US4022942A — Process of preparing fibrous sheet from high-orth…

Claim 1

Independent Claim 189 words

A process for preparing a resin impregnated sheet which comprises: A. preparing a resole resin by reacting a phenol selected from the group consisting of phenol, meta-substituted phenol and a mixture of phenol and at least one substituted phenol with formaldehyde in an aqueous reaction mixture containing at least 14 weight percent water under reflux at about 60° C. to 100° C. in the presence of a divalent electropositive metal ion and sufficient organic acid to maintain a pH in the range between about 4 and 7, and thereafter dehydrating the resulting aqueous emulsion to a water content of from about 0.5 to 15 weight percent, B. dissolving the resole resin in a volatile inert organic solvent to yield a solution of between 20 and 85 weight percent solids and a viscosity in the range of 5 to 500 centipoises, C. impregnating a fibrous sheet substrate with the resole resin solution to provide a fibrous sheet substrate containing from about 15 to 70 weight percent of the resole resin, D. drying the impregnated fibrous sheet substrate to reduce the volatile content, and E. advancing the resin to the B-stage.

Claim 2

Dependent Claim 189 words

A process for preparing a resin impregnated sheet which comprises: A. preparing a resole resin by reacting a phenol selected from the group consisting of phenol, meta-substituted phenol and a mixture of phenol and at least one substituted phenol with formaldehyde in an aqueous reaction mixture containing at least 14 weight percent water under reflux at about 60° C. to 100° C. in the presence of a divalent electropositive metal ion and sufficient organic acid to maintain a pH in the range between about 4 and 7, and thereafter dehydrating the resulting aqueous emulsion to a water content of from about 0.5 to 15 weight percent, B. dissolving the resole resin in a volatile inert organic solvent to yield a solution of between 20 and 85 weight percent solids and a viscosity in the range of 5 to 500 centipoises, C. impregnating a fibrous sheet substrate with the resole resin solution to provide a fibrous sheet substrate containing from about 15 to 70 weight percent of the resole resin, D. drying the impregnated fibrous sheet substrate to reduce the volatile content, and E. advancing the resin to the B-stage.

Claim 3

Dependent Claim 35 words

The process of claim 1 wherein the substituted phenol is a phenol having a least one attached radical selected from the group consisting of alkyl, aryl, cycloalkyl, alkenyl, cycloalkenyl, alkaryl, carbocyclic, halogen and mixtures thereof.

Claim 4

Dependent Claim 35 words

The process of claim 1 wherein the substituted phenol is the addition product of phenol and a compound selected from the group consisting of indenes, vinylidene aromatics, cyclopentadienes, dicyclopentadienes, nonenes, octenes, terpenes and mixtures thereof.

Claim 5

Dependent Claim 30 words

The process of claim 1 wherein the substituted phenol is the addition product of phenol and a compound selected from the group consisting of styrene, limonene, 2,4,4-trimethyl-1-pentene, octene-1 and dicyclopentadiene.

Claim 6

Dependent Claim 173 words

The process of claim 1 wherein the substituted phenol mixture is prepared by gradually adding a mixture of carbocyclic compounds to a preheated liquid phase mixture of phenol and a FriedelCrafts acid catalyst, maintained in the range from about 25° to 200° C., whereby over a time interval of from about 10 minutes to four hours from about 10 to 80 parts by weight of the mixture of carbocyclic compounds reacts with each 100 parts by weight of the phenol, the mixture of carbocyclic compounds comprising (on a 100 weight percent basis when in a form substantially free of other materials): 1. from about 10 to 40 weight percent of compounds each molecule of which has: a. the indene nucleus, b. from 9 to 13 carbon atoms, c. as nuclear substituents from 0 to 4 methyl groups, 2. from about 5 to 70 weight percent of compounds each molecule of which has: a. the dicyclopentadiene nucleus, b. from 10 to 13 carbon atoms, c. as nuclear substituents from 0 to 3 methyl groups,

Claim 7

Dependent Claim 77 words

from about 15 to 65 weight percent of compounds each molecule of which has: a. a phenyl group substituted by a vinylidene group, b. from 8 to 13 carbon atoms, c. as substituents from 0 to 3 groups selected from the class consisting of methyl and ethyl, 4. from about 0 to 5 weight percent divinyl benzene, 5. provided that the sum total of all such compounds in the mixture of carbocyclic compounds is 100 weight percent.

Claim 8

Dependent Claim 77 words

from about 15 to 65 weight percent of compounds each molecule of which has: a. a phenyl group substituted by a vinylidene group, b. from 8 to 13 carbon atoms, c. as substituents from 0 to 3 groups selected from the class consisting of methyl and ethyl, 4. from about 0 to 5 weight percent divinyl benzene, 5. provided that the sum total of all such compounds in the mixture of carbocyclic compounds is 100 weight percent.

Claim 9

Dependent Claim 137 words

The process of claim 1 wherein the substituted phenol mixture is prepared by gradually adding a mixture of carbocyclic compounds to a preheated liquid phase mixture of phenol and a Friedel-Crafts acid catalyst, maintained in the range from about 25° to 200° C., whereby over a time interval of from about 10 minutes to four hours from about 10 to 80 parts by weight of the mixture of carbocyclic compounds reacts with each 100 parts by weight of the phenol, the mixture of carbocyclic compounds comprising (on a 100 weight percent basis when in a form substantially free of other materials): 1. from about 10 to 40 weight percent of compounds each molecule of which has: a. the indene nucleus, b. from 9 to 13 carbon atoms, c. as nuclear substituents from 0 to 4 methyl groups,

Claim 10

Dependent Claim 112 words

from about 15 to 30 weight percent of compounds each molecule of which has: a. the dicyclopentadiene nucleus, b. from 10 to 13 carbon atoms, c. as nuclear substituents from 0 to 3 methyl groups, 3. from about 30 to 65 weight percent of compounds each molecule of which has: a. a phenyl group substituted by vinylidene group, b. from 8 to 13 carbon atoms, c. as substituents from 0 to 3 groups selected from the class consisting of methyl and ethyl, 4. from about 0 to 5 weight percent divinyl benzene, 5. provided that the sum total of all such compounds in the mixture of carbocyclic compounds is 100 weight percent.

Claim 11

Dependent Claim 112 words

from about 15 to 30 weight percent of compounds each molecule of which has: a. the dicyclopentadiene nucleus, b. from 10 to 13 carbon atoms, c. as nuclear substituents from 0 to 3 methyl groups, 3. from about 30 to 65 weight percent of compounds each molecule of which has: a. a phenyl group substituted by vinylidene group, b. from 8 to 13 carbon atoms, c. as substituents from 0 to 3 groups selected from the class consisting of methyl and ethyl, 4. from about 0 to 5 weight percent divinyl benzene, 5. provided that the sum total of all such compounds in the mixture of carbocyclic compounds is 100 weight percent.

Claim 12

Dependent Claim 55 words

The process of claim 1 wherein the divalent electropositive metal ion is provided by a compound selected from the group consisting of oxides, hydroxides, and organic acid salts of the metal, and wherein the amount of the compound is within the range of about 0.1 to 10.0 weight percent of the weight of the phenol.

Claim 13

Dependent Claim 44 words

The process of claim 1 wherein the divalent electropositive metal ion is selected from the group consisting of zinc (Zn + + ), cobalt (Co + + ), magnesium (Mg + + ), manganese (Mn + + ) and calcium (Ca + + ).

Claim 14

Dependent Claim 29 words

The process of claim 1 wherein the organic acid added to control the pH is selected from the group consisting of formic, acetic, lactic, benzoic, adipic, and succinic acids.

Claim 15

Dependent Claim 24 words

The process of claim 1 wherein the fibrous substrate comprises fibers selected from the group consisting of cellulose, asbestos, cotton, glass, nylon and polyester.

Claim 16

Dependent Claim 21 words

The process of claim 1 wherein the thickness of the fibrous substrate is in the range of 5 to 20 mils.

Claim 17

Dependent Claim 20 words

The process of claim 1 wherein the formaldehyde to phenol mol ratio is in the range of 0.9 to 1.75.

Claim 18

Dependent Claim 16 words

The process of claim 1 wherein the B-stage resin is further advanced to the cured state.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1980-05-09	1980-11-08	1981-05-10	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1984-05-09	1984-11-08	1985-05-10	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1988-05-09	1988-11-08	1989-05-10	$7700.00	Window Closed / Lapsed

Process of preparing fibrous sheet from high-ortho phenolic resole resin varnish

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag