Phosphor coating method and resulting fluorescent lamp

Claim 1

In combination with a fluorescent lamp comprising a sealed elongated light-transmitting glass envelope enclosing a discharge-sustaining filling and operating electrodes supported proximate the ends thereof and adapted to have a radiation-generating discharge maintained therebetween, an improved phosphor coating carried on the envelope interior surface and comprising: (a) a predetermined coating weight of preselected finely divided phosphor particles carried on the interior surface of said envelope; and (b) said phosphor particles firmly bound both to one another and to the interior envelope surface by a melted and solidified mixture of boric anhydride and sodium borate, the combined weight of sodium borate plus boric anhydride (expressed in terms of an equivalent amount of boric acid prior to heating and melting) being from about 1% to 3% by weight of the phosphor, and the relative weight ratios of sodium borate to boric anhydride (expressed in terms of an equivalent amount of boric acid prior to heating and melting) being from about 1:2 to 1:4.

Claim 7

The method of improving the adherence and performance of a phosphor coating applied to the interior surface of a tubular, glass fluorescent lamp envelope, which method comprises: (a) forming a phosphor coating suspension comprising a water vehicle, the finely divided phosphor to be coated, a small amount of water-soluble viscosity-imparting organic binder material which will oxidize and burn out when heated to a relatively high temperature, and an inorganic binder comprising dissolved boric acid and sodium borate, the combined weight of said boric acid and said sodium borate in said coating suspension being from about 1% to 3% by weight of said phosphor, and the relative weight ratios of said sodium borate to said boric acid in said coating suspension being from about 1:2 to 1:4; (b) flowing said suspension over the interior surface of said tube to be coated to deposit thereon a predetermined weight of said suspension; and (c) lehring said coating tube for a predetermined time at a predetermined temperature less than the softening temperature of said glass but sufficient to burn out said organic binder and to melt said boric acid and said sodium borate which on cooling forms a solidified matrix to securely adhere said phosphor particles to one another and to the interior surface of said envelope.

Claim 8

The method of improving the adherence and performance of a phosphor coating applied to the interior surface of a tubular, glass fluorescent lamp envelope, which method comprises: (a) forming a phosphor coating suspension comprising a water vehicle, the finely divided phosphor to be coated, a small amount of water-soluble viscosity-imparting organic binder material which will oxidize and burn out when heated to a relatively high temperature, and an inorganic binder comprising dissolved boric acid and sodium borate, the combined weight of said boric acid and said sodium borate in said coating suspension being from about 1% to 3% by weight of said phosphor, and the relative weight ratios of said sodium borate to said boric acid in said coating suspension being from about 1:2 to 1:4; (b) flowing said suspension over the interior surface of said tube to be coated to deposit thereon a predetermined weight of said suspension; and (c) lehring said coating tube for a predetermined time at a predetermined temperature less than the softening temperature of said glass but sufficient to burn out said organic binder and to melt said boric acid and said sodium borate which on cooling forms a solidified matrix to securely adhere said phosphor particles to one another and to the interior surface of said envelope.

Claim 11

The method as specified in laim 8, wherein said formed coating suspension also includes sufficient amine to provide a pH of about 8.5 for said suspension, a small amount of wetting agent, and a small amount of defoamer.

Claim 12

The method as specified in laim 8, wherein said formed coating suspension also includes sufficient amine to provide a pH of about 8.5 for said suspension, a small amount of wetting agent, and a small amount of defoamer.