Process for applying to glass an organic coating having controlled bond strength
Assignee: EIDP Inc
•
Filing: 1977-10-21
•
Granted: 1978-12-19
•
Expires: 1997-10-21
Abstract
Abstract A glass surface is first coated with very thin layers of gamma -aminopropyltriethoxysilane and low molecular weight polyethylene, which may be applied separately or simultaneously. A coating of a copolymer of an alpha -olefin with an alpha , beta -unsaturated carboxylic acid is then applied to the precoated glass surface and heated to form a uniform film, which is capable of delaminating from glass and containing cullet upon impact resulting in glass breakage. This process if of special interest in coating the outer surfaces of glass containers to protect persons or property from injury or damage.
Inventors
- 👤 James R. Huntsberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 02:00
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/3405
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
184 words
A process for applying to glass a coating capable of delamination and stretching upon impact resulting in glass breakage, said process comprising: (1) applying to a glass surface free from materials which are non-dispersible in water a two-component coating which contains as one component γ-aminopropyltriethoxysilane that bonds directly to the glass, and as the other component polyethylene having an average molecular weight within the range of approximately 1000 to 2000 in an amount such that the γ-aminopropyltriethoxysilane/polyethylene layer will be about 0.05-0.25 μm thick when dry, the proportion of γ-aminopropyltriethoxysilane being approximately 5-30% based on the weight of the polyethylene; (2) drying the coating applied in step (1); (3) applying to the above dry coating a second coating of a copolymer of an α-olefin having 3-10 carbon atoms and of an α,β-unsaturated carboxylic acid having 3-8 carbon atoms, the mole proportion of the carboxylic acid being about 0.2-5% of the total monomers; and (4) heating the coating to a sufficiently high temperature to form a continuous film; the amount of the copolymer being such that the dry copolymer film is about 0.07-0.40 mm thick.
Claim 2
Dependent Claim
184 words
A process for applying to glass a coating capable of delamination and stretching upon impact resulting in glass breakage, said process comprising: (1) applying to a glass surface free from materials which are non-dispersible in water a two-component coating which contains as one component γ-aminopropyltriethoxysilane that bonds directly to the glass, and as the other component polyethylene having an average molecular weight within the range of approximately 1000 to 2000 in an amount such that the γ-aminopropyltriethoxysilane/polyethylene layer will be about 0.05-0.25 μm thick when dry, the proportion of γ-aminopropyltriethoxysilane being approximately 5-30% based on the weight of the polyethylene; (2) drying the coating applied in step (1); (3) applying to the above dry coating a second coating of a copolymer of an α-olefin having 3-10 carbon atoms and of an α,β-unsaturated carboxylic acid having 3-8 carbon atoms, the mole proportion of the carboxylic acid being about 0.2-5% of the total monomers; and (4) heating the coating to a sufficiently high temperature to form a continuous film; the amount of the copolymer being such that the dry copolymer film is about 0.07-0.40 mm thick.
Claim 3
Dependent Claim
16 words
The process of claim 1 wherein γ-aminopropyltriethoxysilane and polyethylene are applied simultaneously from an aqueous dispersion.
Claim 4
Dependent Claim
16 words
The process of claim 1 wherein γ-aminopropyltriethoxysilane is applied to the glass surface before the polyethylene.
Claim 5
Dependent Claim
11 words
The process of claim 1 wherein the polyethylene is partially oxidized.
Claim 6
Dependent Claim
52 words
The process of claim 1 wherein the copolymer of an α-olefin with an α,β-unsaturated carboxylic acid is a terpolymer with a monoethylenically unsaturated third monomer, the concentration of the α-olefin-derived portion of the copolymer being at least 70 mole %, and the concentration of the third monomer being about 0.2-25 mole %.
Claim 7
Dependent Claim
32 words
The process of claim 5 wherein the concentration of the α-olefin-derived portion of the copolymer is at least 80 mole %, and the concentration of the third monomer is 1-10 mole %.
Claim 8
Dependent Claim
26 words
The process of claim 6 wherein the third monomer is a C 4 -C 18 alkyl ester of an α,β-unsaturated C 3 -C 8 carboxylic acid.
Claim 9
Dependent Claim
13 words
The process of claim 7 wherein the alkyl group is a butyl group.
Claim 10
Dependent Claim
18 words
The process of claim 1 wherein the copolymer is a dipolymer of ethylene with an α,β-unsaturated carboxylic acid.
Claim 11
Dependent Claim
13 words
The process of claim 9 wherein the α,β-unsaturated carboxylic acid is methacrylic acid.
Claim 12
Dependent Claim
19 words
The process of claim 1 wherein the copolymer is a copolymer of ethylene, propylene, and an α,β-unsaturated carboxylic acid.
Claim 13
Dependent Claim
15 words
The process of claim 1 wherein the copolymer is at least partly in ionized form.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-18 | 1982-06-19 | 1982-12-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-18 | 1986-06-19 | 1986-12-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-18 | 1990-06-19 | 1990-12-19 | $7700.00 | Window Closed / Lapsed |