Process for crystallizing and drying polyethylene terephthalate and apparatus to carry out said process
Assignee: Hoechst AG
•
Filing: 1976-12-16
•
Granted: 1978-10-17
•
Expires: 1996-12-16
Abstract
Abstract Polyester granules are crystallized and dried by passing hot gasses of 120° to 190° C in upward direction through the stationary layer of loose polyester granules resting in a cylindrical container on a plane or conical perforated tray slowly rotating about its vertical axis. The hot gas is passed through the material in an amount such that no fluidization is brought about. Under the action of the hot gas the granules agglomerate and the agglomerate is alternately slightly lifted and lowered again by stripping edges on the perforated tray whereby the agglomerate portion resting on the tray is disintegrated and the crystallized granules are discharged through slots behind the stripping edges in the tray.
Inventors
- 👤 Siegfried Breitschaft
- 👤 Rolf Holtermann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:13
CPC Classifications
F; F26; F26B; F26B17/00; F26B17/12; F26B17/14; F26B17/1433; F26B17/1466; F26B17/1483; B; B29; B29B; B29B13/00; B29B13/06; B29B13/065; B29B9/00; B29B9/16; B29B2009/165
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
127 words
A process for crystallizing and drying granules of amorphous polyethylene terephthalate by treating same with hot gases at a temperature of from 120° to 190° C., the hot gases passing through a cylindrical layer of loose polyester granules, which comprises crystallizing and drying the polyethylene terephthalate in a single process step with avoidance of fluidization and movement of said layer wherein under the action of the hot gases the cylindrical layer of loose polyester granules agglomerates to a cylindrical block, destroying said cylindrical block from the bottom thereof by scratching it off in layers by means of a perforated tray rotating about its vertical axis and provided with stripping edges and discharge slots, and discharging the disintegrated polyester material through the discharge slots of the perforated tray.
Claim 2
Dependent Claim
127 words
A process for crystallizing and drying granules of amorphous polyethylene terephthalate by treating same with hot gases at a temperature of from 120° to 190° C., the hot gases passing through a cylindrical layer of loose polyester granules, which comprises crystallizing and drying the polyethylene terephthalate in a single process step with avoidance of fluidization and movement of said layer wherein under the action of the hot gases the cylindrical layer of loose polyester granules agglomerates to a cylindrical block, destroying said cylindrical block from the bottom thereof by scratching it off in layers by means of a perforated tray rotating about its vertical axis and provided with stripping edges and discharge slots, and discharging the disintegrated polyester material through the discharge slots of the perforated tray.
Claim 3
Dependent Claim
35 words
The process of claim 1, wherein the crystallization and drying is performed continuously and the layer of the loose polyester material has a height which is equal to 1 to 4 times the reactor diameter.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-16 | 1982-04-17 | 1982-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-16 | 1986-04-17 | 1986-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-16 | 1990-04-17 | 1990-10-17 | $7700.00 | Window Closed / Lapsed |