Reinforced carbon and graphite articles
Assignee: Stemcor Corp
•
Filing: 1972-01-03
•
Granted: 1978-10-10
•
Expires: 1992-01-03
Abstract
Abstract A reinforced carbon article which comprises a carbon fiber shape bonded by a carbon binder and having incorporated within said article a friction modifier, e.g., the in situ reaction product of carbon and a boron containing additive which comprises a material selected from the group consisting of boron, boron nitride, boron silicide and refractory metal borides; and a process of making such an article which comprises forming a carbon fiber shape, dispersing a boron containing additive within at least a portion of said carbon fiber shape, impregnating the carbon fiber shape with a carbonizable binder, and heating the shape to carbonize the binder and to form in situ the reaction product of carbon and the boron containing additive.
Inventors
- 👤 Leo C. Ehrenreich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 14:39
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; F; F16; F16D; F16D69/00; F16D69/02; F16D69/023; F16D65/00; F16D65/02; F16D65/12; F16D65/125; F16D65/126; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2916; Y10T428/2918; Y10T428/292; Y10T428/2922; Y10T428/2925; Y10T428/30
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
96 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance even at opening temperature as great as 3000° F, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the friction article, further characterized by a friction modifying amount up to about 48 percent by weight of ditungsten monoboride friction modifier.
Claim 2
Dependent Claim
96 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance even at opening temperature as great as 3000° F, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the friction article, further characterized by a friction modifying amount up to about 48 percent by weight of ditungsten monoboride friction modifier.
Claim 3
Dependent Claim
23 words
The friction article of claim 1, wherein the ditungsten monoboride friction modifier is present in amounts up to about 30 percent by weight.
Claim 4
Dependent Claim
99 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance even at operating temmperature as great as 3000° F, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the substantially all carbon friction article, further characterized by a friction modifying amount up to about 7 percent by volume of ditungsten monoboride friction modifier.
Claim 5
Dependent Claim
99 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance even at operating temmperature as great as 3000° F, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the substantially all carbon friction article, further characterized by a friction modifying amount up to about 7 percent by volume of ditungsten monoboride friction modifier.
Claim 6
Dependent Claim
22 words
The friction article of claim 3, wherein the ditungsten monoboride friction modifier is present in amounts up to about 3.5% by volume.
Claim 7
Dependent Claim
104 words
A friction article comprising carbonized woundup layers of filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material said carbonized binder binding said filamentary material into an integral body, said article having an inner periphery and an outer periphery, and having a differential composition such that material of the article adjacent one of said peripheries has different strength and friction properties than the strength and friction properties of material of the article adjacent the other of its peripheries, whereby to provide maximal article mechanical driving strength properties adjacent one periphery and maximal friction material properties adjacent the other.
Claim 8
Dependent Claim
104 words
A friction article comprising carbonized woundup layers of filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material said carbonized binder binding said filamentary material into an integral body, said article having an inner periphery and an outer periphery, and having a differential composition such that material of the article adjacent one of said peripheries has different strength and friction properties than the strength and friction properties of material of the article adjacent the other of its peripheries, whereby to provide maximal article mechanical driving strength properties adjacent one periphery and maximal friction material properties adjacent the other.
Claim 9
Dependent Claim
103 words
A friction article comprising carbonized layers of filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material said carbonized binder binding said filamentary material into an integral body, said article having an inner periphery and an outer periphery, and having a differential composition such that material of the article adjacent one of said peripheries has different strength and friction properties than the strength and friction properties of material of the article adjacent the other of its peripheries, whereby to provide maximal article mechanical driving strength properties adjacent one periphery and maximal friction material properties adjacent the other.
Claim 10
Dependent Claim
103 words
A friction article comprising carbonized layers of filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material said carbonized binder binding said filamentary material into an integral body, said article having an inner periphery and an outer periphery, and having a differential composition such that material of the article adjacent one of said peripheries has different strength and friction properties than the strength and friction properties of material of the article adjacent the other of its peripheries, whereby to provide maximal article mechanical driving strength properties adjacent one periphery and maximal friction material properties adjacent the other.
Claim 11
Dependent Claim
87 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the friction article, further characterized by a friction modifying amount up to about 48 percent by weight of ditungsten monoboride friction modifier.
Claim 12
Dependent Claim
87 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the friction article, further characterized by a friction modifying amount up to about 48 percent by weight of ditungsten monoboride friction modifier.
Claim 13
Dependent Claim
23 words
The friction article of claim 7, wherein the ditungsten monoboride friction modifier is present in amounts up to about 30 percent by weight.
Claim 14
Dependent Claim
90 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the substantially all carbon friction article, further characterized by a friction modifying amount up to about 7 percent by volume of ditungsten monoboride friction modifier.
Claim 15
Dependent Claim
90 words
A high energy absorbing friction article which is a unified structural member for running in air and which is characterized by light weight and superior heat resistance, the combination of a carbonized filamentary material and a carbonized in situ resin binder material associated with said carbonized filamentary material, said carbonized binder binding said filamentary material into an integral body, whereby to provide superior strength in the substantially all carbon friction article, further characterized by a friction modifying amount up to about 7 percent by volume of ditungsten monoboride friction modifier.
Claim 16
Dependent Claim
22 words
The friction article of claim 9, wherein the ditungsten monobromide friction modifier is present in amounts up to about 3.5% by volume.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |