Impact-resistant chemically blended propylene polymer composition and process for preparation thereof
Assignee: Mitsui Chemicals Inc
•
Filing: 1977-01-05
•
Granted: 1978-12-05
•
Expires: 1997-01-05
Abstract
Abstract An improved process for preparing an impact-resistant chemically blended propylene polymer or copolymer, which comprises the following three steps: (1) a first step of polymerizing propylene containing 0 to 1 mole% of another olefin in the presence of a catalyst composed of (a) a carrier-supported titanium catalyst component containing at least magnesium, halogen and titanium on the surface of the carrier and (b) an organo aluminum compound to form specific crystalline polypropylene; (2) a second step of copolymerizing propylene and ethylene in the presence of the reaction product of the first step and the same catalyst while maintaining the content of propylene in the gaseous phase of the polymerization zone at 65 to 90 mole% thereby to form specific low-crystalline propylene/ethylene copolymer; and (3) a third step of polymerizing ethlene, or both ethylene and propylene in the presence of the reaction product of the second step and the same catalyst while maintaining the content of propylene in the gaseous phase of the polymerization zone at 0 to 15 mole% thereby to form specific polyethylene or ethylene/propylene copolymer.
Inventors
- 👤 Kunio Furutachi
- 👤 Akifumi Kato
- 👤 Mikio Nakagawa
- 👤 Masaru Nakano
- 👤 Shunji Arita
- 👤 Aikich Yamamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:58
CPC Classifications
C; C08; C08F; C08F297/00; C08F297/06; C08F297/08; C08F297/083; C08F297/086
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
258 words
A process for preparing an impact-resistant chemically blended propylene polymer composition having an ethylene content of 3 to 40 mole%, which consists essentially of the following three steps: (1) a first step of polymerizing propylene containing 0 to 1 mole% of another olefin in the presence of a catalyst composed of (a) a carrier-supported titanium catalyst component containing at least magnesium, halogen and titanium on the surface of the carrier and (b) an organoaluminum compound to form crystalline polypropylene having an isotactic index of at least 90 which accounts for 55 to 95% by weight of the final polymer composition; (2) a second step of copolymerizing propylene and ethylene in the presence of the reaction product of the first step and the same catalyst while maintaining the content of propylene in the gaseous phase of the polymerization zone at 65 to 90 mole% therby to form a low-crystalline propylene/ethylene copolymer having a propylene content of 60 to 85 mole% which accounts for 1 to 10% by weight of the final polymer composition; and (3) a third step of polymerizing ethylene, or both ethylene and propylene in the presence of the reaction product of the second step and the same catalyst while maintaining the content of propylene in the gaseous phase of the polymerization zone at 0 to 15 mole% thereby to form polyethylene or an ethylene/propylene copolymer having a propylene content of up to 10 mole% which has an intrinsic viscosity of at least 2.6 and accounts for 1 to 35% by weight of the final polymer composition.
Claim 2
Dependent Claim
258 words
A process for preparing an impact-resistant chemically blended propylene polymer composition having an ethylene content of 3 to 40 mole%, which consists essentially of the following three steps: (1) a first step of polymerizing propylene containing 0 to 1 mole% of another olefin in the presence of a catalyst composed of (a) a carrier-supported titanium catalyst component containing at least magnesium, halogen and titanium on the surface of the carrier and (b) an organoaluminum compound to form crystalline polypropylene having an isotactic index of at least 90 which accounts for 55 to 95% by weight of the final polymer composition; (2) a second step of copolymerizing propylene and ethylene in the presence of the reaction product of the first step and the same catalyst while maintaining the content of propylene in the gaseous phase of the polymerization zone at 65 to 90 mole% therby to form a low-crystalline propylene/ethylene copolymer having a propylene content of 60 to 85 mole% which accounts for 1 to 10% by weight of the final polymer composition; and (3) a third step of polymerizing ethylene, or both ethylene and propylene in the presence of the reaction product of the second step and the same catalyst while maintaining the content of propylene in the gaseous phase of the polymerization zone at 0 to 15 mole% thereby to form polyethylene or an ethylene/propylene copolymer having a propylene content of up to 10 mole% which has an intrinsic viscosity of at least 2.6 and accounts for 1 to 35% by weight of the final polymer composition.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein the carrier-supported titanium catalyst component has been treated with an organic carboxylic acid ester.
Claim 4
Dependent Claim
40 words
The process of claim 1 wherein the reactions for forming the polymer composition are carried out in the presence of an inert hydrocarbon solvent at room temperature to about 100° C. under atmospheric pressure to about 30 kg/cm 2 .
Claim 5
Dependent Claim
39 words
The process of claim 3 wherein the catalyst is composed of about 0.01 to about 10 millimoles/liter of solvent of the carrier-supported catalyst component (a) and about 0.01 to about 30 millimoles/liter of solvent of the organoaluminum compound (b).
Claim 6
Dependent Claim
26 words
The process of claim 1 wherein the reactions for forming the polymer composition are carried out in the further presence of an organic carboxylic acid ester.
Claim 7
Dependent Claim
106 words
An impact-resistant chemically blended propylene polymer composition having an ethylene content of 3 to 40 mole%, and consisting essentially of (A) 55 to 95% by weight of crystalline polypropylene containing 0 to 1 mole% of another olefin and having an isotactic index of at least 90, (B) 1 to 10% by weight of a low-crystalline propylene/ethylene copolymer containing 60 to 85 mole% of propylene, and (C) 1 to 35 mole% by weight of polyethylene or an ethylene/propylene copolymer containing up to 10 mole% of propylene which has an intrinsic viscosity of at least 2.6, the total proportion of (A), (B) and (C) being 100% by weight.
Claim 8
Dependent Claim
106 words
An impact-resistant chemically blended propylene polymer composition having an ethylene content of 3 to 40 mole%, and consisting essentially of (A) 55 to 95% by weight of crystalline polypropylene containing 0 to 1 mole% of another olefin and having an isotactic index of at least 90, (B) 1 to 10% by weight of a low-crystalline propylene/ethylene copolymer containing 60 to 85 mole% of propylene, and (C) 1 to 35 mole% by weight of polyethylene or an ethylene/propylene copolymer containing up to 10 mole% of propylene which has an intrinsic viscosity of at least 2.6, the total proportion of (A), (B) and (C) being 100% by weight.
Claim 9
Dependent Claim
101 words
The impact-resistant chemically blended propylene polymer composition according to claim 6 consisting essentially of (A) 60 to 90% by weight of crystalline polypropylene containing 0 to 1 mole percent of another olefin and having an isotactic index of at least 90, (B) 2 to 8% by wieght of a low-crystalline propylene/ethylene copolymer containing 60 to 85 mole% of propylene, and (C) 3 to 30 mole% by weight of polyethylene or an ethylene/propylene copolymer containing up to 10 mole% of propylene which has an intrinsic viscosity of at least 3, the total proportion of (A), (B) and (C) being 100% by weight.
Claim 10
Dependent Claim
149 words
The process for preparing an impact-resistant chemically blended propylene copolymer composition according to claim 1 wherein (1) the crystalline polypropylene of the first step accounts for 60 to 90% by weight of the final polymer composition; (2) the content of propylene in the gaseous phase of the polymerization zone of the second step is maintained at 70 to 85 mole% and the low-crystalline propylene/ethylene copolymer has a propylene content of 65 to 80 mole% which accounts for 2 to 8% by weight of the final polymer composition; and (3) the content of propylene in the gaseous phase of the polymerization zone of the third step is maintained at 0 to 8 mole% and the polyethylene or ethylene/propylene copolymer has a propylene content of up to 8 mole% and has an intrinsic viscosity of at least 3, and accounts for 3 to 30% by weight of the final polymer composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-04 | 1982-06-05 | 1982-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-04 | 1986-06-05 | 1986-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-04 | 1990-06-05 | 1990-12-05 | $7700.00 | Window Closed / Lapsed |