Abrasive particles consisting of crystalline titanium diboride in a metal carbide matrix
Assignee: EIDP Inc
•
Filing: 1977-09-27
•
Granted: 1979-01-02
•
Expires: 1997-09-27
Abstract
Abstract This invention relates to abrasive particles and process for their preparation. The particles consist essentially of a matrix of titanium carbide, zirconium carbide and tantalum carbide, at least partially in solid solution form and grains of crystalline titanium diboride dispersed throughout the carbide matrix. These abrasive particles are particularly useful as components of grinding wheels for abrading steel.
Inventors
- 👤 Herbert Valdsaar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:33
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/5611; C04B35/622; C04B35/64; C04B35/645; C09; C09K; C09K3/00; C09K3/14; C09K3/1409; C09K3/1418
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
107 words
Abrasive particles consisting essentially of a carbide matrix and boride crystals in a composite system in which, on the basis of the total carbides and boride crystals present, A. from 65 to 98 mole percent of the composite is a matrix of at least one solid solution in which (i) from 10 to 81 mole percent of the total carbides is titanium carbide, (ii) from 18 to 54 mole percent of the total carbides is zirconium carbide, and (iii) from 1 to 36 mole percent of the total carbides is tantalum carbide; and B. from 2 to 35 mole percent of the composite is crystalline titanium diboride.
Claim 2
Dependent Claim
107 words
Abrasive particles consisting essentially of a carbide matrix and boride crystals in a composite system in which, on the basis of the total carbides and boride crystals present, A. from 65 to 98 mole percent of the composite is a matrix of at least one solid solution in which (i) from 10 to 81 mole percent of the total carbides is titanium carbide, (ii) from 18 to 54 mole percent of the total carbides is zirconium carbide, and (iii) from 1 to 36 mole percent of the total carbides is tantalum carbide; and B. from 2 to 35 mole percent of the composite is crystalline titanium diboride.
Claim 3
Dependent Claim
70 words
Abrasive particles of claim 1 in which from 65 to 98 mole percent of the composite is a matrix of at least one solid solution in which (i) from 40 to 75 mole percent of the total carbides is titanium carbide, (ii) from 20 to 35 mole percent of the total carbides is zirconium carbide, and (iii) from 5 to 25 mole percent of the total carbides is tantalum carbide.
Claim 4
Dependent Claim
18 words
Abrasive particles according to claim 1 wherein said titanium diboride is present as grains of 0.5 to 30μm.
Claim 5
Dependent Claim
18 words
Abrasive particles according to claim 2 wherein said titanium diboride is present as grains of 0.5 to 30μm.
Claim 6
Dependent Claim
19 words
Abrasive particles according to claim 1 wherein said carbide matrix is present as grains of up to about 30μm.
Claim 7
Dependent Claim
19 words
Abrasive particles according to claim 2 wherein said carbide matrix is present as grains of up to about 30μm.
Claim 8
Dependent Claim
19 words
Abrasive particles according to claim 1 wherein the size of said abrasive particles is from -20 to +400 mesh.
Claim 9
Dependent Claim
19 words
Abrasive particles according to claim 2 wherein the size of said abrasive particles is from -20 to +400 mesh.
Claim 10
Dependent Claim
19 words
Abrasive particles according to claim 1 wherein the apparent density of said abrasive particles is 5.1 to 8.3 g./cc.
Claim 11
Dependent Claim
19 words
Abrasive particles according to claim 2 wherein the apparent density of said abrasive particles is 5.1 to 8.3 g./cc.
Claim 12
Dependent Claim
101 words
Process for preparing the abrasive particles of claim 1 by the steps of (1) thoroughly mixing tantalum diboride, titanium carbide and zirconium carbide each predominately 1-100μm in maximum dimension, said carbides being present in an amount in excess of the stoichiometric amount required to react with the total amount of tantalum diboride present, (2) hot-pressing the mixture of step (1) from 1 to 60 minutes at a temperature from 1900° C. to 2200° C. and at a pressure of at least 2,000 psi to form a hot-pressed compact, and (3) crushing said hot-pressed compact of step (2) to form abrasive particles.
Claim 13
Dependent Claim
43 words
Process according to claim 11 wherein said mixture of step (1) is milled from 1 to 12 hours and hot-pressed from 5 to 15 minutes at a temperature from 1900° C. to 2050° C. and at a pressure of at least 2,000 psi.
Claim 14
Dependent Claim
36 words
Process according to claim 11 wherein said mixture of step (1) is milled from 1 to 6 hours and hot-pressed for 15 minutes at 1900° C. to 2050° C. and at a pressure of 4,000 psi.
Claim 15
Dependent Claim
25 words
Process according to claim 11 wherein the mixture employed in step (1) consists essentially of predetermined amounts of titanium carbide, zirconium diboride and tantalum carbide.
Claim 16
Dependent Claim
27 words
Process according to claim 11 wherein the mixture employed in step (1) consists essentially of predetermined amounts of titanium carbide, zirconium carbide, tantalum carbide and titanium diboride.
Claim 17
Dependent Claim
23 words
In an abrasive device containing a support, bonding agent and abrasive particles, the improvement comprising using particles of the composition of claim 1.
Claim 18
Dependent Claim
15 words
A grinding wheel comprising a bond, a filler and the abrasive particles of claim 1.
Claim 19
Dependent Claim
15 words
A grinding wheel comprising a bond, a filler and the abrasive particles of claim 2.
References Cited (Backward Citations)
US2806800A
Cited
US2814566A
Cited
US3497368A
Cited
US3852078A
Cited
US3808012A
Cited
US4029000A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |