Polymeric hydroxyalkyl sulfonates

Claim 2

A process for preparing a solid, gel-free ionomer which consists essentially of: (a) reacting a polymer having one or more sulfonic acid groups covalently bonded to one or more carbon atoms in one or more molecules with an oxirane to form a polymeric hydroxyalkyl sulfonate said oxirane having the general formula: ##STR5## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof; (b) mixing said polymeric hydroxyalkyl sulfonate with a metallic salt of a fatty acid having a lower K a than an ionomer sulfonic acid groups, wherein said metallic salt is selected from the group consisting of antimony, hydroxyalkyl lead, aluminum and Groups I-A, I-B, II-A and II-B of the Periodic Table of Elements and mixtures thereof; (c) heating the mixture of the polymeric hydroxyalkyl sulfonate and said metallic salt to a reaction temperature to form a mixture of anionomer and a hydroxyalkyl carboxylate ester, said ionomer being a metal neutralized sulfonated polymer and said hydroxyl carboxylate ester having the formula: ##STR6## wherein said R, R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of hydrogen, C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, and arylalkyl groups and functional derivatives thereof and mixtures thereof; and (d) recovering said mixture of said ionomer and said hydroxyalkyl carboxylate ester from said heated mixture.

Claim 3

A process of claim 1, wherein said polymer is selected from the group consisting essentially of: (a) homopolymers and interpolymers of one or more acyclic and alicyclic mono-olefins; (b) homopolymers and interpolymers of one or more alkenyl aromatic hydrocarbon monomers; (c) interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 8 to C 12 vinyl aromatic hydrocarbons; (d) interpolymers of one or more C 8 to C 12 vinyl aromatic hydrocarbons with one or more C 4 to C 10 Type III mono-olefins; (e) elastomeric interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 4 to C 10 Type III mono-olefins; (f) homopolymers and interpolymers of one or more C 4 to C 10 conjugated diolefins; and (g) interpolymers of one or more C 2 to C 18 Type I mono-olefins and one or more C 6 to C 12 acyclic and alicyclic non-conjugated diolefins.

Claim 4

The process of claim 1, wherein said polymer is Butyl rubber.

Claim 5

The process of claim 1, wherein said polymer is an EPDM terpolymer.

Claim 6

The process of claim 1, wherein said oxirane is ethylene oxide.

Claim 7

The process of claim 1, wherein said oxirane is propylene oxide.

Claim 8

The process for the preparation of an ionomer which consists essentially of: (a) dissolving a polymer selected from the group consisting of: random elastomeric interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 4 to C 10 Type III mono-olefins; and random interpolymers of C 2 to C 18 Type I mono-olefins with one or more C 6 to C 12 acyclic or alicyclic non-conjugated diolefins in a solvent nonreactive to sulfuric acid; (b) sulfonating said polymer to contain a level of sulfonic acid in the range of about 10 to about 100 meq. SO 3 H per 100 grams of polymer with a sulfonation reagent comprising sulfuric acid or a coordination compound of sulfur trioxide; (c) reacting said sulfonated polymer in said solvent with an oxirane to give a sulfonated polymer-oxirane reaction product, said oxirane having the general formula: ##STR7## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof; (d) separating said reaction product from said solvent; and (e) mixing and heating said reaction product with from 0.1 to 10 stoichiometric equivalents, based on the sulfonic acid content of said sulfonated polymer, of a metallic salt of a fatty acid to form a metal neutralized sulfonated polymer and a hydroxyalkyl carboxylate ester having the general formula: ##STR8## wherein R, R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof, a metal of said salt being selected from the group consisting essentially of aluminum, lead, antimony, iron and Groups I-A, II-A, I-B and II-B of the Periodic Table of Elements and mixtures thereof.

Claim 9

The process for the preparation of an ionomer which consists essentially of: (a) dissolving a polymer selected from the group consisting of: random elastomeric interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 4 to C 10 Type III mono-olefins; and random interpolymers of C 2 to C 18 Type I mono-olefins with one or more C 6 to C 12 acyclic or alicyclic non-conjugated diolefins in a solvent nonreactive to sulfuric acid; (b) sulfonating said polymer to contain a level of sulfonic acid in the range of about 10 to about 100 meq. SO 3 H per 100 grams of polymer with a sulfonation reagent comprising sulfuric acid or a coordination compound of sulfur trioxide; (c) reacting said sulfonated polymer in said solvent with an oxirane to give a sulfonated polymer-oxirane reaction product, said oxirane having the general formula: ##STR7## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof; (d) separating said reaction product from said solvent; and (e) mixing and heating said reaction product with from 0.1 to 10 stoichiometric equivalents, based on the sulfonic acid content of said sulfonated polymer, of a metallic salt of a fatty acid to form a metal neutralized sulfonated polymer and a hydroxyalkyl carboxylate ester having the general formula: ##STR8## wherein R, R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof, a metal of said salt being selected from the group consisting essentially of aluminum, lead, antimony, iron and Groups I-A, II-A, I-B and II-B of the Periodic Table of Elements and mixtures thereof.

Claim 10

The process according to claim 7, wherein said sulfonation reagent is a mixture of acetic anhydride and concentrated sulfuric acid in an inert solvent.

Claim 11

The process according to claim 7, wherein said interpolymer of said C 4 to C 10 conjugated diolefin and C 4 to C 10 Type III mono-olefin is Butyl rubber.

Claim 12

the process according to claim 7, wherein said interpolymer of said C 2 to C 18 Type I olefin and C 6 to C 12 non-conjugated diolefin is an EPDM elastomer.

Claim 13

The process according to claim 7, wherein said oxirane is ethylene oxide.

Claim 14

The process according to claim 7, wherein said oxirane is propylene oxide.

Claim 15

The process according to claim 7, wherein said metallic salt is magnesium stearate.

Claim 16

A solid, gel-free hydrolytically stable composition comprising the reaction product of a polymer having one or more sulfonic acid groups covalently linked to one or more carbon atoms in one or more molecules comprising said polymer with an oxirane.

Claim 17

A solid, gel-free hydrolytically stable composition comprising the reaction product of a polymer having one or more sulfonic acid groups covalently linked to one or more carbon atoms in one or more molecules comprising said polymer with an oxirane.

Claim 18

Composition of claim 14, wherein said oxirane is ethylene oxide.

Claim 19

Composition of claim 14, wherein said oxirane is propylene oxide.

Claim 20

Composition of claim 14, wherein said polymer is selected from the group consisting essentially of:

Claim 21

(a) homopolymers and interpolymers of one or more acyclic and alicyclic mono-olefins; (b) homopolymers and interpolymers of one or more alkenyl aromatic hydrocarbon monomers; (c) interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 8 to C 12 vinyl aromatic hydrocarbons; (d) interpolymers of one or more C 8 to C 12 vinyl aromatic hydrocarbons with one or more C 4 to C 10 Type III mono-olefins; (e) elastomeric interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 4 to C 10 Type III mono-olefins; (f) homopolymers and interpolymers of one or more C 4 to C 10 conjugated diolefins; and (g) interpolymers of one or more C 2 to C 18 Type I mono-olefins and one or more C 6 to C 12 acyclic and alicyclic non-conjugated diolefins.

Claim 22

(a) homopolymers and interpolymers of one or more acyclic and alicyclic mono-olefins; (b) homopolymers and interpolymers of one or more alkenyl aromatic hydrocarbon monomers; (c) interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 8 to C 12 vinyl aromatic hydrocarbons; (d) interpolymers of one or more C 8 to C 12 vinyl aromatic hydrocarbons with one or more C 4 to C 10 Type III mono-olefins; (e) elastomeric interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 4 to C 10 Type III mono-olefins; (f) homopolymers and interpolymers of one or more C 4 to C 10 conjugated diolefins; and (g) interpolymers of one or more C 2 to C 18 Type I mono-olefins and one or more C 6 to C 12 acyclic and alicyclic non-conjugated diolefins.

Claim 23

A composition of claim 14, wherein said oxirane has the general formula: ##STR9## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consiting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof.

Claim 24

Composition of claim 14, wherein said polymer is selected from the group consisting essentially of Butyl rubber or an EPDM terpolymer.

Claim 25

A solid, gel-free composition of matter which consists essentially of a mixture of: (a) a metal neutralized sulfonated polymer, the sulfonate groups of said polymer being neutralized with a metal counterion selected from the group conisting of lead, iron, antimony, aluminum and Groups I-A, II-A, I-B, and II-B of the Periodic Table of Elements and mixtures thereof; and (b) a hydroxyalkyl carboxylate ester having the formula: ##STR10## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen, C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, and arylalkyl groups and functional derivatives and mixtures thereof, said ##STR11## being derived from a metallic salt of a fatty acid.

Claim 26

A solid, gel-free composition of matter which consists essentially of a mixture of: (a) a metal neutralized sulfonated polymer, the sulfonate groups of said polymer being neutralized with a metal counterion selected from the group conisting of lead, iron, antimony, aluminum and Groups I-A, II-A, I-B, and II-B of the Periodic Table of Elements and mixtures thereof; and (b) a hydroxyalkyl carboxylate ester having the formula: ##STR10## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen, C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, and arylalkyl groups and functional derivatives and mixtures thereof, said ##STR11## being derived from a metallic salt of a fatty acid.

Claim 27

A composition according to claim 20, wherein said oxirane is propylene oxide.

Claim 28

A process for preparing a solid, gel-free ionomer which consists essentially of: (a) reacting a polymer having one or more sulfonic acid groups covalently bonded to one or more carbon atoms in one or more molecules with an oxirane to form a polymeric hydroxyalkyl sulfonate, said oxirane having the general formula: ##STR12## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof; (b) mixing said polymeric hydroxyalkyl sulfonate with a metallic base having a lower K a than said sulfonic acid groups, wherein said metallic base is selected from the group consisting of antimony, iron, lead, aluminum and Groups I-A, II-A, I-B and II-B of the Periodic Table of Elements and mixtures thereof; (c) heating the mixture of the polymeric hydroxyalkyl sulfonate and said metallic base to a reaction temperature to form said ionomer, said ionomer being a metal neutralized sulfonated polymer; and (d) recovering said gel-free ionomer from said heated mixture.

Claim 29

A process for preparing a solid, gel-free ionomer which consists essentially of: (a) reacting a polymer having one or more sulfonic acid groups covalently bonded to one or more carbon atoms in one or more molecules with an oxirane to form a polymeric hydroxyalkyl sulfonate, said oxirane having the general formula: ##STR12## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof; (b) mixing said polymeric hydroxyalkyl sulfonate with a metallic base having a lower K a than said sulfonic acid groups, wherein said metallic base is selected from the group consisting of antimony, iron, lead, aluminum and Groups I-A, II-A, I-B and II-B of the Periodic Table of Elements and mixtures thereof; (c) heating the mixture of the polymeric hydroxyalkyl sulfonate and said metallic base to a reaction temperature to form said ionomer, said ionomer being a metal neutralized sulfonated polymer; and (d) recovering said gel-free ionomer from said heated mixture.

Claim 30

A process of claim 22, wherein said polymer is selected from the group consisting essentially of: (a) homopolymers and interpolymers of one or more acyclic and alicyclic mono-olefins; (b) homopolymers and interpolymers of one or more alkenyl aromatic hydrocarbon monomers; (c) interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 8 to C 12 vinyl aromatic hydrocarbons; (d) interpolymers of one or more C 8 to C 12 vinyl aromatic hydrocarbons with one or more C 4 to C 10 Type III mono-olefins; (e) elastomeric interpolymers of one or more C 4 to C 10 conjugated diolefins with one or more C 4 to C 10 Type III mono-olefins; (f) homopolymers and interpolymers of one or more C 4 to C 10 conjugated diolefins; and (g) interpolymers of one or more C 2 to C 18 Type I mono-olefins and one or more C 6 to C 12 acyclic and alicyclic non-conjugated diolefins.

Claim 31

The process of claim 22, wherein said polymer is Butyl rubber.

Claim 32

The process of claim 22, wherein said polymer is an EPDM terpolymer.

Claim 33

The process of claim 22, wherein said oxirane is ethylene oxide.

Claim 34

The process of claim 22, wherein said oxirane is propylene oxide.

Claim 35

The product prepared by the process of claim 1.

Claim 36

The product prepared by the process of claim 7.

Claim 37

The product prepared by the process of claim 22.

Claim 38

A gel-free hydrolytically stable polymeric composition which consists essentially of a mixture of the reaction product of a hydroxyalkyl polymeric sulfonate and a metallic base, said hydroxyalkyl polymeric sulfonate being derived from the reaction product of a polymeric sulfonic acid and an oxirane having the general formula: ##STR13## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof, said metallic base having a metal ion selected from the group consisting of iron, lead, aluminum and Groups I-A, I-B, II-A and II-B of the Periodic Table of Elements and mixtures thereof.

Claim 39

A gel-free hydrolytically stable polymeric composition which consists essentially of a mixture of the reaction product of a hydroxyalkyl polymeric sulfonate and a metallic base, said hydroxyalkyl polymeric sulfonate being derived from the reaction product of a polymeric sulfonic acid and an oxirane having the general formula: ##STR13## wherein R 1 , R 2 , R 3 and R 4 are independently selected from the group consisting of hydrogen and C 1 to C 18 straight and branched chain acyclic, alicyclic, aryl, alkylaryl, arylalkyl radicals and functional derivatives thereof, said metallic base having a metal ion selected from the group consisting of iron, lead, aluminum and Groups I-A, I-B, II-A and II-B of the Periodic Table of Elements and mixtures thereof.

Claim 40

The composition of claim 31 wherein said sulfonated polymer is derived from Butyl rubber.

Claim 41

The composition of claim 31, wherein said sulfonated polymer is derived from an EPDM terpolymer.

Claim 42

The process of claim 31, wherein said oxirane is ethylene oxide.

Claim 43

The process of claim 31, wherein said oxirane is propylene oxide.