US4127451A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for providing environmentally stable aluminum surfaces for adhesive bonding and product produced
Assignee: Boeing Co
•
Filing: 1977-08-15
•
Granted: 1978-11-28
•
Expires: 1997-08-15
Abstract
Abstract Environmentally stable bond joints of aluminum metal and aluminum alloys in adhesively joined structures are formed by utilizing a prebonding anodization of the aluminum surfaces in a phosphoric acid electrolyte using an electrolyte bath temperature of 60° to 85° F. The anodized surface is then removed from the electrolyte bath and washed free of electrolyte within from one half to two and one half minutes from cessation of anodizing current, dried and coated with adhesive resin. The anodized aluminum metal surfaces are then juxtaposed with an adhesive resin and bonded together under pressure and heat to cure the adhesive resin. The resulting structure is resistant to failure of the bond joints on exposure to moist atmospheric conditions. The surface preparation provides a porous hydration resistant aluminum oxide surface which minimizes adhesive failure to the oxide-adhesive interface under aqeuous exposure. Alloys containing copper and other constituents may be successfully anodized and bonded by this process.
Inventors
- 👤 J. Arthur Marceau
- 👤 Ralph H. Firminhac
- 👤 Yukimori Moji
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:13
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/06; C25D11/08; B; B32; B32B; B32B15/00; B32B15/20; C23; C23G; C23G1/00; C23G1/02; C23G1/12; C23G1/125; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
99 words
A method of preparing an adhesively bonded aluminum structure comprising: forming a porous columnar aluminum oxide coating on surfaces of aluminum alloy articles by anodizing said articles in an aqueous solution comprising phosphoric acid, the anodizing potential being from about 3 to about 25 volts, the phosphoric acid concentration being about 3 to about 20% by weight and the temperature of said solution being about 50° F. to about 85° F.; rinsing said articles to remove said solution within 0.5 to 2.5 minutes from cessation of anodizing current; bonding said aluminum articles together to form said adhesively bonded structure.
Claim 2
Independent Claim
99 words
A method of preparing an adhesively bonded aluminum structure comprising: forming a porous columnar aluminum oxide coating on surfaces of aluminum alloy articles by anodizing said articles in an aqueous solution comprising phosphoric acid, the anodizing potential being from about 3 to about 25 volts, the phosphoric acid concentration being about 3 to about 20% by weight and the temperature of said solution being about 50° F. to about 85° F.; rinsing said articles to remove said solution within 0.5 to 2.5 minutes from cessation of anodizing current; bonding said aluminum articles together to form said adhesively bonded structure.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein the thickness of said porous coating is from about 500 to about 8,000 Angstroms.
Claim 4
Dependent Claim
30 words
The method of claim 2, wherein said coating has pores leaving a diameter of from about 300 to 1,000 Angstroms and a depth of from about 400 to 7,500 Angstroms.
Claim 5
Dependent Claim
17 words
The method of claim 1, wherein said article is anodized for about 10 to about 30 minutes.
Claim 6
Dependent Claim
17 words
The method of claim 1, wherein said temperature is from about 70° F. to about 75° F.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein the potential between said article and said solution is in the range of four to twelve volts.
Claim 8
Dependent Claim
13 words
The method of claim 1, wherein said potential is 10 ± 1 volt.
Claim 9
Dependent Claim
15 words
The method of claim 1, wherein said article is anodized for 20 ± 5 minutes.
Claim 10
Dependent Claim
17 words
The method of claim 1, wherein said phosphoric acid concentration is 10 ± 2 percent by weight.
Claim 11
Dependent Claim
154 words
An adhesively bonded aluminum alloy structure formed by adhesively bonding together aluminum adherends, said adherends each having a polymer receptive aluminum oxide surface thereon having a porous columnar structure with a thickness of from about 500 to about 6000 Angstroms, having pores from about 300 to about 600 Angstroms in diameter and from about 400 to about 5000 Angstroms in depth extending into said oxide surface, said structure prepared by anodizing the surfaces of said adherends in an aqueous phosphoric acid solution containing from about 3 to about 20% by weight H 3 PO 4 at a temperature of from about 50° F. to about 85° F. for about 10 to about 30 minutes at a potential of from about 3 to about 25 volts, rinsing said adherends to remove said solution within 0.5 to 2.5 minutes from cessation of anodizing current, applying a polymeric adhesive to said surface and bonding said adherends together.
Claim 12
Dependent Claim
154 words
An adhesively bonded aluminum alloy structure formed by adhesively bonding together aluminum adherends, said adherends each having a polymer receptive aluminum oxide surface thereon having a porous columnar structure with a thickness of from about 500 to about 6000 Angstroms, having pores from about 300 to about 600 Angstroms in diameter and from about 400 to about 5000 Angstroms in depth extending into said oxide surface, said structure prepared by anodizing the surfaces of said adherends in an aqueous phosphoric acid solution containing from about 3 to about 20% by weight H 3 PO 4 at a temperature of from about 50° F. to about 85° F. for about 10 to about 30 minutes at a potential of from about 3 to about 25 volts, rinsing said adherends to remove said solution within 0.5 to 2.5 minutes from cessation of anodizing current, applying a polymeric adhesive to said surface and bonding said adherends together.
Claim 13
Dependent Claim
16 words
The article of claim 10, wherein said temperature is about 65° F. to about 75° F.
Claim 14
Dependent Claim
14 words
The article of claim 10, wherein said temperature is 70° F. to 75° F.
Claim 15
Dependent Claim
15 words
The article of claim 10, wherein said article is anodized for 10 to 30 minutes.
Claim 16
Dependent Claim
47 words
The article of claim 10, wherein said temperature is 70° F. to 75° F., said potential is 10-15 volts, and said phosphoric acid concentration is 10 to 12 percent by weight and the part to solution potential is maintained in the range of 4 to 12 volts.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-27 | 1982-05-29 | 1982-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-27 | 1986-05-29 | 1986-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-27 | 1990-05-29 | 1990-11-28 | $7700.00 | Window Closed / Lapsed |