Thermoplastic vulcanizates of olefin rubber and polyolefin resin

Claim 2

A thermoplastic elastomeric composition comprising a blend of about 25 to about 85 parts by weight of crystalline thermoplastic polyolefin resin and about 75 to about 15 parts by weight of vulcanized monoolefin copolymer rubber per 100 parts total weight of said resin and rubber, and extender oil up to 300 parts by weight per 100 parts by weight of rubber provided that, when the amount of resin is greater than 75 parts by weight, extender oil must be present in an amount sufficient to satisfy the equation (W o + W R )/W P is equal to or greater than 0.33 wherein W o is the weight of extender oil, W R is the weight of rubber and W p is the weight of resin, wherein the rubber in said blend is a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1-12 carbon atoms and from none to a minor portion of at least one copolymerizable diene in the form of small dispersed particles essentially of a size of about 50 microns or below and is vulcanized to the extent that no more than about three percent of the rubber is extractable in cyclohexane at 23° C. or that the cross-link density determined on the same monoolefin copolymer rubber as in the blend is greater than about 7 × 10 -5 moles per ml of rubber, the composition being processable in an internal mixer to a product which, upon transferring, with the resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 3

The composition of claim 1 in which the resin is polypropylene and the rubber is EPDM rubber which is a product from the polymerization of ethylene, propylene and a lesser quantity of a non-conjugated diene, in the proportions of about 25-75 parts by weight polypropylene and about 75-25 parts by weight of EPDM rubber.

Claim 4

The composition of claim 1 containing about 30 to 250 parts by weight extender oil per 100 parts by weight of rubber.

Claim 5

The composition of claim 1 in which (W o + W R )/W P is equal to or greater than 0.5.

Claim 6

The composition of claim 3 in which the rubber is vulcanized to the extent that the blend has a tensile strength at least about 60 Kg./sq.cm. greater than that of the unvulcanized blend.

Claim 7

A thermoplastic elastomeric composition comprising a blend of (a) about 25-75 parts by weight of crystalline thermoplastic polyolefin resin and (b) about 75-25 parts by weight of vulcanized monoolefin copolymer rubber, the rubber being a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1 to 12 carbon atoms and from none to a minor portion of at least one copolymerizable diene, and being sufficiently small dispersed particles vulcanized to the extent that the blend has a tensile strength at least about 60 Kg./sq.cm. greater than that of the unvulcanized blend, the composition being processable in an internal mixer to a product which, upon transferring, with the resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 8

A thermoplastic elastomeric composition comprising a blend of (a) about 25-75 parts by weight of crystalline thermoplastic polyolefin resin and (b) about 75-25 parts by weight of vulcanized monoolefin copolymer rubber, the rubber being a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1 to 12 carbon atoms and from none to a minor portion of at least one copolymerizable diene, and being sufficiently small dispersed particles vulcanized to the extent that the blend has a tensile strength at least about 60 Kg./sq.cm. greater than that of the unvulcanized blend, the composition being processable in an internal mixer to a product which, upon transferring, with the resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 9

The composition of claim 6 in which the rubber is vulcanized to the extent either that no more than three percent by weight of the rubber is extractable in cyclohexane at 23° C. or that the cross-link density determined on the same monoolefin copolymer rubber as in the composition is greater than about 7 × 10 -5 moles per ml of rubber.

Claim 10

The composition of claim 6 in which the rubber is vulcanized to the extent that no more than three percent by weight of the rubber is extractable in cyclohexane at 23° C.

Claim 11

The composition of claim 8 in which the resin is polypropylene or polyethylene and the rubber is EPDM rubber which is a product from the polymerization of ethylene, propylene and a lesser quantity of a non-conjugated diene.

Claim 12

The composition of claim 9 in which the resin is polypropylene.

Claim 13

The composition of claim 10 in which the crosslink density determined on the same EPDM rubber as in the blend is greater than 7 × 10 -5 moles per ml of rubber.

Claim 14

The composition of claim 11 in which the blend comprises about 30 to about 70 parts by weight polypropylene and about 30 to about 70 parts by weight EPDM rubber.

Claim 15

The composition of claim 12 which is vulcanized by a sulfur-vulcanizing agent.

Claim 16

The composition of claim 12 in which the rubber is dispersed particles smaller than about 50 microns.

Claim 17

The composition of claim 14 having a tensile strength of about 100 Kg./sq.cm. greater than that of the unvulcanized composition.

Claim 18

The composition of claim 7 which is vulcanized to the extent that the cross-link density is greater than 7 × 10 -5 moles per ml of rubber.

Claim 19

The composition of claim 16 in which the resin is polypropylene and the rubber is EPDM rubber which is a product from the polymerization of ethylene, propylene and a lesser quantity of a non-conjugated diene.

Claim 20

The composition of claim 17 in which the blend comprises about 30 to about 70 parts by weight polypropylene and about 30 to about 70 parts by weight EPDM rubber and the diene is ethylidene norbornene.

Claim 21

The composition of claim 18 which is vulcanized by a sulfur-vulcanizing agent.

Claim 22

The composition of claim 18 in which the rubber is dispersed particles smaller than about 10 microns.

Claim 23

The composition of claim 20 having a tensile strength of about 100 Kg./sq.cm. greater than that of the unvulcanized composition.

Claim 24

The composition of claim 6 containing about 30 to about 250 parts by weight extender oil.

Claim 25

The composition of claim 9 containing about 30 to 250 parts by weight extender oil per 100 parts by weight of rubber.

Claim 26

The composition of claim 15 containing about 30 to 250 parts by weight extender oil per 100 parts by weight of rubber.

Claim 27

The composition of claim 23 in which the blend contains carbon black in the amount of 2-250 parts by weight per 100 parts by weight rubber.

Claim 28

The composition of claim 24 in which the diene is ethylidene norbornene.

Claim 29

The composition of claim 9 in which the resin is polyethylene.

Claim 30

The composition of claim 22 containing 20 to 100 parts by weight carbon black per 100 parts total weight of rubber and extender oil.

Claim 31

The composition of claim 1 containing 5-300 parts by weight extender oil per 100 parts total weight of rubber and olefin resin and 20-100 parts by weight carbon black per 100 parts total weight of rubber and extender oil.

Claim 32

The composition of claim 24 in which the polydispersity of the rubber prior to vulcanization is less than about 3.5.

Claim 33

The composition of claim 16 in which the polydispersity of the rubber prior to vulcanization is less than about 3.5.

Claim 34

The composition of claim 1 which is prepared by the dynamic vulcanization of the unvulcanized blend.

Claim 35

The composition of claim 10 which is prepared by the dynamic vulcanization of the unvulcanized blend.

Claim 36

The composition of claim 33 which the rubber is vulcanized to the extent that no more than three percent by weight of the rubber is extractable in cyclohexane at 23° C. or that the cross-link density determined on the same monoolefin copolymer rubber as in the composition is greater than about 7 × 10 -5 moles per ml of rubber.

Claim 37

The composition of claim 34 in which the polypropylene is about 30 to about 70 parts by weight and the EPDM rubber is about 70 to about 30 parts.

Claim 40

A process of making a thermoplastic filled elastomeric composition which comprises blending (a) about 25-75 parts by weight of crystalline thermoplastic polyolefin resin and (b) about 75-25 parts by weight of a homogeneous mixture of unvulcanized but vulcanizable monoolefin copolymer rubber and filler at a temperature sufficient to melt said resin, adding vulcanizing ingredients to the blend of (a) and (b) to form a vulcanizable blend, then masticating the blend continuously at vulcanization temperature until the rubber, a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1 to 12 carbon atoms and from none to a minor portion of at least one copolymerizable diene, is sufficiently small dispersed particles vulcanized to the extent that the blend has a tensile strength at least 60 Kg./sq.cm. greater than that of the unvulcanized blend, said composition being processable in an internal mixer to a product which, upon transferring, with said resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 41

A process of making a thermoplastic filled elastomeric composition which comprises blending (a) about 25-75 parts by weight of crystalline thermoplastic polyolefin resin and (b) about 75-25 parts by weight of a homogeneous mixture of unvulcanized but vulcanizable monoolefin copolymer rubber and filler at a temperature sufficient to melt said resin, adding vulcanizing ingredients to the blend of (a) and (b) to form a vulcanizable blend, then masticating the blend continuously at vulcanization temperature until the rubber, a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1 to 12 carbon atoms and from none to a minor portion of at least one copolymerizable diene, is sufficiently small dispersed particles vulcanized to the extent that the blend has a tensile strength at least 60 Kg./sq.cm. greater than that of the unvulcanized blend, said composition being processable in an internal mixer to a product which, upon transferring, with said resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 42

The process of claim 37 in which the filler is carbon black in an amount of 2-250 parts by weight per 100 parts by weight rubber.

Claim 43

The process of claim 38 in which the mixture (b) contains extender oil in an amount of 5-300 parts by weight per 100 parts total weight of rubber and resin.

Claim 44

The process of claim 39 wherein the thermoplastic resin is polypropylene and the rubber is a copolymer of monomers comprising ethylene, propylene and and a lesser quantity of a con-conjugated diene.

Claim 45

A process of making a thermoplastic elastomeric filled composition comprising (a) about 25-85 parts by weight of crystalline thermoplastic polyolefin resin, (b) about 75-15 parts by weight of monoolefin copolymer rubber per 100 parts total of resin and rubber, and extender oil up to 300 parts by weight per 100 parts by weight of rubber provided that, when the amount of resin is greater than 75 parts by weight, extender oil must be present in an amount sufficient to satisfy the equation (W o + W R )/W P is equal to or greater than 0.33 wherein W o is the weight of extender oil, W R is the weight of rubber and W P is the weight of resin, and (c) about 5-300 parts by weight filler per 100 parts total weight of resin and rubber in the final composition which comprises blending (a) with a preformed mixture of (b) and (c) and vulcanizing ingredients, at a temperature sufficient to melt said resin, then masticating the blend continuously at vulcanization temperature until the rubber, a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1 to 12 carbon atoms and from none to a minor portion of at least one copolymerizable diene, is sufficiently small dispersed particles vulcanized to the extent that the blend has a tensile strength at least 60 Kg./sq.cm. greater than that of the unvulcanized blend, said composition being processable in an internal mixer to a product which, upon transferring, with said resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 46

A process of making a thermoplastic elastomeric filled composition comprising (a) about 25-85 parts by weight of crystalline thermoplastic polyolefin resin, (b) about 75-15 parts by weight of monoolefin copolymer rubber per 100 parts total of resin and rubber, and extender oil up to 300 parts by weight per 100 parts by weight of rubber provided that, when the amount of resin is greater than 75 parts by weight, extender oil must be present in an amount sufficient to satisfy the equation (W o + W R )/W P is equal to or greater than 0.33 wherein W o is the weight of extender oil, W R is the weight of rubber and W P is the weight of resin, and (c) about 5-300 parts by weight filler per 100 parts total weight of resin and rubber in the final composition which comprises blending (a) with a preformed mixture of (b) and (c) and vulcanizing ingredients, at a temperature sufficient to melt said resin, then masticating the blend continuously at vulcanization temperature until the rubber, a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1 to 12 carbon atoms and from none to a minor portion of at least one copolymerizable diene, is sufficiently small dispersed particles vulcanized to the extent that the blend has a tensile strength at least 60 Kg./sq.cm. greater than that of the unvulcanized blend, said composition being processable in an internal mixer to a product which, upon transferring, with said resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 47

The process of claim 41 in which 30-250 parts by weight extender oil per 100 parts by weight rubber is employed.

Claim 48

The process of claim 41 which comprises blending (a) about 35-75 parts by weight of resin, (b) about 65-25 parts by weight of rubber, and (c) about 40-250 parts by weight of carbon black per 100 parts by weight of rubber.

Claim 49

The process of claim 43 in which the resin is polypropylene and the rubber is a copolymer of monomers comprising ethylene, propylene and and a lesser quantity of a non-conjugated diene.

Claim 50

The process of claim 44 in which extender oil is employed in an amount of about 30 to about 250 parts by weight per 100 parts by weight rubber.

Claim 51

A process of making a thermoplastic elastomeric composition which comprises preparing an unvulcanized but vulcanizable composition by blending (a) about 25 to about 85 parts by weight of crystalline thermoplastic polyolefin resin, (b) about 75 to about 15 parts by weight of monoolefin copolymer rubber per 100 parts total weight of resin and rubber, which rubber is a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1-12 carbon atoms and from none to a minor amount of at least one copolymerizable diene, (c) one or more vulcanizing ingredients, in an amount sufficient to vulcanize the rubber to the extent that no more three three percent of the rubber is extractable in cyclohexane at 23° C. or that the cross-link density determined on the same monoolefin copolymer rubber as in the composition is greater than about 7 × 10 -5 moles per ml of rubber, and (d) extender oil up to 300 parts by weight per 100 parts by weight of rubber provided that, when the amount of resin is greater than 75 parts by weight, extender oil must be present in an amount sufficient to satisfy the equation (W o + W R )/W P is equal to or greater than 0.33 wherein W o is the weight of extender oil, W R is the weight of rubber and W P is the weight of resin, at a temperature sufficient to soften said resin then masticating the blend continuously at vulcanization temperature until the rubber is small dispersed particles of such size and vulcanized to the extent that the blend has a tensile strength at least 60 Kg./sq.cm. greater than that of the unvulcanized blend, giving a composition processable in an internal mixer to a product which, upon transferring, with the resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 52

A process of making a thermoplastic elastomeric composition which comprises preparing an unvulcanized but vulcanizable composition by blending (a) about 25 to about 85 parts by weight of crystalline thermoplastic polyolefin resin, (b) about 75 to about 15 parts by weight of monoolefin copolymer rubber per 100 parts total weight of resin and rubber, which rubber is a polymer of monomers comprising ethylene or propylene, and at least one other alpha olefin of the formula CH 2 ═ CHR in which R is alkyl of 1-12 carbon atoms and from none to a minor amount of at least one copolymerizable diene, (c) one or more vulcanizing ingredients, in an amount sufficient to vulcanize the rubber to the extent that no more three three percent of the rubber is extractable in cyclohexane at 23° C. or that the cross-link density determined on the same monoolefin copolymer rubber as in the composition is greater than about 7 × 10 -5 moles per ml of rubber, and (d) extender oil up to 300 parts by weight per 100 parts by weight of rubber provided that, when the amount of resin is greater than 75 parts by weight, extender oil must be present in an amount sufficient to satisfy the equation (W o + W R )/W P is equal to or greater than 0.33 wherein W o is the weight of extender oil, W R is the weight of rubber and W P is the weight of resin, at a temperature sufficient to soften said resin then masticating the blend continuously at vulcanization temperature until the rubber is small dispersed particles of such size and vulcanized to the extent that the blend has a tensile strength at least 60 Kg./sq.cm. greater than that of the unvulcanized blend, giving a composition processable in an internal mixer to a product which, upon transferring, with the resin in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous sheet.

Claim 53

The process of claim 46 in which the resin is polypropylene and the rubber is EPDM rubber which is a product from the polymerization of ethylene, propylene and a lesser quantity of a non-conjugated diene in the proportions of about 30 to about 70 parts by weight polypropylene and about 30 to 70 parts by weight of said rubber per 100 parts total weight of polypropylene and rubber.

Claim 54

A thermoplastic elastomeric composition comprising a blend of about 30 to about 70 parts by weight of crystalline polypropylene, about 70 to about 30 parts by weight of vulcanized monoolefin rubber, per 100 parts total weight of said polypropylene and rubber and from about 30 to about 250 parts by weight of extender oil per 100 parts by weight of said rubber, wherein the rubber in said blend is a polymer of ethylene, propylene and a minor proportion of at least one copolymerizable non-conjugated diene and is present in said blend in the form of small dispersed particles essentially of a size of about 50 microns or below and is vulcanized to the extent that the blend has a tensile strength at least about 60 Kg./sq.cm. greater than that of the unvulcanized blend and no more than 3% by weight of the rubber is extractable in cyclohexane at 23° C., the composition being processable in an internal mixer to a product which, upon transferring with the polypropylene in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous elastomeric sheet.

Claim 55

A thermoplastic elastomeric composition comprising a blend of about 30 to about 70 parts by weight of crystalline polypropylene, about 70 to about 30 parts by weight of vulcanized monoolefin rubber, per 100 parts total weight of said polypropylene and rubber and from about 30 to about 250 parts by weight of extender oil per 100 parts by weight of said rubber, wherein the rubber in said blend is a polymer of ethylene, propylene and a minor proportion of at least one copolymerizable non-conjugated diene and is present in said blend in the form of small dispersed particles essentially of a size of about 50 microns or below and is vulcanized to the extent that the blend has a tensile strength at least about 60 Kg./sq.cm. greater than that of the unvulcanized blend and no more than 3% by weight of the rubber is extractable in cyclohexane at 23° C., the composition being processable in an internal mixer to a product which, upon transferring with the polypropylene in the molten state, to the rotating rolls of a rubber mill forms an essentially continuous elastomeric sheet.

Claim 56

The composition of claim 48 containing a filler dispersed therein.

Claim 57

The composition of claim 48 in which the diene is ethylidene norbornene.

Claim 58

The composition of claim 48 containing dispersed therein from about 2 to 250 parts by weight of carbon black per 100 parts by weight of rubber.

Claim 59

The composition of claim 50 in which the extender oil is a paraffinic extender oil.