US4122238A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Welding flux formulation and process for fume reduction
Assignee: Caterpillar Inc
•
Filing: 1976-05-19
•
Granted: 1978-10-24
•
Expires: 1996-05-19
Abstract
Abstract The invention is concerned with a welding flux composition comprising a first alloy including iron, at least two metals reactive with oxygen under welding conditions and selected from the group consisting of aluminum, titanium, zirconium and boron and a weld improving metal selected from the group consisting of magnesium and manganese, said first alloy comprising from about 1 percent to about 4.5 percent by weight of the flux composition. The invention is also concerned with a weld forming composition comprising a metal tube having therewithin a welding flux as set out above. The invention is further concerned with a process for reducing particulate matter produced during the welding operation, comprising a welding flux used in said operation including from about 1 percent to about 4.5 percent by weight of the above first alloy.
Inventors
- 👤 John G. Frantzerb, Sr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 08:43
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/36; B23K35/368; B23K35/3601; B23K35/3608; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12097; Y10T428/12139
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
78 words
A welding flux composition which produces a reduced amount of particulate matter, comprising: a first distinct alloy having at least four metals, said first alloy including iron, at least two metals reactive with oxygen under welding conditions selected from a group consisting of aluminum, titanium, zirconium and boron and a weld improving metal selected from a group consisting of magnesium and manganese, said first alloy comprising from about 1 percent to about 4.5 percent of said flux composition.
Claim 2
Dependent Claim
78 words
A welding flux composition which produces a reduced amount of particulate matter, comprising: a first distinct alloy having at least four metals, said first alloy including iron, at least two metals reactive with oxygen under welding conditions selected from a group consisting of aluminum, titanium, zirconium and boron and a weld improving metal selected from a group consisting of magnesium and manganese, said first alloy comprising from about 1 percent to about 4.5 percent of said flux composition.
Claim 3
Dependent Claim
67 words
A composition as in claim 1, wherein said first alloy includes aluminum and titanium with the amount of said aluminum falling within a range from about 4 weight percent to about 25 weight percent and the amount of said titanium falling within a range from about 5 weight percent to about 40 weight percent, said weight percentages being based on the total weight of said first alloy.
Claim 4
Dependent Claim
48 words
A composition as in claim 2 including titanium dioxide, a second alloy including iron and manganese or magnesium and a third alloy including iron and silicon, said titanium dioxide together with said second alloy and said third alloy comprising at least about 50 percent of said flux composition.
Claim 5
Dependent Claim
39 words
A composition as in claim 3, wherein said first alloy includes zirconium in an amount which falls within a range from about 1 weight percent to about 15 weight percent based on the total weight of said first alloy.
Claim 6
Dependent Claim
39 words
A composition as in claim 4, wherein said first alloy includes boron in an amount which falls within a range from about 0.1 weight percent to about 5 weight percent based on the total weight of said first alloy.
Claim 7
Dependent Claim
88 words
A process for reducing particulate matter produced during a welding operation, comprising including in a welding flux used in said operation from about 1 percent to about 4.5 weight percent based on the total weight of said flux of a first distinct alloy having at least four metals, said first alloy including iron, at least two metals reactive with oxygen under welding conditions selected from the group consisting of aluminum, titanium, zirconium and boron and a weld improving metal selected from the group consisting of magnesium and manganese.
Claim 8
Dependent Claim
88 words
A process for reducing particulate matter produced during a welding operation, comprising including in a welding flux used in said operation from about 1 percent to about 4.5 weight percent based on the total weight of said flux of a first distinct alloy having at least four metals, said first alloy including iron, at least two metals reactive with oxygen under welding conditions selected from the group consisting of aluminum, titanium, zirconium and boron and a weld improving metal selected from the group consisting of magnesium and manganese.
Claim 9
Dependent Claim
52 words
A process as in claim 6 wherein said flux includes titanium dioxide, a second alloy including iron and manganese or magnesium and a third alloy including iron and silicon, said titanium dioxide together with said second alloy and said third alloy comprising at least about 50 weight percent of said flux composition.
Claim 10
Dependent Claim
60 words
A process as in claim 7 wherein said flux includes aluminum and titanium in amounts which fall within the range from about 4 weight percent to about 25 weight percent aluminum and from about 5 weight percent to about 40 weight percent titanium, said weight percentages of aluminum and titanium being based on the total weight of said first alloy.
Claim 11
Dependent Claim
34 words
A process as in claim 8 wherein said first alloy includes zirconium in an amount from about 1 weight percent to about 15 weight percent based on the total weight of said first alloy.
Claim 12
Dependent Claim
33 words
A process as in claim 9 wherein said first alloy includes boron in an amount from about 0.1 weight percent to about 5 weight percent based on the total of said first alloy.
Claim 13
Dependent Claim
81 words
A weld forming electrode comprising a metal tube having therewithin a compacted welding flux comprising: a first distinct alloy having at least four metals, said first alloy including: iron; at least two metals reactive with oxygen under welding conditions selected from the group consisting aluminum, titanium, zirconium and boron; and a weld improving metal selected from the group consisting of magnesium and manganese, said first alloy comprising from about 1 percent to about 5 percent by weight of said flux composition.
Claim 14
Dependent Claim
81 words
A weld forming electrode comprising a metal tube having therewithin a compacted welding flux comprising: a first distinct alloy having at least four metals, said first alloy including: iron; at least two metals reactive with oxygen under welding conditions selected from the group consisting aluminum, titanium, zirconium and boron; and a weld improving metal selected from the group consisting of magnesium and manganese, said first alloy comprising from about 1 percent to about 5 percent by weight of said flux composition.
Claim 15
Dependent Claim
49 words
A weld forming composition as in claim 11 including titanium dioxide, a second alloy including iron and manganese or magnesium and a third alloy including iron and silicon, said titanium dioxide together with said second alloy and said third alloy comprising at least about 50 percent of said flux.
Claim 16
Dependent Claim
50 words
A welding electrode as in claim 12 wherein said first alloy includes aluminium in an amount from about 4 weight percent to about 25 weight percent and titanium in an amount from about 5 weight percent to about 40 weight percent based on the total weight of said first alloy.
Claim 17
Dependent Claim
34 words
An electrode as in claim 13 wherein said first alloy includes zirconium in an amount from about 1 weight percent to about 15 weight percent based on the total weight of said first alloy.
Claim 18
Dependent Claim
34 words
An electrode as in claim 14 wherein said first alloy includes boron in an amount from about 0.1 weight percent to about 5 weight percent based on the total weight of said first alloy.
References Cited (Backward Citations)
US3177340A
Cited
US3461270A
Cited
US3405250A
Cited
US3420980A
Cited
US3513289A
Cited
US3558851A
Cited
US3560702A
Cited
US3539765A
Cited
US3603763A
Cited
US3911244A
Cited
US3745294A
Cited
US3702390A
Cited
US3924091A
Cited
US3805016A
Cited
US3875363A
Cited
US3796609A
Cited
US3866015A
Cited
US3868491A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |