High ortho etherified resole resins

Claim 2

An aqueous emulsion of a high ortho etherified phenol-formaldehyde resole resin said resin being characterized by: A. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, B. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, C. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, D. having an average degree of polymerization of less than 4.0, and E. having said methylol groups partially etherified with monohydric alcohols, said aqueous emulsion comprising about 20 to 50 percent by weight of said etherified phenol-formaldehyde resole resin solids contained in said aqueous emulsion, said solids being emulsified with an nonionic emulsifier, said etherified resoles being prepared by an improved process by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C., in the presence of a divalent electropositive metal ion, while maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, forming said resole in said reaction mixture, the improvement comprising, etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C. in said reaction mixture and dehydrating the resultant aqueous reaction mixture to a water content of less than about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin.

Claim 3

A high ortho etherified resole resin varnish comprising: A. from about 30 to 99 weight percent of reactive solids of a high ortho etherified phenol-formaldehyde resole resin,

Claim 4

A high ortho etherified resole resin varnish comprising: A. from about 30 to 99 weight percent of reactive solids of a high ortho etherified phenol-formaldehyde resole resin,

Claim 5

B. from about 0.5 to 30 weight percent of dissolved water, C. the balance up to 100 weight percent of any given varnish being an organic liquid which: 1. is substantially inert (as respects such resin and water), 2. evaporates below about 200° C., at atmospheric pressures, and 3. is a mutual solvent for said resole resin and said water (if present), the amount of said organic liquid being present in any given varnish being such as to maintain both said resole resin and said water in dissolved form, said high etherified phenol formaldehyde resole resin being characterized by: D. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, E. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, F. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, G. hving an average degree of polymerization of less than 4.0, and H. having said methylol groups partially etherified with monohydric alcohols, said etherified resoles being prepared by an improved process by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C. to 100° C., in the presence of a divalent electropositive metal ion, while maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, forming said resole in said reaction mixture, the improvement comprising, etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C. in said reaction mixture and dehydrating the resultant aqueous reaction mixture to a water content of less than about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin.

Claim 6

B. from about 0.5 to 30 weight percent of dissolved water, C. the balance up to 100 weight percent of any given varnish being an organic liquid which: 1. is substantially inert (as respects such resin and water), 2. evaporates below about 200° C., at atmospheric pressures, and 3. is a mutual solvent for said resole resin and said water (if present), the amount of said organic liquid being present in any given varnish being such as to maintain both said resole resin and said water in dissolved form, said high etherified phenol formaldehyde resole resin being characterized by: D. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, E. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, F. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, G. hving an average degree of polymerization of less than 4.0, and H. having said methylol groups partially etherified with monohydric alcohols, said etherified resoles being prepared by an improved process by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C. to 100° C., in the presence of a divalent electropositive metal ion, while maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, forming said resole in said reaction mixture, the improvement comprising, etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C. in said reaction mixture and dehydrating the resultant aqueous reaction mixture to a water content of less than about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin.

Claim 7

An aqueous emulsion of claim 1 having present a nonionic emulsifier selected from the group consisting of a hydroxy ethyl cellulose, and a partially hydrolyzed polyvinyl acetate having 15 to 30 percent by weight polyvinyl alcohol, said emulsifier being present in an amount sufficient to provide a stable aqueous emulsion.

Claim 8

An aqueous emulsion of claim 1 wherein said meta substituted phenol is a phenol having at least one attached radical selected from the group consisting of alkyl, aryl, cycloalkyl, alkenyl, cycloalkenyl, alkaryl, aralkyl, carbocyclic, halogen and mixtures thereof.

Claim 9

An aqueous emulsion of claim 1 wherein said substituted phenol is a phenol substituted with a material selected from the group consisting of indenes, vinylidene aromatics, cyclopentadienes, dicylopentadienes, nonenes, octenes, terpenes and mixtures thereof.

Claim 10

An aqueous emulsion of claim 1 wherein said resole resin having been prepared by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C., in the presence of a divalent electropositive metal ion while maintaining a pH in the range between about 4 and 7 wherein said pH is controlled by adding sufficient amounts of an organic acid and thereafter etherifying said resole resin with a monohydric alcohol at a temperature of 65°-100° C., and dehydrating the resulting aqueous solution to a water content of less than about 1 weight percent and an alcohol content of less than about 5 percent.

Claim 11

An aqueous emulsion of claim 6 wherein said divalent electropositive metal ion is provided by a compound selected from the group consisting of oxides, hydroxides and organic acid salts of such metal ions, and wherein said resole resins are prepared in the presence of said compounds wherein the amount of said compound is within the range of about 0.1 to 10.0 weight percent based on the weight of said phenols.

Claim 12

An aqueous emulsion of claim 6 wherein said divalent electropositive metal ion is selected from the group consisting of zinc (Zn++), cobalt (Co+++), magnesium (Mg++), manganese (Mn++) and calcium (Ca++) or mixtures thereof.

Claim 13

An aqueous emulsion of claim 6 wherein said resole resins are prepared while maintaining a pH in the range of between about 4 and 7 wherein said pH is controlled by adding sufficient amounts of an organic acid selected from the group consisting of an aliphatic monocarboxylic acid such as formic or acetic, an aliphatic hydroxy-carboxylic acid such as lactic, an aromatic carboxylic acid such as benzoic or a dicarboxylic acid such as adipic or succinic or mixtures thereof.

Claim 14

An aqueous emulsion of claim 1 wherein the monohydric alcohol is selected from the group consisting of alkyl and aralkyl.

Claim 15

An aqueous emulsion of claim 10 wherein said alkyl alcohols are primary and secondary alcohols having 1 to 12 carbon atoms.

Claim 16

An aqueous emulsion of claim 10 wherein said aralkyl are benzyl and phenethyl.

Claim 17

An aqueous emulsion of claim 1 wherein said alcohol is incorporated in amounts of about 0.05 to 0.50 methylol ether groups per phenolic group.

Claim 18

An aqueous emulsion of a high ortho etherified phenol-formaldehyde resole resin, said resin being characterized by: A. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, B. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, C. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, D. having an average degree of polymerization of less than 4.0, and E. having said methylol groups partially etherified with monohydric alcohols, said etherified resole being prepared by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C. to 100° C., in the presence of a divalent electropositive metal ion while maintaining a pH in the range between about 4 and 7 wherein said pH is controlled by adding sufficient amounts of an organic acid and thereafter etherifying said resole resin with a monohydric alcohol at a temperature of 65-100° C., and dehydrating the resulting aqueous solution to a water content of less than about 1 weight percent and an alcohol content of less than about 5%, said aqueous emulsion having present about 20 to 50% by weight of said etherified phenolformaldehyde resole resin solids based on said aqueous emulsion.

Claim 19

An aqueous emulsion of a high ortho etherified phenol-formaldehyde resole resin, said resin being characterized by: A. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, B. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, C. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, D. having an average degree of polymerization of less than 4.0, and E. having said methylol groups partially etherified with monohydric alcohols, said etherified resole being prepared by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C. to 100° C., in the presence of a divalent electropositive metal ion while maintaining a pH in the range between about 4 and 7 wherein said pH is controlled by adding sufficient amounts of an organic acid and thereafter etherifying said resole resin with a monohydric alcohol at a temperature of 65-100° C., and dehydrating the resulting aqueous solution to a water content of less than about 1 weight percent and an alcohol content of less than about 5%, said aqueous emulsion having present about 20 to 50% by weight of said etherified phenolformaldehyde resole resin solids based on said aqueous emulsion.

Claim 20

A resin varnish of claim 2 wherein said meta substituted phenol is a phenol having at least one attached radical selected from the group consisting of alkyl, aryl, cycloalkyl, alkenyl, cycloalkenyl, alkaryl, aralkyl, carbocyclic, halogen and mixtures thereof.

Claim 21

A resin varnish of claim 2 wherein said substituted phenol is a phenol substituted with a material selected from the group consisting of indenes, vinylidene aromatics, cyclopentadienes, dicyclopentadienes, nonenes, octenes, terpenes and mixtures thereof.

Claim 22

A resin varnish of claim 2 wherein said resole resin having been prepared by first reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C. to 100° C., in the presence of a divalent electropositive metal ion while maintaining a pH in the range between about 4 and 7 wherein said pH is controlled by adding sufficient amounts of an organic acid and thereafter etherifying said resole resin with a monohydric alcohol at a temperature of 65°-100° C., and dehydrating the resulting aqueous solution to a water content of less than about 1 weight percent and an alcohol content of less than about 5 percent.

Claim 23

A resin varnish of claim 17 wherein said divalent electropositive metal ion is provided by a compound selected from the group consisting of oxides, hydroxides and organic acid salts of such metal ions, and wherein said resole resins are prepared in the presence of said compounds wherein the amount of said compound is within the range of about 0.1 to 10.0 weight percent based on the weight of said phenols.

Claim 24

A resin varnish of claim 17 wherein said divalent electropositive metal ion is selected from the group consisting of zinc (Zn++), cobalt (CoL30 ++), magnesium (Mg++), manganese (Mn++) and calcium (Ca++) or mixtures thereof.

Claim 25

A resin varnish of claim 17 wherein said resole resins are prepared while maintaining a pH in the range of between about 4 and 7 wherein said pH is controlled by adding sufficient amounts of an organic acid selected from the group consisting of an aliphatic monocarboxylic acid such as formic or acetic, an aliphatic hydroxy-carboxylic acid such as lactic, an aromatic carboxylic acid such as benzoic or a dicarboxylic acid such as adipic or succinic or mixtures thereof.

Claim 26

A resin varnish of claim 2 wherein the monohydric alcohol is selected from the group consisting of alkyl and aralkyl.

Claim 27

A resin varnish of claim 21 wherein said alkyl alcohols are primary and secondary alcohols having 1 to 12 carbon atoms.

Claim 28

A resin varnish of claim 21 wherein said aralkyl are benzyl and phenethyl.

Claim 29

A resin varnish of claim 2 wherein said alcohol is incorporated in amounts of about 0.05 to 0.50 methylol ether groups per phenolic group.

Claim 30

A resin varnish of claim 2 wherein said organic liquid is selected from the group consisting of lower alkanols, lower alkones, aromatic hydrocarbons, aliphatic hydrocarbons and ether-esters or mixtures thereof.

Claim 31

An improved process for preparing aqueous emulsions of a high ortho etherified phenol-formaldehyde resole, said resin being characterized by: A. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, B. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, C. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, D. having an average degree of polymerization of less than 4.0, and E. having said methylol groups partially etherified with monohydric alcohols, said aqueous emulsion comprising about 20 to 50% by weight of said etherified phenolformaldehyde resole resin solids contained in said aqueous emulsion, said solids being emulsified with an nonionic emulsifier, said improved process including the steps: 1. reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C., to 100° C., 2. maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, 3. forming said resole in said reaction mixture, the improvement comprising: 4. etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C., in said reaction mixture, 5. dehyrating the resultant aqueous reaction mixture to a water content of less that about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin, and 6. blend said resin with an aqueous solution containing an nonionic emulsifier forming a stable emulsion having about 20 to 50% by weight of said resin in said emulsion.

Claim 32

An improved process for preparing aqueous emulsions of a high ortho etherified phenol-formaldehyde resole, said resin being characterized by: A. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, B. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, C. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, D. having an average degree of polymerization of less than 4.0, and E. having said methylol groups partially etherified with monohydric alcohols, said aqueous emulsion comprising about 20 to 50% by weight of said etherified phenolformaldehyde resole resin solids contained in said aqueous emulsion, said solids being emulsified with an nonionic emulsifier, said improved process including the steps: 1. reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C., to 100° C., 2. maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, 3. forming said resole in said reaction mixture, the improvement comprising: 4. etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C., in said reaction mixture, 5. dehyrating the resultant aqueous reaction mixture to a water content of less that about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin, and 6. blend said resin with an aqueous solution containing an nonionic emulsifier forming a stable emulsion having about 20 to 50% by weight of said resin in said emulsion.

Claim 33

An improved process for preparing a high ortho etherified resole resin varnish, said varnish being characterized by: A. from about 30 to 99 weight percent of reactive solids of a high ortho etherified phenol-formaldehyde resole resin, B. from about 0.5 to 30 weight percent of dissolved water, C. the balance up to 100 weight percent of any given varnish being an organic liquid which:

Claim 34

An improved process for preparing a high ortho etherified resole resin varnish, said varnish being characterized by: A. from about 30 to 99 weight percent of reactive solids of a high ortho etherified phenol-formaldehyde resole resin, B. from about 0.5 to 30 weight percent of dissolved water, C. the balance up to 100 weight percent of any given varnish being an organic liquid which:

Claim 35

is substantially inert (as respects such resin and water), 2. evaporates below about 200° C., at atmospheric pressures, and 3. is a mutual solvent for said resole resin and said water (if present), the amount of said organic liquid being present in any given varnish being such as to maintain both said resole resin and said water in dissolved form, said high etherified phenol formaldehyde resole resin being characterized by: D. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, E. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, F. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, G. having an average degree of polymerization of less than 4.0, and H. having said methylol groups partially etherified with monohydric alcohols, said improved process including the steps:

Claim 36

is substantially inert (as respects such resin and water), 2. evaporates below about 200° C., at atmospheric pressures, and 3. is a mutual solvent for said resole resin and said water (if present), the amount of said organic liquid being present in any given varnish being such as to maintain both said resole resin and said water in dissolved form, said high etherified phenol formaldehyde resole resin being characterized by: D. having a reacted formaldehyde to phenol mol ratio of 1.10 to 2.0, said formaldehyde reacting with said phenol, forming methylol groups taking a final orientation of about 90% to 100% in the ortho position, E. having said phenol selected from the group consisting of phenol, meta-substituted phenols and mixtures of phenol and substituted phenols, F. having condensed phenol-aldehyde linkages wherein 25 to 90% of said linkages are benzyl ether linkages having a final orientation essentially in the ortho position and 10 to 75% are methylene linkages taking a final orientation of about 70 to 90% in the ortho position and about 10 to 30% in the para position, G. having an average degree of polymerization of less than 4.0, and H. having said methylol groups partially etherified with monohydric alcohols, said improved process including the steps:

Claim 37

reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C., to 100° C., 2. maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, 3. forming said resole in said reaction mixture, the improvement comprising: 4. etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C., in said reaction mixture, 5. dehydrating the resultant aqueous reaction mixture to a water content of less than about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin, and 6. dissolving said resole resin in said organic liquid such that said high ortho etherified resole is present in amount of from about 30 to 99% by weight.

Claim 38

reacting said phenol and said formaldehyde in an aqueous reaction mixture under reflux at about 80° C., to 100° C., 2. maintaining the pH in the range of about 4 to 7, wherein said pH is controlled by having a sufficient amount of an organic acid present, 3. forming said resole in said reaction mixture, the improvement comprising: 4. etherifying said resole with a monohydric alcohol at a temperature of 65° to 100° C., in said reaction mixture, 5. dehydrating the resultant aqueous reaction mixture to a water content of less than about 1 weight percent and an alcohol content of less than about 5% by weight providing an etherified high ortho resole resin as a single phase clear liquid resole resin, and 6. dissolving said resole resin in said organic liquid such that said high ortho etherified resole is present in amount of from about 30 to 99% by weight.