Process for the production of phenol silicate compounds and their condensation products

Claim 2

The process for the production of phenol silicate compounds and their resinous products by the following steps: (a) mixing about 1 part by weight of fine granular silica (SiO 2 ) and 1 to 2 parts by weight of a phenol compound; (b) adding an alkali catalyst in an aqueous solution until the pH is 10 to 12; (c) heating said mixture to 70° to 120° C. while agitating for 30 to 120 minutes, thereby (d) producing a granular phenol silicate compound.

Claim 3

The process of claim 1 wherein the phenol compound is selected from the group consisting of phenol, p-cresol, o-cresol, m-cresol, cresylic acid, xylenols, resorcinol, cashew-nut shell liquids, anacordol, p-tert-butyl phenol, cardol, anacardic acid, Bisphenol A, creosote oil, 2,6-dimethylphenol, and mixtures thereof.

Claim 4

The process of claim 1 wherein the alkali catalyst is selected from the group consisting of sodium hydroxide and potassium hydroxide.

Claim 5

The process of claim 1 including the further steps of: (a) adding an aldehyde in the ratio of 0.5 to 3 mols of each mol of the phenol compound; (b) heating said mixture to 70° to 120° C. for 30 to 120 minutes while agitating, thereby (c) producing a poly (aldehyde phenol silicate) resinous product.

Claim 6

The process of claim 4 wherein the aldehyde is selected from the group consisting of formaldehyde, acetaldehyde, butylaldehyde, acrolein, paraformaldehyde, furfural, crotonaldehyde, and mixtures thereof.

Claim 7

The process of claim 4 including the further step of adding an acid catalyst until the pH is 4 to 6 following step (a) and before step (b).

Claim 8

The process of claim 6 wherein the acid catalyst is selected from the group consisting of sulfuric acid, hydrochloric acid, acetic acid, formic acid, oxalic acid, aromatic sulfonic acid, sodium hydrogen sulfate and mixtures thereof.

Claim 9

The process of claim 1 wherein the phenol compound is phenol.

Claim 10

The method of claim 4 wherein the aldehyde is formaldehyde in an aqueous solution.

Claim 11

The process for the production of phenol silicate resinous products by the following steps: (a) adding 1 part by weight of fine granular silica to 1 to 3 parts by weight of a phenol compound, selected from the group consisting of phenol, p-cresol, o-cresol, m-cresol, cresylic acid, xylenols, resorcinol, cashew-nut shell liquids, anacordol, p-tert-butyl phenol, p-tert-amyl phenol, p-phenyl phenol, cardol, anacardic acid, Bisphenol A, creosote oil, 2,6-dimethylphenol and mixtures thereof; (b) adding an alkali catalyst, in an aqueous solution to the silica and phenol compound, selected from the group consisting of sodium hydroxide and potassium hydroxide until the pH is 10 to 12; (c) adding an aldehyde to said mixture in the ratio of 0.5 to 3 mols to each mol of the phenol compound, and the aldehyde is selected from the group consisting of formaldehyde in an aqueous solution, acetaldehyde, butylaldehyde, acrolein, paraformaldehyde, furfural, crotonaldehyde and mixtures thereof; (d) heating said mixture to 70° to 120° C. for 30 to 120 minutes while agitating, thereby (e) producing a poly(aldehyde phenol silicate) resinous product.

Claim 12

The process for the production of phenol silicate resinous products by the following steps: (a) adding 1 part by weight of fine granular silica to 1 to 3 parts by weight of a phenol compound, selected from the group consisting of phenol, p-cresol, o-cresol, m-cresol, cresylic acid, xylenols, resorcinol, cashew-nut shell liquids, anacordol, p-tert-butyl phenol, p-tert-amyl phenol, p-phenyl phenol, cardol, anacardic acid, Bisphenol A, creosote oil, 2,6-dimethylphenol and mixtures thereof; (b) adding an alkali catalyst, in an aqueous solution to the silica and phenol compound, selected from the group consisting of sodium hydroxide and potassium hydroxide until the pH is 10 to 12; (c) adding an aldehyde to said mixture in the ratio of 0.5 to 3 mols to each mol of the phenol compound, and the aldehyde is selected from the group consisting of formaldehyde in an aqueous solution, acetaldehyde, butylaldehyde, acrolein, paraformaldehyde, furfural, crotonaldehyde and mixtures thereof; (d) heating said mixture to 70° to 120° C. for 30 to 120 minutes while agitating, thereby (e) producing a poly(aldehyde phenol silicate) resinous product.

Claim 13

The process of claim 10 wherein an acid selected from the group consisting of sulphuric acid, hydrochloric acid, acetic acid, formic acid, oxalic acid, aromatic sulfonic acids, sodium hydrogen sulfate and mixtures thereof is added until the pH is about 3 to 5 in step (e) after the mixture has been heated for 30 to 120 minutes while agitating.

Claim 14

The phenol silicate compound as produced by the process of claim 1.

Claim 15

The poly(aldehyde phenol silicate) resinous product as produced by the process of claim 4.

Claim 16

The poly(aldehyde phenol silicate) resinous product as produced by the process of claim 10.

Claim 17

The process of claim 1 wherein additional steps are taken as follows: (a) mixing 1 part by weight of said phenol silicate compound with 0.5 to 2 parts by weight of an epoxy compound, epichlorohydrin; (b) heating the mixture to a temperature just below the boiling temperature of epichlorohydrin for 20 to 40 minutes while agitating at ambient pressure, thereby (c) producing an epoxy silicate compound.

Claim 18

The process of claim 1 wherein additional steps are taken as follows: (a) mixing 1 part by weight of said phenol silicate compound with 0.5 to 1 part by weight of a polyisocyanate, then agitated at ambient temperature and pressure for 10 to 20 minutes, thereby (b) producing a poly (urethane silicate) prepolymer; (c) adding 1 to 3% by weight of curing catalyst, percentage based on the weight of the urethane silicate resinous product, and the mixture expands, thereby (b) producing a self standing poly (urethane silicate) foam.

Claim 19

The process of claim 10 wherein additional steps are taken as follows: (a) mixing 1 part by weight of said poly (aldehyde phenol silicate) resinous product with 0.5 to 2 parts by weight of an epoxy compound, epichlorohydrin; (b) heating said mixture to a temperature just below the boiling temperature of epichlorohydrin for 20 to 40 minutes, thereby producing an epoxy silicate resinous product.

Claim 20

The process of claim 10 wherein additional steps are taken as follows: (a) mixing 1 part by weight of said poly (adelhyde phenol silicate) resinous product with 0.5 to 1 part by weight of a polyisocyanate, then agitating for 10 to 20 minutes, thereby (b) producing poly (urethane silicate) prepolymer; (c) adding 1 to 3% by weight of glacial acetic acid, percentage based on the weight of the urethane silicate resinous product, and the mixture expands, thereby (d) producing a self standing poly (urethane silicate) foam.

Claim 21

The process of claim 1 wherein additional steps are taken as follows: (a) mixing about equal parts by weight of the phenol silicate compound and furfuryl alcohol (b) adding a mineral acid until the pH is 5 to 6 while agitating for 10 to 20 minutes, thereby (c) producing poly (furfuryl phenol silicate) resinous product.

Claim 22

The process of claim 16 wherein the polyisocyanate is selected from the group consisting of arylene polyisocyanates and alkylene polyisocyanates.

Claim 23

The process of claim 16 wherein the polyisocyanate is is toluene-2,4-diisocyanate, toluene-2,6-diisocyanate and mixtures thereof.

Claim 24

The poly (urethane silicate) foam as produced by the process of claim 16.

Claim 25

The poly (urethane silicate) foam as produced by the process of claim 18.

Claim 26

The epoxy silicate resinous product as produced by the process of claim 17.

Claim 27

Th poly (furfuryl phenol silicate) resinous product as produced by the process of claim 19.

Claim 28

The epoxy silicate compound as produced by the process of claim 15.

Claim 29

The process of claim 16 wherein the curing catalyst is selected from the group consisting of water, glacial acetic acid, aqueous solution of butynediol and mixtures thereof.

Claim 30

The process of claim 15 wherein a catalytic amount of a curing catalyst, selected from the group consisting of Lewis acids and amine compounds, is added to the epoxy silicate compound thereby producing an epoxy silicate product.

Claim 31

The epoxy silicate product as produced by the process of claim 28.