Torsion bar and method of forming the same
Assignee: FMC Corp
•
Filing: 1977-12-22
•
Granted: 1978-12-26
•
Expires: 1997-12-22
Abstract
Abstract A method of forming a torsion bar wherein steel, preferably an alloy steel of medium carbon content, is formed in the desired size and shape and is through hardened for providing a desired core hardness. The case of the bar is then hardened for transforming austenite in the case into martensite causing the case to expand thereby inducing high compressive stresses near the surface with the compressive stress decreasing radially inward of the surface. The core of the bar is retained below lower transformation temperature for resisting expansion of the case thereby inducing hoop and axial compressive stresses and radial tensile stressed in the case. The hardened bar is then cold worked by twisting and releasing the bar at least twice for applying a torsional stress in the angular direction of the bar loading which presets the bar by twisting it beyond its initial yield strength for redistributing the stresses and inducing a residual torsional stress therein in a direction opposite to the preset direction. A torsion bar formed by the method of the present invention is also disclosed.
Inventors
- 👤 George L. Joseph
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:25
CPC Classifications
B; B60; B60G; B60G21/00; B60G21/02; B60G21/04; B60G21/05; B60G21/055; B60G21/0551; C; C21; C21D; C21D1/00; C21D1/06; C21D7/00; C21D7/02; C21D7/10; B60G2204/00; B60G2204/10; B60G2204/12; B60G2204/122; B60G2204/1222; B60G2204/40; B60G2204/44; B60G2204/45; B60G2206/00; B60G2206/01; B60G2206/40; B60G2206/42; B60G2206/427; B60G2206/80; B60G2206/84; B60G2206/8402; B60G2206/8403
Claims Analysis
Total Claims: 51
Claim 1
Independent Claim
182 words
A method of forming a torsion bar having an outer case and a core from a steel alloy bar of the desired size and shape and with a medium carbon content, or a steel bar having similar hardenability characteristics; comprising the steps of through hardening the bar to a predetermined hardness, case hardening the bar for transforming austenite in the case into martensite which expands inducing a high compressive stress near the surface of the bar with the compressive stresses diminishing radially inward to the center of the bar, retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stresses in the case, and presetting the hardened bar by cold working the bar at least twice by applying sufficient torsional stresses on the bar for twisting the bar beyond its initial yield strength causing a redistribution of stresses and inducing residual torsional stresses in the case and in the core in a direction opposite to the direction of the applied torque.
Claim 2
Independent Claim
182 words
A method of forming a torsion bar having an outer case and a core from a steel alloy bar of the desired size and shape and with a medium carbon content, or a steel bar having similar hardenability characteristics; comprising the steps of through hardening the bar to a predetermined hardness, case hardening the bar for transforming austenite in the case into martensite which expands inducing a high compressive stress near the surface of the bar with the compressive stresses diminishing radially inward to the center of the bar, retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stresses in the case, and presetting the hardened bar by cold working the bar at least twice by applying sufficient torsional stresses on the bar for twisting the bar beyond its initial yield strength causing a redistribution of stresses and inducing residual torsional stresses in the case and in the core in a direction opposite to the direction of the applied torque.
Claim 3
Dependent Claim
29 words
A method according to claim 1 wherein the steel bar is a steel alloy bar having a carbon content within the range of about 0.28 to 0.60 percent carbon.
Claim 4
Independent Claim
195 words
A method of forming a torsion bar having an outer case and a core from a steel alloy bar having a circular cross section and a medium carbon content or a steel bar having similar hardenability characteristics; comprising the steps of forming the bar into the desired size and shape with non-circular anchoring means on both end portions thereof, through hardening the bar to a predetermined hardness, case hardening the bar for transforming austenite in the case into martensite which expands inducing a high compressive stress near the surface of the bar with the compressive stresses diminishing radially inward of the surface, retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stresses in the case, and presetting the hardened bar by cold working the bar at least twice by applying sufficient torsional stresses on the bar for twisting the bar beyond its initial yield strength causing a redistribution of stresses and inducing residual torsional stresses in the case and in the core in a direction opposite to the direction of the applied torque.
Claim 5
Independent Claim
195 words
A method of forming a torsion bar having an outer case and a core from a steel alloy bar having a circular cross section and a medium carbon content or a steel bar having similar hardenability characteristics; comprising the steps of forming the bar into the desired size and shape with non-circular anchoring means on both end portions thereof, through hardening the bar to a predetermined hardness, case hardening the bar for transforming austenite in the case into martensite which expands inducing a high compressive stress near the surface of the bar with the compressive stresses diminishing radially inward of the surface, retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stresses in the case, and presetting the hardened bar by cold working the bar at least twice by applying sufficient torsional stresses on the bar for twisting the bar beyond its initial yield strength causing a redistribution of stresses and inducing residual torsional stresses in the case and in the core in a direction opposite to the direction of the applied torque.
Claim 6
Dependent Claim
29 words
A method according to claim 3 wherein the steel bar is a steel alloy bar having a carbon content within the range of about 0.28 to 0.60 percent carbon.
Claim 7
Dependent Claim
24 words
A method according to claim 3 wherein the bar is through hardened to provide a core hardness of between about Rockwell C20 to C45.
Claim 8
Dependent Claim
16 words
A method according to claim 5 wherein the bar is through hardened by quenching and tempering.
Claim 9
Dependent Claim
23 words
A method according to claim 3 wherein induction hardening provides a case depth of between about 20% to 45% of the bar radius.
Claim 10
Dependent Claim
28 words
A method according to claim 3 wherein induction hardening is effective to provide a minimum hardness at 0.01 inches below the surface of the case of Rockwell C46.
Claim 11
Dependent Claim
28 words
A method according to claim 7 wherein induction hardening is effective to provide a minimum hardness at 0.01 inches below the surface of the case of Rockwell C46.
Claim 12
Dependent Claim
43 words
A method according to claim 4 wherein the selected steel alloy has a carbon content of about 0.46 percent to 0.53 percent, and additionally comprising the step of drawing the torsion bar at a temperature up to about 400° F. after induction hardening.
Claim 13
Dependent Claim
43 words
A method according to claim 9 wherein the selected steel alloy has a carbon content of about 0.46 percent to 0.53 percent, and additionally comprising the step of drawing the torsion bar at a temperature up to about 400° F. after induction hardening.
Claim 14
Dependent Claim
88 words
A method according to claim 3 wherein presetting the bar by cold working is performed by cyclically twisting and relaxing the bar at least three times while gradually increasing predetermined applied torque stresses to the bar for minimizing excessive angular yielding of the bar during each cycle and for gradually increasing the residual torsional stress in the bar, the applied presetting twisting torque being in the same direction as the working load subsequently applied to the bar and the induced residual torsional stress being in the opposite direction.
Claim 15
Dependent Claim
57 words
A method according to claim 12 wherein nine cold working cycles are applied to the bar with the predetermined applied torque for the first three cycles being the lowest, the predetermined applied torque for the next three cycles being at an intermediate stress, and with the next three cycles being twisted at the third predetermined torque stress.
Claim 16
Dependent Claim
42 words
A method according to claim 13 wherein the three predetermined applied torsional stresses are about 8442 foot pounds, 8970 foot pounds, and 9498 foot pounds for alloy steels having a carbon content within the range of about 0.38 percent to 0.43 percent.
Claim 17
Dependent Claim
42 words
A method according to claim 13 wherein the three predetermined applied torsional stresses are about 8442 foot pounds, 8707 foot pounds and 8970 foot pounds for alloy steels having a carbon content within the range of about 0.28 percent to 0.33 percent.
Claim 18
Dependent Claim
22 words
A method according to claim 15 wherein the maximum degree of permanent set during cold working of AISI 4130 steel is 45°.
Claim 19
Dependent Claim
20 words
A method according to claim 15 wherein the maximum degree of permanent set of AISI 4140 alloy steel is 14°.
Claim 20
Dependent Claim
20 words
A method according to claim 15 wherein the maximum degree of permanent set of AISI 4150 alloy steel is 21°.
Claim 21
Dependent Claim
20 words
A method according to claim 15 wherein the maximum degree of permanent set of AISI 4340 alloy steel is 8°.
Claim 22
Dependent Claim
23 words
A method according to claim 3 and additionally including the step of protecting the surface of the bar by shot peening the bar.
Claim 23
Dependent Claim
49 words
A method according to claim 3 and additionally including the step of protecting the surface of the bar by applying an adhesive primer to the bar, and applying a coating of plastic over the primer on the body of the bar and priming the ends with zinc rich primer.
Claim 24
Independent Claim
266 words
A method of forming a torsion bar having an outer case and a core from a steel alloy having a medium carbon content of between about 0.28% to 0.60% carbon; comprising the steps of forming the bar into the desired size and shape with a circular body and non-circular anchoring means on both end portions thereof, through hardening the bar to a hardness within the range of about Rockwell C25 to C40, induction hardening the bar for transforming austenite in the case into martensite causing expansion of the case which induces a high compressive stress near the surface of the case, said compressive stresses diminishing radially inward of the bar, said induction hardening forming a case having a depth within the range of about 25% to 40% of the radius of the bar and a minimum hardness at 0.005 inches below the surface of Rockwell C52, retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stress in the case and in the core, increasing torsional yield strength by twisting the bar beyond its elastic limit in the direction of working torque by applying a torque of at least 105% of the initial yield torque, relaxing the bar after the initial twisting for inducing a residual torsional stress in the bar in the opposite direction, and repeating the twisting and relaxing cycle at least two more times with the applied yield torque for the second cycle being at least 108% of the initial yield torque.
Claim 25
Independent Claim
266 words
A method of forming a torsion bar having an outer case and a core from a steel alloy having a medium carbon content of between about 0.28% to 0.60% carbon; comprising the steps of forming the bar into the desired size and shape with a circular body and non-circular anchoring means on both end portions thereof, through hardening the bar to a hardness within the range of about Rockwell C25 to C40, induction hardening the bar for transforming austenite in the case into martensite causing expansion of the case which induces a high compressive stress near the surface of the case, said compressive stresses diminishing radially inward of the bar, said induction hardening forming a case having a depth within the range of about 25% to 40% of the radius of the bar and a minimum hardness at 0.005 inches below the surface of Rockwell C52, retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stress in the case and in the core, increasing torsional yield strength by twisting the bar beyond its elastic limit in the direction of working torque by applying a torque of at least 105% of the initial yield torque, relaxing the bar after the initial twisting for inducing a residual torsional stress in the bar in the opposite direction, and repeating the twisting and relaxing cycle at least two more times with the applied yield torque for the second cycle being at least 108% of the initial yield torque.
Claim 26
Dependent Claim
24 words
A method according to claim 22 wherein the torque applied to the bar when relaxed is less than 50% of the initial yield torque.
Claim 27
Dependent Claim
12 words
A method according to claim 23 wherein the relaxed torque is 0.
Claim 28
Dependent Claim
53 words
A method according to claim 22 wherein the selected steel alloy has a carbon content of about 0.38% to 0.43%, and additionally comprising the step of drawing the torsion bar at a temperature up to about 400° F. for a time interval of about 1 hour per inch of diameter after induction hardening.
Claim 29
Dependent Claim
29 words
A method according to claim 22 wherein the maximum degree of permanent set permitted in a bar of AISI 4130 steel while increasing the torsional yield strength is 45°.
Claim 30
Dependent Claim
29 words
A method according to claim 22 wherein the maximum degree of permanent set permitting in a bar of AISI 4140 steel while increasing the torsional yield strength is 14°.
Claim 31
Dependent Claim
29 words
A method according to claim 22 wherein the maximum degree of permanent set permitted in a bar of AISI 4150 steel while increasing the torsional yield strength is 21°.
Claim 32
Dependent Claim
29 words
A method according to claim 22 wherein the maximum degree of permanent set permitted in a bar of AISI 4340 steel while increasing the torsional yield strength is 8°.
Claim 33
Dependent Claim
23 words
A method according to claim 22 and additionally including the step of protecting the surface of the bar by shot peening the bar.
Claim 34
Dependent Claim
42 words
A method according to claim 22 and additionally including the step of protecting the surface of the bar by applying an adhesive primer to the bar, and thereafter applying a coating of plastic over the primer on the body of the bar.
Claim 35
Independent Claim
288 words
A method of forming a torsion bar having an outer case and a core from a steel alloy having a medium carbon content of between about 0.38% to 0.60%; comprising the steps of forming the bar into the desired size and shape with a body of circular cross section and non-circular anchoring means on both end portions thereof, through hardening the bar to a hardness within the range of about Rockwell C30 to C40 by quenching and drawing, induction hardening the bar for transforming austenite in the case into martensite causing expansion of the case which induces a high compressive stress near the surface of the case, which compressive stress diminishes radially inward of the bar, said induction hardening forming a case having a depth within the range of about 25% to 40% of the radius of the bar and a minimum hardness at 0.005 inches below the surface of Rockwell C54, retaining the core at a temperature below the lower transformation temperature for resisting expansion of both the case and the core for inducing hoop and axial compressive stresses and radial tensile stress in the case and the core, increasing torsional yield strength by twisting the bar after hardening beyond its elastic limit in the direction of working torque by applying a torque at least 105% of the initial yield torque, relaxing the bar after the initial twisting for inducing a residual torsional stress in the bar in the opposite direction, and repeating the twisting and relaxing cycle at least two more times with the applied yield torque for the second cycle being at least 108% of the initial yield torque, the torque on the bar when relaxed being less than 50% of the initial yield torque.
Claim 36
Independent Claim
288 words
A method of forming a torsion bar having an outer case and a core from a steel alloy having a medium carbon content of between about 0.38% to 0.60%; comprising the steps of forming the bar into the desired size and shape with a body of circular cross section and non-circular anchoring means on both end portions thereof, through hardening the bar to a hardness within the range of about Rockwell C30 to C40 by quenching and drawing, induction hardening the bar for transforming austenite in the case into martensite causing expansion of the case which induces a high compressive stress near the surface of the case, which compressive stress diminishes radially inward of the bar, said induction hardening forming a case having a depth within the range of about 25% to 40% of the radius of the bar and a minimum hardness at 0.005 inches below the surface of Rockwell C54, retaining the core at a temperature below the lower transformation temperature for resisting expansion of both the case and the core for inducing hoop and axial compressive stresses and radial tensile stress in the case and the core, increasing torsional yield strength by twisting the bar after hardening beyond its elastic limit in the direction of working torque by applying a torque at least 105% of the initial yield torque, relaxing the bar after the initial twisting for inducing a residual torsional stress in the bar in the opposite direction, and repeating the twisting and relaxing cycle at least two more times with the applied yield torque for the second cycle being at least 108% of the initial yield torque, the torque on the bar when relaxed being less than 50% of the initial yield torque.
Claim 37
Dependent Claim
152 words
A torsion bar comprising; a steel bar having a hardenability characteristic similar to an alloy steel having a carbon content within the range of about 0.28% to 0.06%, said bar including an outer case and a core within the case, said case including a variable composition of martensite and austenite with a high percent of martensite being at the outer surface and diminishing to approximately 80% martensite at the interface between the case and the core, said case having an induced hardness at 0.01 inches below the surface of a minimum of Rockwell C46 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C20 to C45, said case and core having torsional stresses induced therein which act in a direction opposite to that of the torsional load to be applied to the bar during normal operation.
Claim 38
Dependent Claim
152 words
A torsion bar comprising; a steel bar having a hardenability characteristic similar to an alloy steel having a carbon content within the range of about 0.28% to 0.06%, said bar including an outer case and a core within the case, said case including a variable composition of martensite and austenite with a high percent of martensite being at the outer surface and diminishing to approximately 80% martensite at the interface between the case and the core, said case having an induced hardness at 0.01 inches below the surface of a minimum of Rockwell C46 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C20 to C45, said case and core having torsional stresses induced therein which act in a direction opposite to that of the torsional load to be applied to the bar during normal operation.
Claim 39
Dependent Claim
25 words
A torsion bar according to claim 33 wherein the bar is generated about a linear axis and wherein said linear bar has non-circular end portions.
Claim 40
Dependent Claim
35 words
A torsion bar according to claim 33 and additionally comprising a coating of adhesive primer over the body and over the non-circular end portions, and a coating of plastic over the primer on the body.
Claim 41
Dependent Claim
36 words
A torsion bar according to claim 33 wherein one end of the bar is twisted relative to the other end through a maximum of about 45° of permanent set when the alloy is AISI 4130 steel.
Claim 42
Dependent Claim
36 words
A torsion bar according to claim 33 wherein one end of the bar is twisted relative to the other end through a maximum of about 14° of permanent set when the alloy is AISI 4140 steel.
Claim 43
Dependent Claim
36 words
A torsion bar according to claim 33 wherein one end of the bar is twisted relative to the other end through a maximum of about 21° of permanent set when the alloy is AISI 4150 steel.
Claim 44
Dependent Claim
36 words
A torsion bar according to claim 33 wherein one end of the bar is twisted relative to the other end through a maximum of about 8° of permanent set when the alloy is AISI 4340 steel.
Claim 45
Dependent Claim
23 words
A torsion bar according to claim 33 wherein the case has a radial depth of about 20% to 40% of the bar radius.
Claim 46
Dependent Claim
158 words
A torsion bar comprising; a steel bar having a body of circular cross section and hardenability characteristics similar to an alloy steel having a carbon content within the range of about 0.28% to 0.60%, said bar including an outer case and a core within the case, said case including a variable composition of martensite and austenite with a high percent of martensite being at the outer surface and diminishing to approximately 80% martensite at the interface between the case and the core, said case having an induced hardness at 0.01 inches below the surface of a minimum of Rockwell C46 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C20 to C45, said case and core having torsional stresses induced therein which act in a direction opposite to that of the torsional load to be applied to the bar during normal operation.
Claim 47
Dependent Claim
158 words
A torsion bar comprising; a steel bar having a body of circular cross section and hardenability characteristics similar to an alloy steel having a carbon content within the range of about 0.28% to 0.60%, said bar including an outer case and a core within the case, said case including a variable composition of martensite and austenite with a high percent of martensite being at the outer surface and diminishing to approximately 80% martensite at the interface between the case and the core, said case having an induced hardness at 0.01 inches below the surface of a minimum of Rockwell C46 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C20 to C45, said case and core having torsional stresses induced therein which act in a direction opposite to that of the torsional load to be applied to the bar during normal operation.
Claim 48
Dependent Claim
25 words
A torsion bar according to claim 41 wherein the bar is generated about a linear axis and wherein said linear bar has non-circular end portions.
Claim 49
Dependent Claim
166 words
A torsion bar comprising; an alloy steel bar having a body of circular cross section and a carbon content within the range of about 0.28% to 0.60%, said bar including an outer case and a core with the case having a radial depth of between about 25% to 40% of the bar radius, said case including a variable composition of martensite and austenite with a high percent of the martensite being at the outer surface and diminishing to approximately 30% martensite at the interface between the case and the core, said case having an induced hardness at 0.005 inches below the surface of the minimum of Rockwell C52 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C25 to C40, said case and core having torsional stresses induced therein which act in a direction opposite to that of the torsional load to be applied to the bar during normal operation.
Claim 50
Dependent Claim
166 words
A torsion bar comprising; an alloy steel bar having a body of circular cross section and a carbon content within the range of about 0.28% to 0.60%, said bar including an outer case and a core with the case having a radial depth of between about 25% to 40% of the bar radius, said case including a variable composition of martensite and austenite with a high percent of the martensite being at the outer surface and diminishing to approximately 30% martensite at the interface between the case and the core, said case having an induced hardness at 0.005 inches below the surface of the minimum of Rockwell C52 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C25 to C40, said case and core having torsional stresses induced therein which act in a direction opposite to that of the torsional load to be applied to the bar during normal operation.
Claim 51
Dependent Claim
25 words
A torsion bar according to claim 43 wherein the bar is generated about a linear axis and wherein said linear bar has non-circular end portions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-25 | 1982-06-26 | 1982-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-25 | 1986-06-26 | 1986-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-25 | 1990-06-26 | 1990-12-26 | $7700.00 | Window Closed / Lapsed |