Aqueous vinylidene fluoride polymer coating composition
Assignee: Arkema Inc
•
Filing: 1977-01-21
•
Granted: 1978-12-05
•
Expires: 1997-01-21
Abstract
Abstract A water-based coating composition which may be air dried to form durable, fire resistant coatings includes dispersed vinylidene fluoride polymer particles, emulsified liquid epoxy resin and a dissolved emulsifying agent for said epoxy resin which agent is also capable of rapidly curing the epoxy resin upon removal of the water from the composition.
Inventors
- 👤 Edward J. Bartoszek
- 👤 Alkis Christofas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:54
CPC Classifications
C; C09; C09D; C09D163/00; C09D127/00; C09D127/02; C09D127/12; C09D127/16; C08; C08L; C08L63/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
147 words
An aqueous coating composition comprising, for each 100 parts by weight of aqueous liquid medium, from about 25 to about 125 parts of dispersed polymer particles of vinylidene fluoride homopolymer or copolymer of at least 50 mol percent vinylidene fluoride copolymerized with at least one other copolymerizable monomer and from about 3 to about 50 parts of emulsified liquid epoxy resin, and, for each part by weight of liquid epoxy resin, from about 0.25 to about 2.5 parts of an emulsifying agent comprising an acidified aminoalkylated polymer having pendant aminoalkylate groups of the formula ##STR2## wherein R 1 and R 2 are independantly selected from the group consisting of hydrogen and lower alkyl radicals having 1 to 4 carbon atoms and the average value of n ranges from about 1.0 to 2.5, and wherein said aminoalkylated polymer before aminoalkylation contains at least 3% by weight pendant-COOH groups.
Claim 2
Dependent Claim
147 words
An aqueous coating composition comprising, for each 100 parts by weight of aqueous liquid medium, from about 25 to about 125 parts of dispersed polymer particles of vinylidene fluoride homopolymer or copolymer of at least 50 mol percent vinylidene fluoride copolymerized with at least one other copolymerizable monomer and from about 3 to about 50 parts of emulsified liquid epoxy resin, and, for each part by weight of liquid epoxy resin, from about 0.25 to about 2.5 parts of an emulsifying agent comprising an acidified aminoalkylated polymer having pendant aminoalkylate groups of the formula ##STR2## wherein R 1 and R 2 are independantly selected from the group consisting of hydrogen and lower alkyl radicals having 1 to 4 carbon atoms and the average value of n ranges from about 1.0 to 2.5, and wherein said aminoalkylated polymer before aminoalkylation contains at least 3% by weight pendant-COOH groups.
Claim 3
Dependent Claim
32 words
The composition of claim 1 wherein the vinylidene fluoride polymer is a copolymer of about 62 weight percent vinylidene fluoride, about 24 weight percent tetrafluoroethylene and about 14 weight percent of hexafluoropropene.
Claim 4
Dependent Claim
58 words
The composition of claim 1 wherein the liquid epoxy resin consists of a mixture of from about 10 to about 12 parts by weight of a liquid epoxy resin of the diglycidyl ether of bisphenol A and from about 1 to about 3 parts by weight of a liquid epoxy resin of the diglycidyl ether of propylene glycol.
Claim 5
Dependent Claim
30 words
The composition of claim 1 which contains from about 10 to about 170 parts by weight of dispersed, finely-divided pigment for each 100 parts by weight of vinylidene fluoride polymer.
Claim 6
Dependent Claim
58 words
The composition of claim 2 wherein the liquid epoxy resin consists of a mixture of from about 10 to about 12 parts by weight of a liquid epoxy resin of the diglycidyl ether of bisphenol A and from about 1 to about 3 parts by weight of a liquid epoxy resin of the diglycidyl ether of propylene glycol.
Claim 7
Dependent Claim
30 words
The composition of claim 5 which contains from about 10 to about 170 parts by weight of dispersed, finely-divided pigment for each 100 parts by weight of vinylidene fluoride polymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-04 | 1982-06-05 | 1982-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-04 | 1986-06-05 | 1986-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-04 | 1990-06-05 | 1990-12-05 | $7700.00 | Window Closed / Lapsed |