of the pigment is between about 1 and 30% by weight.
Claim 15
Dependent Claim
91 words
A process for making a corrosion-inhibiting molybdate pigment comprising stirring a finely particulated carrier material in a solution of sodium molybdate, potassium molybdate, ammonium molybdate or mixtures thereof for sufficient time to allow the molybdate solution to wet the surface of the particles, and subsequently adding at least a stoichiometric amount of a solution containing dissolved zinc ion, in order to effect the formation of a sparingly soluble sodium, potassium or ammonium zinc molybdate salt as a deposit on the substrate particles, and recovering the solid pigment material from the solution.
Claim 16
Dependent Claim
91 words
A process for making a corrosion-inhibiting molybdate pigment comprising stirring a finely particulated carrier material in a solution of sodium molybdate, potassium molybdate, ammonium molybdate or mixtures thereof for sufficient time to allow the molybdate solution to wet the surface of the particles, and subsequently adding at least a stoichiometric amount of a solution containing dissolved zinc ion, in order to effect the formation of a sparingly soluble sodium, potassium or ammonium zinc molybdate salt as a deposit on the substrate particles, and recovering the solid pigment material from the solution.
Claim 17
Dependent Claim
34 words
Process as claimed in claim 10, wherein the finely particulated carrier material is selected from zinc oxide, titanium dioxide, talc, mica and mixtures thereof and has a particle size of up to about 30μ.
Claim 18
Dependent Claim
17 words
Process as claimed in claim 10, wherein the solution containing dissolved zinc ion is zinc nitrate solution.
Claim 19
Dependent Claim
20 words
Process as claimed in claim 10, wherein the pigment material, after recovery from the solution, is dried and eventually calcined.
Claim 20
Dependent Claim
88 words
A process for making a corrosion-inhibiting molybdate pigment comprising stirring an excess of finely particulated zinc oxide in an aqueous solution of sodium molybdate, potassium molybdate, ammonium molybdate or mixtures thereof for sufficient time to allow the molybdate to wet the surface of the zinc oxide particles, adding a predetermined volume of an acid to the solution, such as to cause the precipitation of sodium zinc molybdate, potassium zinc molybdate or ammonium zinc molybdate on the zinc oxide particles, and recovering the solid pigment material from the solution.
Claim 21
Dependent Claim
88 words
A process for making a corrosion-inhibiting molybdate pigment comprising stirring an excess of finely particulated zinc oxide in an aqueous solution of sodium molybdate, potassium molybdate, ammonium molybdate or mixtures thereof for sufficient time to allow the molybdate to wet the surface of the zinc oxide particles, adding a predetermined volume of an acid to the solution, such as to cause the precipitation of sodium zinc molybdate, potassium zinc molybdate or ammonium zinc molybdate on the zinc oxide particles, and recovering the solid pigment material from the solution.
Claim 22
Dependent Claim
17 words
Process as claimed in claim 14, wherein the acid is nitric acid, hydrochloric acid or sulphuric acid.
Claim 23
Dependent Claim
27 words
Process as claimed in claim 14, wherein the molar ratio of H + in the acid, to sodium molybdate, potassium molybdate or ammonium molybdate is about 1.5.
Claim 24
Dependent Claim
21 words
Process as claimed in claim 14, wherein the finely particulate zinc oxide has a particle size of up to about 30μ.
Claim 25
Dependent Claim
20 words
Process as claimed in claim 14, wherein the pigment material, after recovery from the solution, is dried and eventually calcined.
Claim 26
Dependent Claim
22 words
Process as claimed in claim 14, wherein the excess of finely particulate zinc oxide is replaced by a suitable particulate inert carrier.
Claim 27
Dependent Claim
66 words
A process for making a corrosion-inhibiting molybdate pigment comprising stirring an excess of finely particulate zinc oxide into a solution comprising molybdic oxide dissolved in an aqueous solution of sodium molybdate, potassium molybdate, ammonium molybdate or mixtures thereof, to effect precipitation of sodium zinc molybdate, potassium zinc molybdate or ammonium zinc molybdate on the zinc oxide particles, and recovering the solid pigment material from the solution.
Claim 28
Dependent Claim
66 words
A process for making a corrosion-inhibiting molybdate pigment comprising stirring an excess of finely particulate zinc oxide into a solution comprising molybdic oxide dissolved in an aqueous solution of sodium molybdate, potassium molybdate, ammonium molybdate or mixtures thereof, to effect precipitation of sodium zinc molybdate, potassium zinc molybdate or ammonium zinc molybdate on the zinc oxide particles, and recovering the solid pigment material from the solution.
Claim 29
Dependent Claim
21 words
Process as claimed in claim 20, wherein the finely particulate zinc oxide has a particle size of up to about 30μ.
Claim 30
Dependent Claim
20 words
Process as claimed in claim 20, wherein the pigment material, after recovery from the solution, is dried and eventually calcined.
Claim 31
Dependent Claim
22 words
Process as claimed in claim 20, wherein the excess of finely particulate zinc oxide is replaced by a suitable particulate inert carrier.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |