Method of manufacturing silicon nitride products
Assignee: Individual
•
Filing: 1976-03-17
•
Granted: 1978-11-21
•
Expires: 1996-03-17
Abstract
Abstract In manufacturing a silicon nitride product of complex shape and uniform density, a mixture of silicon nitride in powder form together with a fluxing agent and a temporary binder is first produced. From the mixture a preform of substantially uniform density less than the density of the required product is then formed, the dimensions of the preform in the direction of subsequent hot pressing to the dimensions of the final product in the same direction being arranged to be in the ratio of the preform density to the required final density. The preform is then heated to remove the temporary binder and is hot pressed in a die carrying punches which together form a cavity defining the shape of the required product, the preform shape not conforming to the die cavity.
Inventors
- 👤 Dexter W. Smith
- 👤 William J. Arrol
- 👤 Adrian C. Brennan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 23:26
CPC Classifications
F; F01; F01D; F01D5/00; F01D5/12; F01D5/28; F01D5/284; C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; Y; Y10; Y10S; Y10S264/00; Y10S264/64; Y10S264/66; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/49336
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
162 words
A method of manufacturing a silicon nitride product of complex shape and substantially uniform density including the steps of: (a) forming a mixture of silicon nitride in powder form with a fluxing agent and a temporary binder; (b) forming from said mixture a preform of substantially uniform density less than the final density of the product; (c) heating the preform to remove the temporary binder; (d) positioning the preform in a die cavity defined between punches which together define the shape of the product, the shape of the preform being non-commensurate with the shape of the die cavity but being of dimensions such that the product will be of substantially uniform density; (e) hot pressing the preform between the punches so that different areas of the preform are compressed by different amounts until the preform comforms to the shape of the punches; and (f) continuing said hot pressing of the preform between said punches until a substantially uniform density product is obtained.
Claim 2
Independent Claim
162 words
A method of manufacturing a silicon nitride product of complex shape and substantially uniform density including the steps of: (a) forming a mixture of silicon nitride in powder form with a fluxing agent and a temporary binder; (b) forming from said mixture a preform of substantially uniform density less than the final density of the product; (c) heating the preform to remove the temporary binder; (d) positioning the preform in a die cavity defined between punches which together define the shape of the product, the shape of the preform being non-commensurate with the shape of the die cavity but being of dimensions such that the product will be of substantially uniform density; (e) hot pressing the preform between the punches so that different areas of the preform are compressed by different amounts until the preform comforms to the shape of the punches; and (f) continuing said hot pressing of the preform between said punches until a substantially uniform density product is obtained.
Claim 3
Dependent Claim
50 words
The method as claimed in claim 1, wherein the dimensions of the preform in a direction parallel to the direction of hot-pressing are greater than the dimensions of the product by an amount equal to the ratio of the final density of the product to the density of the preform.
Claim 4
Dependent Claim
27 words
The method as claimed in claim 1 including the further step of mixing the silicon nitride and the fluxing agent with the temporary binder in a liquid.
Claim 5
Dependent Claim
16 words
The method as claimed in claim 3 wherein the temporary binder is dissolved in said liquid.
Claim 6
Dependent Claim
16 words
A method as claimed in claim 3 wherein the temporary binder is dispersed in said liquid.
Claim 7
Dependent Claim
33 words
The method as claimed in claim 3 wherein the mixture is of extrudable consistency and including the further step of extruding said mixture into a suitably shaped die cavity to form said preform.
Claim 8
Dependent Claim
55 words
The method as claimed in claim 1 wherein the mixture of silicon nitride, fluxing agent and temporary binder is formed by: (i) mixing silicon nitride in powder form with a temporary binder dispersed in a liquid, (ii) heating to drive off the liquid, and (iii) adding a fluxing agent either before or after step (ii).
References Cited (Backward Citations)
US2386604A
Cited
US2747231A
Cited
US2938807A
Cited
US3468992A
Cited
US3835211A
Cited
US3819786A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |