Manufacture of plates by powder-metallurgy
Assignee: Airco Inc
•
Filing: 1977-03-30
•
Granted: 1978-11-21
•
Expires: 1997-03-30
Abstract
Abstract A powder-metallurgy process, product, and assembly particularly adapted for manufacturing plates of hard-to-work materials, such as chromium and its alloys, are disclosed. The assembly is formed by placing a metal powder into the cavity of a die and disposing one punch or two opposed punches to intrude into the cavity and enclose the powder. Preferably, the powder is compacted by applying pressure to the punches, and the punches are fixed to the die with their outer ends protruding from the die. The enclosed powder may be purified, outgassed, and sealed under vacuum. The enclosed powder is consolidated and elongated by heating and compressing, preferably by rolling one or more times in a conventional rolling mill. The composite product is cooled slowly and cut to the desired size. Remnants of the die and punch may serve as frame and backing for the consolidated powder layer. The plates have application, for example, as sputtering targets.
Inventors
- 👤 Harbhajan S. Nayar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:08
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/3407; C23C14/3414; B; B22; B22F; B22F3/00; B22F3/12; B22F3/1208; B22F3/18
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
104 words
A method of manufacturing a plate from a metal powder which comprises the steps of: placing a layer of the powder inside a die having a cavity which has an opening at an end of the die; disposing a punch into the opening so as to partially intrude and partially protrude from the end of the die, and to enclose the powder in an assembly comprising the punch and die; heating the assembly to a temperature sufficient to allow consolidation of the powder; and compressing the heated assembly by rolling to apply pressure to the punch to consolidate and elongate the layer of powder.
Claim 2
Independent Claim
104 words
A method of manufacturing a plate from a metal powder which comprises the steps of: placing a layer of the powder inside a die having a cavity which has an opening at an end of the die; disposing a punch into the opening so as to partially intrude and partially protrude from the end of the die, and to enclose the powder in an assembly comprising the punch and die; heating the assembly to a temperature sufficient to allow consolidation of the powder; and compressing the heated assembly by rolling to apply pressure to the punch to consolidate and elongate the layer of powder.
Claim 3
Dependent Claim
35 words
The method in accordance with claim 1 further comprising the steps of: applying pressure to the punch to compact the enclosed powder; and then fixing the punch to the die to prevent disassembly during rolling.
Claim 4
Dependent Claim
32 words
The method in accordance with claim 2 further comprising the steps of: evacuating the assembly to outgas the compacted powder; and sealing the evacuated assembly prior to the heating and compressing steps.
Claim 5
Dependent Claim
36 words
The method in accordance with claim 3 further comprising the step of flowing a chemically reducing gas through the assembly prior to the evacuating step to decrease the amounts of non-metallic impurities in the enclosed powder.
Claim 6
Dependent Claim
40 words
The method in accordance with claim 1 wherein the metal of the powder is selected from the group consisting of titanium, zirconium, niobium, tantalum, chromium, molybdenum, tungsten, rhenium, iron, osmium, cobalt, rhodium, iridium, nickel, palladium, and platinum, and their alloys.
Claim 7
Dependent Claim
34 words
The method in accordance with claim 1 wherein the powder consists essentially of a hard-to-work material characterized by a hot-tensile-reduction-in-area-at-fracture of less than 50% at temperatures within the working range of the compressing step.
Claim 8
Dependent Claim
37 words
The method in accordance with claim 1 wherein the punch and die are formed from metals which have hot-tensile-reduction-in-area-at-fracture at least 10% greater than the powder material, at temperatures within the working range of the compressing step.
Claim 9
Dependent Claim
42 words
The method in accordance with claim 1 wherein the flow-strength of the punch and die materials are not less than one-third nor greater than three times the flow-strength of the powder material at temperatures within the working range of the compressing step.
Claim 10
Dependent Claim
28 words
The method in accordance with claim 1 wherein the density of the consolidated powder is increased to at least 90% of the theoretical maximum by a first rolling.
Claim 11
Dependent Claim
20 words
The method in accordance with claim 1 wherein the consolidated powder has an area greater than 100 in 2 .
Claim 12
Independent Claim
164 words
A method of manufacturing a plate from a metal powder which comprises the steps of: placing a layer of the powder inside a metal die having a cavity which has a first opening in a first end of the die and a second opening in a second end opposite to the first end of the die; disposing a first metal punch into the first opening so as to partially intrude and partially protrude from the first end of the die; disposing a second metal punch into the second opening so as to partially intrude and partially protrude from the second end of the die, and to enclose the powder in an assembly comprising the first punch, second punch, and die; heating the assembly to a temperature sufficient to allow consolidation of the powder; and compressing the powder by passing the heated assembly between two rolls which apply pressure to the first punch and the second punch to consolidate and elongate the layer of powder.
Claim 13
Independent Claim
164 words
A method of manufacturing a plate from a metal powder which comprises the steps of: placing a layer of the powder inside a metal die having a cavity which has a first opening in a first end of the die and a second opening in a second end opposite to the first end of the die; disposing a first metal punch into the first opening so as to partially intrude and partially protrude from the first end of the die; disposing a second metal punch into the second opening so as to partially intrude and partially protrude from the second end of the die, and to enclose the powder in an assembly comprising the first punch, second punch, and die; heating the assembly to a temperature sufficient to allow consolidation of the powder; and compressing the powder by passing the heated assembly between two rolls which apply pressure to the first punch and the second punch to consolidate and elongate the layer of powder.
Claim 14
Dependent Claim
79 words
The method in accordance with claim 11 wherein the protrusion ratio P/(1-ρ c )T M lies in the range 1 to 2, where P is the total distance which the two punches protrude from the die, T M is the thickness of the powder, ρ c is the density of the powder expressed as a fraction of the theoretical maximum density, and the quantities P, T M , and ρ c are evaluated just prior to the compressing step.
Claim 15
Dependent Claim
59 words
The method in accordance with claim 12 wherein for each punch just prior to the compressing step, the intrusion ratio d i /d p is within the range 0.5 to 2, where d i is the distance which said punch intrudes into the cavity and d p is the distance said punch protrudes from the end of the die.
Claim 16
Dependent Claim
62 words
The method in accordance with claim 11 further comprising the steps of: compacting the enclosed powder by applying pressure to the first punch and the second punch; fixing the punches to the die after the compacting step to prevent disassembly during rolling; evacuating the assembly to outgas the compacted powder; and sealing the evacuated assembly prior to the heating and compressing steps.
Claim 17
Dependent Claim
34 words
The method according to claim 14 wherein the powder is compacted to a density not exceeding 75% of the theoretical maximum density, and the density resulting from the first rolling is at least 90%.
Claim 18
Dependent Claim
47 words
The method according to claim 15 wherein the protrusion ratio is in the range 1.2 to 2, and the gap ratio G/T D is within the range 0.95 to 1.05, where G is the distance between the rolls, and T D is the thickness of the die.
Claim 19
Independent Claim
186 words
The method of making high-density plates from a powder containing a first metal, which comprises the steps of: placing the powder into a cavity of a die of a second metal which has a ductility substantially exceeding that of the first metal; disposing a pair of metal punches to partially penetrate into the cavity from opposite ends of the die and to form an assembly which encloses the powder; the punches having sufficient thickness that a portion of each punch protrudes from the end of the die after the compacting step; compacting the powder by applying pressure to the punches; welding the punches to the die after the compacting step; evacuating the assembly to outgas the compacted powder; sealing the evacuated assembly with the powder under vacuum; heating the sealed assembly to a temperature at which the powder can be consolidated; rolling the assembly in a first pass between two rolls to depress each punch substantially flush with the ends of the die, and to consolidate the powder; and rolling the assembly in a second pass to elongate and increase the density of the consolidated powder.
Claim 20
Independent Claim
186 words
The method of making high-density plates from a powder containing a first metal, which comprises the steps of: placing the powder into a cavity of a die of a second metal which has a ductility substantially exceeding that of the first metal; disposing a pair of metal punches to partially penetrate into the cavity from opposite ends of the die and to form an assembly which encloses the powder; the punches having sufficient thickness that a portion of each punch protrudes from the end of the die after the compacting step; compacting the powder by applying pressure to the punches; welding the punches to the die after the compacting step; evacuating the assembly to outgas the compacted powder; sealing the evacuated assembly with the powder under vacuum; heating the sealed assembly to a temperature at which the powder can be consolidated; rolling the assembly in a first pass between two rolls to depress each punch substantially flush with the ends of the die, and to consolidate the powder; and rolling the assembly in a second pass to elongate and increase the density of the consolidated powder.
Claim 21
Dependent Claim
51 words
The method in accordance with claim 17 wherein the powder is compacted to a density not exceeding 75% of theoretical maximum density by the compacting step; the density is increased to at least 90% by the first pass; and the density is increased to at least 95% by the second pass.
Claim 22
Dependent Claim
37 words
The method in accordance with claim 18 further comprising the steps of: flowing a chemically reducing gas through the assembly to purify the powder; and preventing oxidation of the powder until the assembly is sealed under vacuum.
Claim 23
Dependent Claim
30 words
The method in accordance with claim 19 wherein the powder contains chromium, the temperature of the assembly during rolling is 1100° to 1300° C., and the reactive gas is hydrogen.
Claim 24
Dependent Claim
142 words
An assembly adapted to be heated and rolled to form a composite including a layer of consolidated powder, comprising: a metal die having a cavity; at least one metal punch disposed to intrude a distance d i into the cavity and protrude a distance d p from an end of the die; means for fixing the punch to the die; and a layer of metal powder which is enclosed in the cavity by the die and the punch, and which has a thickness T M and a fractional density ρ c ; wherein the intrusion ratio d i /d p for each punch is within the range 0.5 to 2, and the protrusion ratio P/(1-ρ c )T M is within the range 1 to 2, where P is the total distance by which the punches protrude from the ends of the die.
Claim 25
Dependent Claim
142 words
An assembly adapted to be heated and rolled to form a composite including a layer of consolidated powder, comprising: a metal die having a cavity; at least one metal punch disposed to intrude a distance d i into the cavity and protrude a distance d p from an end of the die; means for fixing the punch to the die; and a layer of metal powder which is enclosed in the cavity by the die and the punch, and which has a thickness T M and a fractional density ρ c ; wherein the intrusion ratio d i /d p for each punch is within the range 0.5 to 2, and the protrusion ratio P/(1-ρ c )T M is within the range 1 to 2, where P is the total distance by which the punches protrude from the ends of the die.
Claim 26
Dependent Claim
22 words
The assembly in accordance with claim 21 further comprising: means for sealing the assembly so that the powder layer is under vacuum.
Claim 27
Dependent Claim
28 words
The assembly in accordance with claim 22 which includes a pair of punches disposed to intrude into said cavity from opposite ends with the powder layer between them.
Claim 28
Dependent Claim
18 words
The combination in accordance with claim 19 wherein at least one auxiliary plate is interposed between the punches.
Claim 29
Dependent Claim
30 words
The combination in accordance with claim 24 wherein the total thickness of one punch is equal to the thickness of the other punch plus the thickness of the auxiliary plate.
References Cited (Backward Citations)
US2195297A
Cited
US2549596A
Cited
US3182391A
Cited
US3256088A
Cited
US3331686A
Cited
US3413393A
Cited
US3676079A
Cited
US3474516A
Cited
US3436802A
Cited
US3496425A
Cited
US3611546A
Cited
US3671230A
Cited
US3814598A
Cited
US4008023A
Cited
US3810757A
Cited
US3975193A
Cited
US3861839A
Cited
US4025313A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-20 | 1982-05-22 | 1982-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-20 | 1986-05-22 | 1986-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-20 | 1990-05-22 | 1990-11-21 | $7700.00 | Window Closed / Lapsed |