Method for the manufacture of multi-layer sliding material
Assignee: Daido Metal Co Ltd
•
Filing: 1976-07-09
•
Granted: 1978-10-24
•
Expires: 1996-07-09
Abstract
Abstract This invention discloses a method for manufacturing a multi-layer sliding material, said method substantially comprising laying and distributing metal powder which contains aluminum as a main component thereof, uniformly on a steel plate or a steel plated with Ni or the like in the form of a multi-layer composite metal plate, cold rolling the metal powder loaded plate and then sintering the same into a sufficiently bonded composite material. In accordance with the present invention, there is provided a multi-layer sliding material which has high adhesion between the steel plate and the sintered metal powder, is excellent in fatigue resistance and is satisfactory in surface properties as well as a method for manufacturing said multi-layer sliding material in a simple and inexpensive manner.
Inventors
- 👤 Sanae Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:51
CPC Classifications
C; C23; C23C; C23C24/00; C23C24/08; C23C24/082; C23C24/085; B; B22; B22F; B22F7/00; B22F7/02; B22F7/04; C23C28/00; C23C28/02; C23C28/021; C23C28/023; C23C28/027; F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/12; F16C33/121; F16C2204/00; F16C2204/20; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49636; Y10T29/49705; Y10T29/49709
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
286 words
A method of manufacturing multi-layer sliding material, which comprises following the steps in the sequence set forth: (a) preparing a surface of a steel plate to make said surface suitable for adhering a coating; (b) preparing two kinds of powder mixtures, one for a first, boundary layer and the other for a second, alloy layer, the first powder mixture consisting of aluminum alone or aluminum with at least one powder additive selected from the group consisting of strengthening elements, solid lubricants and lubricants of metal powder of low melting point; the second powder mixture consisting of aluminum powder as a main component and 2 to 40 percent by weight of at least one powder additive selected from the group consisting of metal powder lubricants of low melting point, solid lubricants and strengthening elements, the amount of additives being adjusted to have more weight percent than that added to the first powder mixture; (c) laying and distributing by gravity said first powder mixture as a first layer on the surface of said steel plate; (d) laying and distributing by gravity the second powder mixture as a second layer on said steel plate over said first layer; (e) passing the steel plate and two layers of powder mixtures loosely laid thereon together through a cold rolling mill and rolling down the metal powder loaded steel plate at room temperature so as to compact it until the average density of the distributed metal powder mixture reaches at least 90% of the theoretical density of said metal powder and to bond said powder mixture to said steel plate; (f) and sintering the rolled and compacted steel plate and powder mixtures at a temperature range of from 280° to 520° C.
Claim 2
Independent Claim
286 words
A method of manufacturing multi-layer sliding material, which comprises following the steps in the sequence set forth: (a) preparing a surface of a steel plate to make said surface suitable for adhering a coating; (b) preparing two kinds of powder mixtures, one for a first, boundary layer and the other for a second, alloy layer, the first powder mixture consisting of aluminum alone or aluminum with at least one powder additive selected from the group consisting of strengthening elements, solid lubricants and lubricants of metal powder of low melting point; the second powder mixture consisting of aluminum powder as a main component and 2 to 40 percent by weight of at least one powder additive selected from the group consisting of metal powder lubricants of low melting point, solid lubricants and strengthening elements, the amount of additives being adjusted to have more weight percent than that added to the first powder mixture; (c) laying and distributing by gravity said first powder mixture as a first layer on the surface of said steel plate; (d) laying and distributing by gravity the second powder mixture as a second layer on said steel plate over said first layer; (e) passing the steel plate and two layers of powder mixtures loosely laid thereon together through a cold rolling mill and rolling down the metal powder loaded steel plate at room temperature so as to compact it until the average density of the distributed metal powder mixture reaches at least 90% of the theoretical density of said metal powder and to bond said powder mixture to said steel plate; (f) and sintering the rolled and compacted steel plate and powder mixtures at a temperature range of from 280° to 520° C.
Claim 3
Dependent Claim
67 words
A method of manufacturing multi-layer sliding material as claimed in claim 1, wherein a third powder mixture for an additional alloy layer consisting of pure aluminum powder with additives of more amount than that of the first layer but less than that of the second layer is prepared, laid and interposed by gravity between the first layer and the second layer, prior to said rolling down operation.
Claim 4
Dependent Claim
88 words
A method of manufacturing multi-layer sliding material as claimed in claim 1 wherein said lubricant of metal powder of low melting point is selected from the group consisting of Pb, Sn, Bi, Cd, Sb, Te, Tl, In or mixtures thereof; said solid lubricant is selected from the group consisting of metal sulphides, metal oxides, metal fluorides, graphite, intermetallic compounds, nitrified boron, P.T.F.E., fluoridized graphite, carbon fiber and mixtures thereof; and said strengthening element is selected from the group consisting of Cu, Ni, Si, Mg, Zn and mixtures thereof.
Claim 5
Dependent Claim
24 words
A method of manufacturing multi-layer sliding material as claimed in claim 1, wherein the steel plate is plated with nickel, cobalt, Co-P and Ag.
Claim 6
Dependent Claim
32 words
A method of manufacturing multi-layer sliding material as claimed in claim 1, wherein the preparation of said steel plate comprises cleaning said plate using a degreasing chamber filled with vapour of trichloroethylene.
Claim 7
Dependent Claim
27 words
A method of manufacturing multi-layer sliding material as set forth in claim 1, wherein the preparation of said steel plate comprises roughing said plate using wire brushes.
Claim 8
Dependent Claim
25 words
A method of manufacturing multi-layer sliding material as claimed in claim 1, wherein said sintering step is conducted in a non-oxidizing or a reducing atmosphere.
Claim 9
Dependent Claim
63 words
A method of manufacturing multi-layer sliding material as claimed in claim 1 which further comprises the steps of cold-rolling or hot-rolling the material which has been subjected to all of the steps so as to make the finished sliding material more dense and to form it to predetermined dimensions and then annealing said material at a temperature ranging from 280° to 520° C.
Claim 10
Dependent Claim
36 words
A method of manufacturing multi-layer sliding material as claimed in claim 8, wherein said step of rolling for making the material more dense and forming it to predetermined dimensions is conducted using a multi-stage rolling mill.
Claim 11
Dependent Claim
45 words
A method of manufacturing multi-layer sliding material as claimed in claim 8, wherein the total amount of reduction ratio for the steel plate through repeated steps of rolling for making the material more dense and forming it to predetermined dimensions is maintained less than 55%.
Claim 12
Dependent Claim
89 words
A method of manufacturing multi-layer sliding material as claimed in claim 3, wherein said metal sulphide is selected from the group consisting of MoS 2 and PbS, said intermetallic compound is selected from the group consisting of MoSe 2 , WTe 2 and Mn 5 Si 3 , and said metal oxide is selected from the group consisting of PbO, Pb 3 O 4 , TiO 2 and CdO, and said metal fluoride is selected from the group consisting of CdF 2 , BaF 2 and PbF 2 .
Claim 13
Dependent Claim
36 words
A method of manufacturing multi-layer sliding material as claimed in claim 3, wherein said solid lubricant is selected from the group consisting of talc, mica, iodide, chloride, bromide, plastics, metallic soap, glass fiber and mixtures thereof.
References Cited (Backward Citations)
US2339208A
Cited
US3104135A
Cited
US3755090A
Cited
US3884729A
Cited
US3812563A
Cited
US3797084A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |