Crimped bicomponent-filament yarn with randomly reversing helical filament twist
Assignee: EIDP Inc
•
Filing: 1977-05-11
•
Granted: 1978-10-03
•
Expires: 1997-05-11
Abstract
Abstract Crimped bicomponent-filament yarn is produced by spinning composite filaments of polyhexamethyleneadipamide and polyethylene terephthalate modified with 5-(sodium sulfo) isophthalate, with the two components side by side in oblong filament cross sections wherein the length of the major axis is 2.5 to 4.5 times the length of the minor axis and the polyhexamethyleneadipamide component occupies 20 to 35 percent of the total cross-sectional area, drawing the filaments about 3 × in about 200° C steam, and crimping the filaments in a bulking jet with air or steam at about 280° C. The composite filaments have a randomly reversing filament twist with an average of 60 to 120 crimps per inch (23.5 to 47 crimps/cm) of filament and, when the yarn is heated at about 100° C in aqueous caustic solution, filament components split apart to form a yarn having crimped copolyester filaments surrounded by arched filaments of polyhexamethyleneadipamide.
Inventors
- 👤 Harry Eugene Stanley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 11:34
CPC Classifications
D; D01; D01F; D01F8/00; D01F8/04; D01F8/14; D02; D02G; D02G1/00; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2924; Y10T428/2925; Y10T428/2929; Y10T428/2931; Y10T428/2973
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
162 words
A crimped bicomponent-filament yarn comprising fliaments having a polyhexamethyleneadipamide component and a copolyester component adhered together in a side-by-side composite filament of oblong cross section along the length of the filament wherein the length of the major axis of the cross section is between 2.5 and 4.5 times the length of the minor axis, the polyhexamethyleneadipamide component occupies an area at one side of the cross section that extends along said major axis for a distance about equal to the length of said minor axis and is between 20 and 35 percent of the total cross-sectional area; said copolyester component consisting essentially of poly[ethylene terephthalate/5-(sodium sulfo)isophthalate] containing 0.5 to 3 mole percent of the 5-(sodium sulfo)isophthalate units; the bicomponent filaments having a randomly reversing filament twist with an average of 60 to 120 crimps per inch of filament and having the property of splitting into polyhexamethyleneadipamide filaments and copolyester filaments when heated at about 100° C. in 1 percent aqueous caustic solution.
Claim 2
Dependent Claim
162 words
A crimped bicomponent-filament yarn comprising fliaments having a polyhexamethyleneadipamide component and a copolyester component adhered together in a side-by-side composite filament of oblong cross section along the length of the filament wherein the length of the major axis of the cross section is between 2.5 and 4.5 times the length of the minor axis, the polyhexamethyleneadipamide component occupies an area at one side of the cross section that extends along said major axis for a distance about equal to the length of said minor axis and is between 20 and 35 percent of the total cross-sectional area; said copolyester component consisting essentially of poly[ethylene terephthalate/5-(sodium sulfo)isophthalate] containing 0.5 to 3 mole percent of the 5-(sodium sulfo)isophthalate units; the bicomponent filaments having a randomly reversing filament twist with an average of 60 to 120 crimps per inch of filament and having the property of splitting into polyhexamethyleneadipamide filaments and copolyester filaments when heated at about 100° C. in 1 percent aqueous caustic solution.
Claim 3
Dependent Claim
31 words
A bicomponent-filament yarn as defined in claim 1 wherein the two components of the filament are adhered together at an interface perpendicular to the major axis of the filament cross section.
Claim 4
Dependent Claim
28 words
A bicomponent-filament yarn as defined in claim 2 wherein the polyhexamethyleneadipamide component contains about 0.4 percent by weight of aminopropylmorpholine and about 0.1 percent by weight of bis-hexamethylenetriamine.
Claim 5
Dependent Claim
49 words
A bicomponent-filament yarn as defined in claim 1 wherein the length of the major axis of the filament cross section is about 2.7 to 3.1 times the length of the minor axis and the polyhexamethyleneadipamide component occupies about 28 to 32 percent of the cross-sectional area of the filament.
Claim 6
Dependent Claim
24 words
A bicomponent-filament yarn as defined in claim 1 wherein the copolyester component contains about 1 to 2 mole percent of the 5-(sodium sulfo)isophthalate units.
Claim 7
Dependent Claim
45 words
A bicomponent-filament yarn as defined in claim 1 comprising at least 17 filaments that split when heated at about 100° C. in 1 percent aqueous caustic solution and form a yarn of helically crimped copolyester filaments surrounded by less highly crimped, arched filaments of polyhexamethyleneadipamide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-02 | 1982-04-03 | 1982-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-02 | 1986-04-03 | 1986-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-02 | 1990-04-03 | 1990-10-03 | $7700.00 | Window Closed / Lapsed |