Radiation shielding material and a process for producing the same

Claim 2

An optically transparent radiation shielding material of a composition containing a polymer comprising (A) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in an alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene and (B) lead acrylate or lead methacrylate, and a lead carboxylate represented by the general formula: (RCOO) a Pb, a being an integer equal to the valency of lead and R representing a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to the total constituent monomer in the polymer and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of said total monomer in said composition satisfy anyone of the following three formulas I, II and III: 200≧y≧2, where 9≦x≦30 (I) 200≧y≧2/5 (x - 30) + 2, where 30≦x≦75 (II) and 200≧y≧-(9/10) (x - 75) + 20, where 75≦x≦95 (III).

Claim 3

A radiation shielding material as defined in claim 1, wherein a is an integer between 2-4 inclusive and R is a saturated or unsaturated aliphatic hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 4

A radiation shielding material as defined in claim 2, wherein a is an integer between 2-4 inclusive and R is a saturated or unsaturated, non-substituted aliphatic hydrocarbon residue having 5-20 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 5

A radiation shielding material as defined in claim 2, wherein a is an integer between 2-4 inclusive and R is a saturated or unsaturated aliphatic hydrocarbon residue substituted with a hydroxyl group and having 5-20 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 6

A radiation shielding material as defined in claim 3, wherein a is 2 and R is a saturated or unsaturated aliphatic hydrocarbon residue having 5-18 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 7

A radiation shielding material as defined in claim 4, wherein a is 2 and R is a saturated or unsaturated aliphatic hydrocarbon residue having 5-18 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 8

A radiation shielding material as defined in claim 5, wherein the lead carboxylate is selected from the group consisting of lead hexanoate, octanoate, decanoate, laurate, myristate, palmitate, stearate, myristoleate, palmitoleate, oleate, linoleate, linolenate and naphthenate.

Claim 9

A radiation shielding material as defined in claim 6, wherein the lead carboxylate is lead ricinoleate.

Claim 10

A radiation shielding material as defined in claim 1, wherein the hydroxyalkyl acrylate or hydroxyalkyl methacrylate contains an alkyl group having 2-4 carbon atoms.

Claim 11

A radiation shielding material as defined in claim 9, wherein the hydroxyalkyl acrylate or the hydroxyalkyl methacrylate is hydroxyethyl acrylate or hydroxyethyl methacrylate.

Claim 12

A radiation shielding material as defined in claim 1, wherein the alkyl methacrylate is methyl methacrylate.

Claim 13

A radiation shielding material as defined in claim 1, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to the total constituent monomer in the polymer and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of said total monomer contained in said composition can satisfy either of the above formulas I or II.

Claim 14

An optically transparent radiation shielding material of a composition containing a polymer comprising (A) a substrate monomer comprising (a) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in the alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene, and (b) 8-75% by weight of the substrate monomer of at least one polyfunctional monomer selected from the group consisting of a monomer represented by the general formula: ##STR3## where R 1 is H or CH 3 , A is an alkylene group having 2-4 carbon atoms and n is an integer between 2-60 inclusive and a monomer represented by the formula: ##STR4## where R 2 is H or CH 3 , B is a saturated or unsaturated hydrocarbon residue having 4-25 carbon atoms and m is an integer between 2-4 inclusive and (B) lead acrylate or lead methacrylate, and a lead carboxylate represented by the general formula: (RCOO) a Pb, a being an integer equal to the valency of lead and R represents a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to the total constituent monomer in the polymer and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of the total monomer in said composition can satisfy either of the following formula I or II: 20≧ y≧2 where 9≦x≦30 (I) and 200≧y≧2/5 (x - 30) + 2 where 30≦x≦75 (II).

Claim 15

An optically transparent radiation shielding material of a composition containing a polymer comprising (A) a substrate monomer comprising (a) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in the alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene, and (b) 8-75% by weight of the substrate monomer of at least one polyfunctional monomer selected from the group consisting of a monomer represented by the general formula: ##STR3## where R 1 is H or CH 3 , A is an alkylene group having 2-4 carbon atoms and n is an integer between 2-60 inclusive and a monomer represented by the formula: ##STR4## where R 2 is H or CH 3 , B is a saturated or unsaturated hydrocarbon residue having 4-25 carbon atoms and m is an integer between 2-4 inclusive and (B) lead acrylate or lead methacrylate, and a lead carboxylate represented by the general formula: (RCOO) a Pb, a being an integer equal to the valency of lead and R represents a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to the total constituent monomer in the polymer and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of the total monomer in said composition can satisfy either of the following formula I or II: 20≧ y≧2 where 9≦x≦30 (I) and 200≧y≧2/5 (x - 30) + 2 where 30≦x≦75 (II).

Claim 16

a radiation shielding material as defined in claim 13, wherein the polyfunctional monomer is contained in an amount of 12-60% by weight to the total substrate monomer composed of said polyfunctional monomer and the essential monomer.

Claim 17

A radiation shielding material as defined in claim 13, wherein the repetition number n in the general formula IV for the polyfunctional monomer is an integer between 3-30.

Claim 18

A radiation shielding material as defined in claim 13, wherein B in the general formula V for another polyfunctional monomer represents a saturated or unsaturated hydrocarbon residue having 4-15 carbon atoms.

Claim 19

A process for producing an optically transparent radiation shielding material which comprises polymerizing a monomer mixture of (A) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in an alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene and (B) lead acrylate or lead methacrylate in the presence of a lead carboxylate represented by the general formula: (RCOO) a Pb a being an integer equal to the valency of lead and R representing a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to said monomer mixture and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of said monomer mixture satisfy anyone of the following formulas I, II and III: 200≧y≧2, where 9≦x≦30 (I) 200≧y≧2/5 (x - 30) + 2, where 30≦x≦75 (II) and 200≧y≧-(9/10) (x - 75) + 20, where 75≦x≦95 (III).

Claim 20

A process for producing an optically transparent radiation shielding material which comprises polymerizing a monomer mixture of (A) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in an alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene and (B) lead acrylate or lead methacrylate in the presence of a lead carboxylate represented by the general formula: (RCOO) a Pb a being an integer equal to the valency of lead and R representing a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to said monomer mixture and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of said monomer mixture satisfy anyone of the following formulas I, II and III: 200≧y≧2, where 9≦x≦30 (I) 200≧y≧2/5 (x - 30) + 2, where 30≦x≦75 (II) and 200≧y≧-(9/10) (x - 75) + 20, where 75≦x≦95 (III).

Claim 21

A process as defined in claim 17, wherein a is an integer between 2-4 inclusive and R is a saturated or unsaturated aliphatic hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms in the general formula: (RCOO) a Pb for representing the carboxylate.

Claim 22

A process as defined in claim 18, wherein a is an integer between 2-4 inclusive and R is a saturated or unsaturated non-substituted aliphatic hydrocarbon residue having 5-20 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 23

A process as defined in claim 18, wherein a is an integer between 2-4 inclusive and is a saturated or unsaturated aliphatic hydrocarbon residue substituted with a hydroxyl group and having 5-20 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 24

A process as defined in claim 19, wherein a is 2 and R is a saturated or unsaturated aliphatic hydrocarbon residue having 5-18 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 25

A process as defined in claim 20, wherein a is 2 and R is a saturated or unsaturated aliphatic hydrocarbon residue having 5-18 carbon atoms in the general formula: (RCOO) a Pb for representing the lead carboxylate.

Claim 26

A process as defined in claim 21, wherein the lead carboxylate is selected from the group consisting of lead hexanoate, octanoate, decanoate, laurate, myristate, palmitate, stearate, myristoleate, palmitoleate, oleate, linoleate, linolenate and naphthenate.

Claim 27

A process as defined in claim 22, wherein the lead carboxylate is lead ricinoleate.

Claim 28

A process as defined in claim 17, wherein the hydroxyalkyl acrylate or hydroxyalkyl methacrylate contains an alkyl group having 2-4 carbon atoms.

Claim 29

A process as defined in claim 25, wherein the hydroxyalkyl acrylate or hydroxyalkyl methacrylate is hydroxyethyl acrylate or hydroxyethyl methacrylate.

Claim 30

A process as defined in claim 17, wherein the alkyl methacrylate is methyl methacrylate.

Claim 31

A process as defined in claim 17, wherein the polymerization reaction is effected at a temperature between -10° and +150° C. in the presence of an initiator for radical polymerization.

Claim 32

A process as defined in claim 28, wherein the polymerization reaction is effected at a temperature between 40° and 130° C. in the presence of an initiator for radical polymerization.

Claim 33

A process as defined in claim 17, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to the monomer mixture and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of the monomer mixture can satisfy either of the formulas I or II described above.

Claim 34

A process for producing an optically transparent radiation shielding material which comprises polymerizing a monomer mixture of (A) a substrate monomer composed of (a) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in the alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene, and (b) 8-75% by weight said substrate monomer of at least one polyfunctional monomer selected from the group consisting of a monomer represented by the formula: ##STR5## where R 1 is H or CH 3 , A is an alkylene group having 2-4 carbon atoms and n is an integer between 2-60 inclusive and a monomer represented by the formula: ##STR6## where R 2 is H or CH 3 , B is a saturated or unsaturated hydrocarbon residue having 4-25 carbon atoms and m is an integer between 2-4 inclusive and (B) lead acrylate or lead methacrylate in the presence of a lead carboxylate represented by the formula: (RCOO) a Pb, a being an integer equal to the valency of lead and R representing a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to said monomer mixture and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of said monomer mixture satisfy either of the following formulas I or II: 20≧ y≧2 where 9≦x≦30 (I) and 200≧y≧2/5 (x - 30) + 2 where 30≦x≦75 (II).

Claim 35

A process for producing an optically transparent radiation shielding material which comprises polymerizing a monomer mixture of (A) a substrate monomer composed of (a) at least one essential monomer selected from the group consisting of alkyl methacrylate having 1-4 carbon atoms in the alkyl group, hydroxyalkyl acrylate, hydroxyalkyl methacrylate and styrene, and (b) 8-75% by weight said substrate monomer of at least one polyfunctional monomer selected from the group consisting of a monomer represented by the formula: ##STR5## where R 1 is H or CH 3 , A is an alkylene group having 2-4 carbon atoms and n is an integer between 2-60 inclusive and a monomer represented by the formula: ##STR6## where R 2 is H or CH 3 , B is a saturated or unsaturated hydrocarbon residue having 4-25 carbon atoms and m is an integer between 2-4 inclusive and (B) lead acrylate or lead methacrylate in the presence of a lead carboxylate represented by the formula: (RCOO) a Pb, a being an integer equal to the valency of lead and R representing a saturated or unsaturated hydrocarbon residue non-substituted or substituted with a hydroxyl group and having 5-20 carbon atoms, wherein the ratio x (% by weight) of the lead acrylate or the lead methacrylate to said monomer mixture and the compounding ratio y (parts by weight) of the lead carboxylate to 100 parts by weight of said monomer mixture satisfy either of the following formulas I or II: 20≧ y≧2 where 9≦x≦30 (I) and 200≧y≧2/5 (x - 30) + 2 where 30≦x≦75 (II).

Claim 36

a process as defined in claim 31, wherein the polyfunctional monomer is contained in an amount between 12-60% by weight to the total substrate monomer composed of said polyfunctional monomer and the essential monomer.

Claim 37

A process as defined in claim 31, wherein the repetition number n in the general formula IV for the polyfunctional monomer is an integer between 3-30.

Claim 38

A process as defined in claim 31, wherein B in the general formula V for another polyfunctional monomer represents a saturated or unsaturated hydrocarbon residue having 4-15 carbon atoms.