Abstract
Abstract A primary electrochemical cell is described in which a novel granular cathode material is utilized. The cathode is formed from about 40 to 99 weight percent of carbon black, at least 1 weight percent of a binder which is inert in the primary electrochemical cell and the remainder thereof is graphite. The cathode material may be formed by mixing the individual components together with a quantity of a suitable liquid to form a uniform slurry. The slurry is then dried at room temperature to remove the liquid. The dried mixture is crumbled into fine particles. The particles are cured at an elevated temperature to stablize the binder. The resulting material when utilized as the cathode material of a primary electrochemical cell provides a porous carbon structure of high surface area in which a network of large channels exists for continual diffusion of electrolytic solution to the carbon cathodic particles throughout the entire volume of the cell cathode regardless of the cell size.
Inventors
- 👤 Franz Goebel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:36
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/06; H01M4/86; H01M4/96; H01M6/00; H01M6/14; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
120 words
A method for forming a cathode material for a primary electrochemical cell, which material is an aggregate of porous globules of superior density, said material being formed essentially from carbon black, a binder, and a suitable liquid, said method comprising the steps of mixing a quantity of said carbon black with a quantity of said binder which is inert in the primary electrochemical cell and an amount of said suitable liquid, the quantity of said binder being at least 1 percent by weight of the resulting cathode material, the amount of liquid being at least an amount effective to cause the mix to form small, generally spherical masses, and curing the mix for a time sufficient to stabilize said binder.
Claim 2
Independent Claim
120 words
A method for forming a cathode material for a primary electrochemical cell, which material is an aggregate of porous globules of superior density, said material being formed essentially from carbon black, a binder, and a suitable liquid, said method comprising the steps of mixing a quantity of said carbon black with a quantity of said binder which is inert in the primary electrochemical cell and an amount of said suitable liquid, the quantity of said binder being at least 1 percent by weight of the resulting cathode material, the amount of liquid being at least an amount effective to cause the mix to form small, generally spherical masses, and curing the mix for a time sufficient to stabilize said binder.
Claim 3
Dependent Claim
50 words
A method according to claim 1, wherein a quantity of graphite particles is mixed with a quantity of carbon black particles, the carbon black being present within the range of 40 to 99 percent by weight of the resulting cathode material and the remainder thereof consisting essentially of the graphite.
Claim 4
Dependent Claim
29 words
A method according to claim 2, wherein the quantities of carbon black and graphite are initially dry mixed to assure a uniform distribution of carbon black and graphite particles.
Claim 5
Dependent Claim
18 words
A method according to claim 1, wherein the amount of suitable liquid is sufficient to form a slurry.
Claim 6
Dependent Claim
34 words
A method according to claim 4, wherein prior to curing the following additional steps are performed: drying the slurry at a temperature below that necessary to stabilize the binder, and crumbling the dried mixture.
Claim 7
Dependent Claim
22 words
A method according to claim 4, wherein after curing the following additional step is performed: breaking the cured material into the globules.
Claim 8
Dependent Claim
13 words
A method according to claim 1, wherein the binder is a fluorocarbon polymer.
Claim 9
Dependent Claim
42 words
A method according to claim 7, wherein the resulting cathode material is composed of the following components whose concentrations are within the ranges as given in weight percent: Graphite- 0 - 30 Carbon black: 65 - 90 Fluorocarbon polymer: 1 - 10
Claim 10
Independent Claim
111 words
A method for forming a cathode material for a primary electrochemical cell, which material is an aggregate of porous globules of superior density, said method comprising: dry mixing carbon black with graphite; adding a 50% isopropanol solution in water to the dry mixed carbon black and graphite, and mixing therewith to form a slurry; adding, approximately 5% by weight of the dry mixed carbon black and graphite, a fluorocarbon polymer is suspension selection from the group tetrafluoroethylene fluorocarbon polymers and fluorinated ethylenepropylene resins to said slurry, and mixing to disperse said selected fluorocarbon polymer uniformly throughout said slurry; drying the overall mixture; crumbling the dried mixture; and curing the crumbled particles.
Claim 11
Independent Claim
111 words
A method for forming a cathode material for a primary electrochemical cell, which material is an aggregate of porous globules of superior density, said method comprising: dry mixing carbon black with graphite; adding a 50% isopropanol solution in water to the dry mixed carbon black and graphite, and mixing therewith to form a slurry; adding, approximately 5% by weight of the dry mixed carbon black and graphite, a fluorocarbon polymer is suspension selection from the group tetrafluoroethylene fluorocarbon polymers and fluorinated ethylenepropylene resins to said slurry, and mixing to disperse said selected fluorocarbon polymer uniformly throughout said slurry; drying the overall mixture; crumbling the dried mixture; and curing the crumbled particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-02 | 1982-04-03 | 1982-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-02 | 1986-04-03 | 1986-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-02 | 1990-04-03 | 1990-10-03 | $7700.00 | Window Closed / Lapsed |