Process for the production of thermoformable polyisocyanurate foams
Assignee: Bayer AG
•
Filing: 1977-02-04
•
Granted: 1978-12-12
•
Expires: 1997-02-04
Abstract
Abstract The invention relates to thermoformable polyisocyanurate foams which are produced by reacting a polymethylene polyphenyl polyisocyanate having a specified diisocyanate content with polyethers which have an OH number between 28 and 112 and dihydric alcohols which have a molecular weight between 62 and 200 in the presence of isocyanate trimerization catalysts, blowing agents and other foaming agents.
Inventors
- 👤 Dietmar Schapel
- 👤 Ulrich VON Gizycki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:17
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/80; C08G18/8003; C08G18/8006; C08G18/8009; C08G18/8012; C08G18/8019; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G18/74; C08G18/76; C08G18/7657; C08G18/7664; C08G18/77; C08G18/78; C08G18/79; C08G18/797; C08G2110/00; C08G2110/0025; C08G2110/0041; C08G2110/005; C08G2110/0058; C08G2115/00; C08G2115/02; Y; Y10; Y10S; Y10S521/00; Y10S521/902; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31547
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
145 words
In a process for the production of thermoformable polyisocyanurate foams by reaction of compounds which have hydroxyl groups with an excess of polyisocyanates in the presence of isocyanate trimerization catalysts, and blowing agents, the improvement which comprises reacting a polymethylene polyphenyl polyisocyanate which contains at least 80% by weight of diisocyanatodiphenylmethane and a mixture of (a) polyethers containing at least one hydroxyl group and having an OH number of from 28 to 112, in which at least 20% by weight of the alkylene oxide component consists of ethylene oxide groups, and (b) dihydric alcohols which have a molecular weight of from 62 to 200, said polyethers being used in a quantity corresponding to from 0.015 to 0.04 equivalents of OH per equivalent NCO and the dihydric alcohols being used in a quantity corresponding to from 0.2 to 0.4 equivalents of OH per equivalent of NCO.
Claim 2
Dependent Claim
145 words
In a process for the production of thermoformable polyisocyanurate foams by reaction of compounds which have hydroxyl groups with an excess of polyisocyanates in the presence of isocyanate trimerization catalysts, and blowing agents, the improvement which comprises reacting a polymethylene polyphenyl polyisocyanate which contains at least 80% by weight of diisocyanatodiphenylmethane and a mixture of (a) polyethers containing at least one hydroxyl group and having an OH number of from 28 to 112, in which at least 20% by weight of the alkylene oxide component consists of ethylene oxide groups, and (b) dihydric alcohols which have a molecular weight of from 62 to 200, said polyethers being used in a quantity corresponding to from 0.015 to 0.04 equivalents of OH per equivalent NCO and the dihydric alcohols being used in a quantity corresponding to from 0.2 to 0.4 equivalents of OH per equivalent of NCO.
Claim 3
Dependent Claim
21 words
The process of claim 1, characterized in that the polymethylene polyphenyl polyisocyanate contains from 5 to 60% by weight, of 2,4'-diisocyanatodiphenylmethane.
Claim 4
Dependent Claim
24 words
The process of claim 1, characterized in that at least 10%, by weight, of the hydroxyl groups in said polyether are primary hydroxyl groups.
Claim 5
Dependent Claim
18 words
The process of claim 1 wherein 30 to 50% of the alkylene oxide component consists of ethylene oxide.
Claim 6
Dependent Claim
11 words
Thermoformable polyisocyanurate foams obtainable by the process according to claim 1.
References Cited (Backward Citations)
US3745133A
Cited
US3644232A
Cited
US3676380A
Cited
US3865762A
Cited
US3857800A
Cited
US3836424A
Cited
US4009130A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-11 | 1982-06-12 | 1982-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-11 | 1986-06-12 | 1986-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-11 | 1990-06-12 | 1990-12-12 | $7700.00 | Window Closed / Lapsed |