Fire retardant urea-formaldehyde compositions
Assignee: Individual
•
Filing: 1977-05-06
•
Granted: 1978-10-10
•
Expires: 1997-05-06
Abstract
Abstract A method of preparing a resinous system, and the resinous system produced by the method is described wherein about 65-80 moles of an aldehyde such as formaldehyde, about 15-25 moles of a catalyzing inorganic acid, optionally, about 3-7 moles of an alkanolamine such as triethanolamine, and about 20-30 moles of urea, are reacted to provide an aqueous resinous solution. The resinous solution will cure at room temperature or upon application of heat, permitting its use as a flexible, pliable, waterproof, non-burning coating.
Inventors
- 👤 Glenn A. Pearson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:41
CPC Classifications
C; C08; C08G; C08G12/00; C08G12/02; C08G12/04; C08G12/10; C08G12/12; C08G12/043; C08G12/046; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/31504; Y10T428/31551; Y10T428/31627; Y10T428/31678; Y10T428/31688; Y10T428/31942; Y10T428/31949; Y10T428/31957; Y10T428/31964
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
96 words
A resinous solution comprising the reaction product of (a) about 65-80 moles of formaldehyde, (b) about 20-30 moles of urea, and (c) about 15-25 moles of phosphoric acid, said solution being formed by initial mixing of said formaldehyde and said urea followed by the addition of said phosphoric acid, whereby upon addition of said phosphoric acid, an exothermic reaction occurs leading to a substantially immediate and complete exothermic reaction to form a viscous, syrupy, water-white, aqueous resinous solution, the solution being a stable solution having a good shelf life and forming flexible, waterproof and non-burning films.
Claim 2
Dependent Claim
96 words
A resinous solution comprising the reaction product of (a) about 65-80 moles of formaldehyde, (b) about 20-30 moles of urea, and (c) about 15-25 moles of phosphoric acid, said solution being formed by initial mixing of said formaldehyde and said urea followed by the addition of said phosphoric acid, whereby upon addition of said phosphoric acid, an exothermic reaction occurs leading to a substantially immediate and complete exothermic reaction to form a viscous, syrupy, water-white, aqueous resinous solution, the solution being a stable solution having a good shelf life and forming flexible, waterproof and non-burning films.
Claim 3
Dependent Claim
23 words
A solution according to claim 1 wherein 3-7 moles of triethanolamine are mixed with the formaldehyde prior to addition of the other reactants.
Claim 4
Dependent Claim
14 words
A solution according to claim 1 wherein the formaldehyde is a 37% aqueous solution.
Claim 5
Dependent Claim
15 words
A solution according to claim 1 wherein the phosphoric acid is 85% aqueous phosphoric acid.
Claim 6
Dependent Claim
25 words
A solution according to claim 1 wherein the reaction product comprises the reaction of 73 moles formaldehyde, 24 moles urea and 18 moles phosphoric acid.
Claim 7
Dependent Claim
11 words
A solution according to claim 5 which includes 4 moles triethanolamine.
Claim 8
Dependent Claim
44 words
A solution according to claim 1 wherein a metal salt selected from the group consisting of the oxides, hydroxides, sulfates, nitrates, phosphates and chlorides of aluminum, zinc, tin and antimony, is added to the phosphoric acid prior to mixing with the formaldehyde and urea.
Claim 9
Dependent Claim
24 words
A solution according to claim 1 wherein ammonium hydroxide is added to the urea and formaldehyde solution prior to mixing with the phosphoric acid.
Claim 10
Dependent Claim
15 words
A solution according to claim 1 wherein lactic acid is added to the final solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |