Process for making fiber-forming polyesters

Claim 2

A flame retardant and easily dyeable fiber-forming polyester polymer containing (A) 82-98 weight percent ethylene terephthalate; (B) 8 to 1 weight percent of a dyeability improver selected from the group consisting of R--O(G--O).sub.x --H where R is an alkyl group containing from about 8 to about 20 carbon atoms; G is a hydrocarbon radical selected from the group consisting of ethylene, propylene, butylene and isomers thereof, and mixtures of the above, and x has a value of about 8-20, and ##STR8## where R is O, (CH 3 ) 2 or H 2 and the sum of x and y is 4-30, and; (C) 10 to 1 weight percent of a phosphine oxide selected from the group consisting of bis(carboxyethyl) methyl phosphine oxide and bis(3-hydroxypropyl) phenyl phosphine oxide.

Claim 3

The polymer of claim 1 wherein the dyeability improver is selected from the group consisting of C 14-15 H 29-31 O(CH 2 CH 2 O) 14 H and ##STR9##

Claim 4

The polymer of claim 2 wherein the amount of dyeability improver is 1-3 weight percent, based on polymer weight.

Claim 5

The polymer of claim 2 wherein the dyeability improver is C 14-15 H 29-31 O(CH 2 CH 2 O) 14 H and the phosphine oxide is bis(carboxyethyl) methyl phosphine oxide.

Claim 6

The polymer of claim 4 wherein the dyeability improver is ##STR10##

Claim 7

The process for making a flame-retardant, easily-dyeable polyester polymer, comprising polycondensing a glycol phthalate prepolymer with a dyeability improver selected from the group consisting of R--O(G--O).sub.x --H where R is an alkyl group containing an average of from about 8 to 20 carbon atoms; G is a hydrocarbon radical selected from the group consisting of ethylene propylene, butylene and isomers thereof, and mixtures of the above, and x has an average value of about 8-20, and ##STR11## where R is O, (CH 3 ) 2 or H 2 and the sum of x and y is 4-30, and a phosphine oxide selected from the group consisting of bis(carboxyethyl) methyl phosphine oxide, bis(hydroxypropyl) phenyl phosphine oxide, bis(carboxyethyl) phenyl phosphine oxide, bis(4-carboxyphenyl) methyl phosphine oxide and bis (carboxyphenyl) phenyl phosphine oxide in the presence of an effective amount of the reaction product of germanium dioxide and a tetraalkyl ammonium hydroxide selected from the group consisting of tetramethyl ammonium hydroxide and tetraethyl ammonium hydroxide.

Claim 8

The process for making a flame-retardant, easily-dyeable polyester polymer, comprising polycondensing a glycol phthalate prepolymer with a dyeability improver selected from the group consisting of R--O(G--O).sub.x --H where R is an alkyl group containing an average of from about 8 to 20 carbon atoms; G is a hydrocarbon radical selected from the group consisting of ethylene propylene, butylene and isomers thereof, and mixtures of the above, and x has an average value of about 8-20, and ##STR11## where R is O, (CH 3 ) 2 or H 2 and the sum of x and y is 4-30, and a phosphine oxide selected from the group consisting of bis(carboxyethyl) methyl phosphine oxide, bis(hydroxypropyl) phenyl phosphine oxide, bis(carboxyethyl) phenyl phosphine oxide, bis(4-carboxyphenyl) methyl phosphine oxide and bis (carboxyphenyl) phenyl phosphine oxide in the presence of an effective amount of the reaction product of germanium dioxide and a tetraalkyl ammonium hydroxide selected from the group consisting of tetramethyl ammonium hydroxide and tetraethyl ammonium hydroxide.

Claim 9

The process of claim 6 wherein the glycol phthalate is ethylene terephthalate.

Claim 10

The process of claim 7 wherein the amount of catalyst, calculated as germanium dioxide, is 0.008 to 0.04 weight percent, based on the weight of the ethylene terephthalate.

Claim 11

The process of claim 8 wherein the dyeability improver is selected from the group consisting of C 14-15 H 29-31 O(CH 2 CH 2 O) 14 H and ##STR12## and the phosphine oxide is selected from the group consisting of bis(carboxyethyl) methyl phosphine oxide and bis(hydroxypropyl) phenyl phosphine oxide.

Claim 12

The process of claim 9 wherein the phosphine oxide is bis(hydroxypropyl) phenyl phosphine oxide and the dye improver is C 14-15 H 29-31 O(CH 2 CH 2 O) 14 H.

Claim 13

The process of claim 9 wherein the phosphine oxide is bis(3-hydroxypropyl) phenyl phosphine oxide and the dyeability improver is ##STR13##

Claim 14

The process of claim 9 wherein the phosphine oxide is bis(carboxyethyl) methyl phosphine oxide and the dyeability improver is C 14-15 H 29-31 O(CH 2 CH 2 O) 14 H.

Claim 15

The process of claim 9 wherein the phosphine oxide is bis(carboxyethyl) methyl phosphine oxide and the dyeability improver is ##STR14##