Fire protective thermal barriers for foam plastics
Assignee: Individual
•
Filing: 1978-01-09
•
Granted: 1978-10-24
•
Expires: 1998-01-09
Abstract
Abstract A foamed polymeric material is coated with a fire protective thermal barrier product. The polymeric material, thus protected, is used for on-site application on walls, ceilings, decks and roofs of buildings. The thermal barrier product (hereafter "thermal barrier" for brevity) is also used to protect foam plastics in fire-resistant factory-made building panels, the exteriors of tanks and other vessels, and the coverings over pipes. The thermal barrier comprises a normally fluent thermosetting synthetic resinous material in which is dispersed an effective amount of hydrated magnesium sulfate and, optionally, inert inorganic fillers, pigments and the like. The thermal barrier is flowed or sprayed onto the foamed polymeric material, optionally, with an adhesive interlayer or "tie-coat" therebetween, to form a fire resistant laminate which laminate meets the "15-minute finish rating" or "hourly rated" requirement of building codes as determined by a testing procedure currently designated ASTM E-119-76, and other fire resistance requirements as determined by other fire resistance tests. A process is disclosed for utilizing compositions belonging to a family of thermal barrier products containing inorganic salts having water of crystallization which is driven off at a temperature from about 200° F but less than 600° F.
Inventors
- 👤 Joel S. Stahl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:37
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/065; B32B5/00; B32B5/18; B32B27/18; E; E04; E04B; E04B1/00; E04B1/62; E04B1/92; E04B1/94; B32B38/00; B32B2038/0052; B32B2038/0084; B32B2264/00; B32B2264/10; B32B2264/104; B32B2307/00; B32B2307/30; B32B2307/306; B32B2307/3065; B32B2607/00; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249991; Y10T428/249992; Y10T428/25; Y10T428/256
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
85 words
A fire-protective thermal barrier comprising a cured thermosetting synthetic resinous material having dispersed therein an effective amount of a finely divided, crystalline, hydrated inorganic salt extender, sufficient to provide a predetermined level of fire resistance as specifically determined by ASTM E-119-76 or other fire resistance testing procedures, said hydrated extender being characterized by having at least 35% by weight water of crystallization, the major portion of which is released upon heating to a temperature in the range from about 200° F. but below 600° F.
Claim 2
Dependent Claim
85 words
A fire-protective thermal barrier comprising a cured thermosetting synthetic resinous material having dispersed therein an effective amount of a finely divided, crystalline, hydrated inorganic salt extender, sufficient to provide a predetermined level of fire resistance as specifically determined by ASTM E-119-76 or other fire resistance testing procedures, said hydrated extender being characterized by having at least 35% by weight water of crystallization, the major portion of which is released upon heating to a temperature in the range from about 200° F. but below 600° F.
Claim 3
Dependent Claim
49 words
The fire-protective thermal barrier of claim 1 wherein said hydrated extender is selected from the group consisting of hydrated salts of Group II A elements of the Periodic Table, and said thermosetting resinous material is selected from the group consisting of a polyester, polyrurethane, polyacrylate, epoxy and urea-formaldehyde resin.
Claim 4
Dependent Claim
18 words
The fire-protective thermal barrier of claim 1 wherein said thermal barrier includes catalysts promoters, viscosity modifiers and pigments.
Claim 5
Dependent Claim
39 words
The fire-protective thermal barrier of claim 1 including in addition to said hydrated extender, an inorganic particulate filler in an amount from about 1 part by wt to about 15 parts by weight per 100 part of thermal barrier.
Claim 6
Dependent Claim
26 words
The fire-protective thermal barrier of claim 2 wherein said hydrated salts are selected from the group consisting of magnesium sulfate heptahydrate, magnesium sulfite, and magnesium monohydroorthophosphate.
Claim 7
Dependent Claim
41 words
The fire-protective thermal barrier of claim 5 wherein said magnesium sulfate heptahydrate (MgSO 4 .7H 2 O) is present in an amount from about 30 parts to about 80 parts by weight per 100 parts of mixed resin an hydrated extender.
Claim 8
Dependent Claim
59 words
The fire-protective thermal barrier of claim 1 further charactized, in that it is essentially impermeable to moisture, said thermal barrier in a thickness of 0.135 inch having a perm rating of 0.0295 as determined by testing procedure designated ASTM E 96-66, and impact resistance in excess of about 20 inch pounds as determined by the Gardner Drop Dart test.
Claim 9
Dependent Claim
99 words
A fire-protective insulating laminate comprising a foam plastic and bonded thereto a thermal barrier comprising a cured thermosetting synthetic resinous material having dispersed therein an effective amount of a finely divided, crystalline, hydrated inorganic salt extender, sufficient to provide a predetermined level of fire resistance as determined specifically by a testing procedure designated ASTM E-119-76, or other fire resistance testing procedures, said hydrated extender being characterized by having at least 35% by weight water of crystallization, the major portion of which is released upon heating to a temperature in the range from about 200° F. but below 600° F.
Claim 10
Dependent Claim
99 words
A fire-protective insulating laminate comprising a foam plastic and bonded thereto a thermal barrier comprising a cured thermosetting synthetic resinous material having dispersed therein an effective amount of a finely divided, crystalline, hydrated inorganic salt extender, sufficient to provide a predetermined level of fire resistance as determined specifically by a testing procedure designated ASTM E-119-76, or other fire resistance testing procedures, said hydrated extender being characterized by having at least 35% by weight water of crystallization, the major portion of which is released upon heating to a temperature in the range from about 200° F. but below 600° F.
Claim 11
Dependent Claim
49 words
The fire-protective laminate of claim 8 wherein said hydrated extender is selected from the group consisting of hydrated salts of Group II A elements of the Periodic Table, and said thermosetting synthetic resinous material is selected from the group consisting of a polyester, polyurethane, polyacrylate, epoxy, and urea-formaldehyde resin.
Claim 12
Dependent Claim
38 words
The fire-protective laminate of claim 8 including in addition to said hydrated extender, an inorganic particulate filler in an amount from about 1 part by weight to about 15 parts by weight per 100 parts of thermal barrier.
Claim 13
Dependent Claim
17 words
The fire-protective laminate of claim 8 wherein said thermal barrier includes catalysts, promoters, viscosity modifiers and pigments.
Claim 14
Dependent Claim
33 words
The fire-protective laminate of claim 8 wherein said foam plastic is a synthetic material selected from the group consisting of a polyurethane foam, a polyisocyanurate foam, a urea-formaldehyde foam, and a polystyrene foam.
Claim 15
Dependent Claim
25 words
The fire-protective laminate of claim 9 wherein said hydrated salts are selected from the group consisting of magnesium sulfate heptahydrate, magnesium sulfite, and magnesium monohydroorthophosphate.
Claim 16
Dependent Claim
40 words
The fire-protective laminate of claim 13 wherein said magnesium sulfate heptahydrate (MgSO 4 .7H 2 O) is present in an amount from about 30 parts to about 80 parts by weight per 100 parts of mixed resin and hydrated extender.
Claim 17
Dependent Claim
18 words
The fire-protective laminate of claim 10 wherein said foam plastic and said thermal barrier are each selectively field-applied.
Claim 18
Dependent Claim
36 words
The fire-protective laminate of claim 8 wherein said foam plastic consists essentially of a synthetic resinous material selected from the group consisting of a polyurethane foam, a polyisocyanurate foam, a urea-formaldehyde foam, and a polystyrene foam.
Claim 19
Dependent Claim
16 words
The fire-protective laminate of claim 8 wherein said thermal barrier is self-adhered to said foam plastic.
Claim 20
Dependent Claim
114 words
A fire-protective insulating panel comprising an inner and outer skin and a laterally coextensive laminate bonded thereto, said laminate comprising a foam plastic and bonded to one side a thermal barrier comprising a cured thermosetting synthetic resinous material having dispersed therein an effective amount of a finely divided, crystalline, hydrated inorganic salt extender, sufficient to provide a predetermined level of fire resistance as specifically determined by testing procedure designated ASTM E-119-76, or other fire resistance testing procedures, said hydrated extender being characterized by having at least 35% by weight of crystallization, the major portion of which is released upon heating to a temperature in the range from about 200° F. but below 600° F.
Claim 21
Dependent Claim
114 words
A fire-protective insulating panel comprising an inner and outer skin and a laterally coextensive laminate bonded thereto, said laminate comprising a foam plastic and bonded to one side a thermal barrier comprising a cured thermosetting synthetic resinous material having dispersed therein an effective amount of a finely divided, crystalline, hydrated inorganic salt extender, sufficient to provide a predetermined level of fire resistance as specifically determined by testing procedure designated ASTM E-119-76, or other fire resistance testing procedures, said hydrated extender being characterized by having at least 35% by weight of crystallization, the major portion of which is released upon heating to a temperature in the range from about 200° F. but below 600° F.
Claim 22
Dependent Claim
52 words
The fire-protective insulating panel of claim 18 including in addition, an inner and outer skin and a laterally coextensive laminate bonded thereto, said laminate comprising a foam plastic and bonded to each side a first and second thermal barrier, said second thermal barrier being of similar composition to said first thermal barrier.
Claim 23
Dependent Claim
151 words
A spraying or flowing method for forming a fire-protective laminate comprising a foam plastic and, bonded thereto, a thermal barrier comprising a mixture of liquid thermosetting synthetic resin and said inorganic material dispersed therein, said method comprising: (a) admixing into said liquid resin from about 30 parts to about 80 parts by weight of a hydrated inorganic salt extender consisting essentially of a hydrated salt of a Group II A element, said hydrated salt being present in the size range from about 10 U.S. Standard mesh to about 325 mesh, (b) admixing into said liquid resin sufficient catalyst to provide cured resin in a predetermined period of time, and (c) bonding said resin to a foam plastic to form said laminate, so as to provide said laminate with fire resistant properties sufficient to meet the requirements as determined by a testing procedure designated ASTM E-119-76 or other fire resistance testing procedures.
Claim 24
Dependent Claim
151 words
A spraying or flowing method for forming a fire-protective laminate comprising a foam plastic and, bonded thereto, a thermal barrier comprising a mixture of liquid thermosetting synthetic resin and said inorganic material dispersed therein, said method comprising: (a) admixing into said liquid resin from about 30 parts to about 80 parts by weight of a hydrated inorganic salt extender consisting essentially of a hydrated salt of a Group II A element, said hydrated salt being present in the size range from about 10 U.S. Standard mesh to about 325 mesh, (b) admixing into said liquid resin sufficient catalyst to provide cured resin in a predetermined period of time, and (c) bonding said resin to a foam plastic to form said laminate, so as to provide said laminate with fire resistant properties sufficient to meet the requirements as determined by a testing procedure designated ASTM E-119-76 or other fire resistance testing procedures.
Claim 25
Dependent Claim
67 words
The method of claim 20 including continuously forming a building panel having a foam plastic core comprising applying a predetermined thickness of said resin, including catalyst, heating said thickness of resin to effect an incomplete cure, and foaming said foam plastic in place on said resin prior to said resin being fully cured, so as subsequently to effect bonding of said foam plastic to said cured resin.
Claim 26
Dependent Claim
15 words
The method of claim 20 comprising applying said thermal barrier to foam plastic board stock.
Claim 27
Dependent Claim
34 words
The method of claim 20 comprising spraying said thermal barrier in a fluent state on foam plastic which is applied to walls, ceilings, decks, roofs and the exterior surfaces of tanks, vessels and pipes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |